The microscopic fatigue crack behavior in a Ti-24Al-11Nb alloy was investigated. Particular attention was given to the path of the fatigue crack through the microstructure, the fracture mode, and the effects of R-ratio and crack closure on the fatigue crack growth behavior. The FCGR of the alloy at R = 0.5 was an order of magnitude higher than that at R = 0.1.
Results are presented on the measurements of the residual strengths of T300/934 graphite epoxy laminates, in tension and in compression, after the samples were exposed to tension-compression fatigue loading (R = -1). Four laminate ocnfigurations were tested: unidirectional, cross-ply, angle-ply, and quasi-isotropic. It was found that the fatigue behavior of laminates was dependent on the quasi-static strengths and the specific structure of the laminate. No direct correlation was found between remaining residual strengths and the percentage of average fatigue life. However, a correlation scheme was developed for the individual specimen under test, based on a cumulative damage model and a stiffness change of the material.
The fatigue behavior of composite laminates under tension-compression loading is analyzed and compared with behavior under tension-tension and compression-compression loading. It is shown that for meaningful fatigue conditions, the tension-compression case is the dominant one. Both tension and compression failure modes can occur under the reversed loading, and failure is dependent on the specific lay-up of the laminate and the difference between the tensile static strength and the absolute value of the compressive static strength. The use of a fatigue failure envelope for determining the fatigue life and mode of failure is proposed and demonstrated.
The critical load levels and associated cracking beyond which a multidirectional laminate can be considered as structurally failed has been determined by loading graphite fiber-reinforced epoxy laminates to different strain levels up to ultimate failure. Transverse matrix cracking was monitored by acoustic and optical methods. The residual stiffness and strength parallel and perpendicular to the cracks were determined and related to the environmental/loading history. Within the range of experimental conditions studied, it is concluded that the transverse cracking process does not have a crucial effect on the structural performance of multidirectional composite laminates.
An investigation was conducted to determine the critical load levels and associated cracking beyond which a multidirectional laminate can be considered as structurally failed. Graphite/epoxy laminates were loaded to different strain levels up to ultimate failure. Transverse matrix cracking was monitored by acoustic and optical methods. Residual stiffness and strength that were parallel and perpendicular to the cracks were determined and related to the environmental/loading history. Results indicate that cracking density in the transverse layers has no major effect on laminate residual properties as long as the angle ply layers retain their structural integrity. Exposure to hot water revealed that cracking had only a small effect on absorption and reduced swelling when these specimens were compared with uncracked specimens. Cracked, moist specimens showed a moderate reduction in strength when compared with their uncracked counterparts. Within the range of environmental/loading conditions of the present study, it is concluded that the transverse cracking process is not crucial in its effect on the structural performance of multidirectional composite laminates.
The stress corrosion susceptibility of two powder metallurgy (P/M) alloys, Al-Li-Cu and Al-Li-Cu-Mg; two mechanically attrited (M/A) alloys, Al-Li-Cu and Al-Li-Mg; and two wrought, ingot alloys, X-2020 and AA7475, are compared. Time-dependent fracture in an aqueous sodium chloride environment under alternate immersion condition was found to vary significantly between alloys. The stress corrosion behavior of the two powder metallurgy processed alloys was studied in detail under conditions of crack initiation, static crack growth, and fatigue crack growth. A variety of stress corrosion tests were performed including smooth surface, time-to-failure tests; potentiostatic tests on smooth surfaces exposed to constant applied strain rates; and fracture mechanics-type tests under static and cyclic loads. Both alloys show surface pitting and subsequent intergranular corrosion. Pitting is more severe in the magnesium-bearing alloy and is associated with stringer particles strung along the extrusion direction as a result of P/M processing.
Recently, much attention has been given to aluminum-lithium alloys because of rather substantial specific-strength and specific-stiffness advantages offered over commercial 2000and 7000-series aluminum alloys. An obstacle to Al-Li alloy development has been inherent limited ductility. In order to obtain a more refined microstructure, powder metallurgy (P/M) has been employed in alloy development programs. As stress corrosion (SC) of high-strength aluminum alloys has been a major problem in the aircraft industry, the possibility of an employment of Al-Li alloys has been considered, taking into account a use of Al-Li-Cu alloys. Attention is given to a research program concerned with the evaluation of the relative SC resistance of two P/M processed Al-Li-Cu alloys. The behavior of the alloys, with and without an addition of magnesium, was studied with the aid of three test methods. The susceptibility to SC was found to depend on the microstructure of the alloys.
The stress corrosion susceptibility of two powder metallurgy (P/M) alloys, Al-Li-Cu and Al-Li-Cu-Mg two mechanically attrited (M/A) alloys, Al-Li-Cu and Al-Li-Mg; and two wrought, ingot alloys, X-2020 and AA7475, are compared. Time-dependent fracture in an aqueous sodium chloride environment under alternate immersion condition was found to vary significantly between alloys. The stress corrosion behavior of the two powder metallurgy processed alloys was studied in detail under conditions of crack initiation, static crack growth, and fatigue crack growth. A variety of stress corrosion tests were performed including smooth surface, time-to-failure tests; potentiostatic tests on smooth surfaces exposed to constant applied strain rates; and fracture mechanics-type tests under static and cyclic loads. Both alloys show surface pitting and subsequent intergranular corrosion. Pitting is more severe in the magnesium-bearing alloy and is associated with stringer particles strung along the extrusion direction as a result of P/M processing.
(Previously announced in STAR as N81-19276)
Two powder metallurgy processed (Al-Li-Cu) alloys with and without Mg addition were studied in aqueous 3.5% NaCl solution during the alternate immersion testing of tuning fork specimens, slow crack growth tests using fracture mechanics specimens, and the slow strain rate testing of straining electrode specimens. Scanning electron microscopy and optical metallography were used to demonstrate the character of the interaction between the Al-Li-Cu alloys and the selected environment. Both alloys are susceptible to SC in an aqueous 3.5% NaCl solution under the right electrochemical and microstructural conditions. Each test method yields important information on the character of the SC behavior. Under all conditions investigated, second phase particles strung out in rows along the extrusion direction in the alloys were rapidly attacked, and played principal role in the SC process. With time, larger pits developed from these rows of smaller pits and under certain electrochemical conditions surface cracks initiated from the larger pits and contributed directly to the fracture process. Evidence to support slow crack growth was observed in both the slow strain rate tests and the sustained immersion tests of precracked fracture mechanics specimens. The possible role of H2 in the stress corrosion cracking process is suggested.
This paper reports on measurements that demonstrate that oxygen absorbed on clean polycrystalline Fe films can produce an excess current noise. The noise is indicative of dynamic processes occurring in the surface region of the film. We propose that the noise results from the dynamics of a reversible reaction between absorbed states. The measurements are accurately modeled with a single correlation time implying that surface heterogeneity is not important to the reaction. In addition to offering promise for future states of solid-state surface reactions, these measurements also have implications for the origin of 1/f current noise in conductors.
(Previously announced in STAR as N81-21134)
The influence of a specific surface reaction on the transport of gas-phase hydrogen through iron membranes has been investigated on the basis of model calculations. The surface reaction involves an adsorbed molecular hydrogen precursor between the gas phase and the dissociated chemisorbed state. The calculations demonstrate that the surface reaction for the H2/Fe system makes significant contributions to the time delay associated with the transient hydrogen transport through iron membranes, even under conditions where the steady-state hydrogen transport is independent of the surface reaction. These contributions to the time delay are interpreted in terms of an effective diffusivity, which is a function of the pressure on the entrance side and the thickness of the membrane.
The hydrogen containment materials are studied. The safe, reliable, and economic containment of hydrogen is essential to the success of virtually any hydrogen energy transport and storage scheme. The potential problems associated with hydrogen containment are presented.
Corrosion of SAE 310 stainless steel in H2-H2O-H2S gas mixtures was studied at a constant temperature of 1150 K. Reactive gas mixtures were chosen to yield a constant oxygen potential of approximately 6 x 10 to the minus 13th power/cu Nm and sulfur potentials ranging from 0.19 x 10 to the minus 2nd power/cu Nm to 33 x 10 to the minus 2nd power/cu Nm. The kinetics of corrosion were determined using a thermobalance, and the scales were analyzed using metallography, scanning electron microscopy, and energy dispersive X-ray analysis. Two corrosion regimes, which were dependent on sulfur potential, were identified. At high sulfur potentials (p sub S sub 2 less than or equal to 2.7 x 10 to the minus 2nd power/cu Nm) the corrosion rates were high, the kinetics obeyed a linear rate equation, and the scales consisted mainly of sulfide phases similar to those observed from pure sulfication. At low sulfur potentials (P sub S sub 2 less than or equal to 0.19 x 10 to the minus 2nd power/cu Nm) the corrosion rates were low, the kinetics obeyed a parabolic rate equation, and scales consisted mainly of oxide phases.
An examination and analysis is presented of the elevated temperature fatigue behavior of multidirectional graphite-epoxy laminates in terms of single lamina behavior. The laminate strength is predicted by considering the cyclic stress field in each lamina, the interlaminar stresses, and the experimentally determined temperature-effect 'shifting factors'. The initial failure of a lamina in a laminate is examined first in terms of stress redistribution, and then in terms of total failure and final laminate fracture; these analytical results are then compared with the actual fatigue behavior of T300/5208 graphite-epoxy composite laminates. In view of the agreement obtained, it is concluded that the temperature 'shifting factors' introduced here enable one to predict long-term behavior at a given temperature from short-time testing at elevated temperatures.
Explore the source record for details and available documents.
The form of the moisture distribution in the specimen (gradient and flat profile) was considered to establish the influence of accelerated moisture conditioning on fatigue behavior. For the gradient specimens having an average moisture content of 1.4 percent, fatigue life was reduced by a factor of 8 at all stress levels investigated. Corresponding reduction in fatigue life for the flat moisture profile specimens at the same average moisture content was comparatively smaller, being about a factor of 5 from the value in dry specimens. X-ray radiographic analysis of damage accumulation in compression-compression fatigue revealed interlaminar cracking to be the dominant mode of failure responsible for the observed enhanced cyclic degradation of moisture-conditioned specimens. This finding was corroborated by the observed systematic reduction in interlaminar shear strength as a function of moisture content, which, in turn, increased the propensity for delamination under cyclic compressive loads. Residual strength measurements on cycled specimens indicated significant strength reductions at long lives, particularly in moisture conditioned specimens.