NASA NTRS1988

Processable Aromatic Polyimide Thermoplastic Blends

Method developed for preparing readily-processable thermoplastic polyimides by blending linear, high-molecular-weight, polyimic acid solutions in ether solvents with ultrafine, semicrystalline, thermoplastic polyimide powders. Slurries formed used to make prepregs. Consolidation of prepregs into finsihed composites characterized by excellent melt flow during processing. Applied to film, fiber, fabric, metal, polymer, or composite surfaces. Used to make various stable slurries from which prepregs prepared.

Baucom, Robert M↗

NASA NTRS1987

Effect of geometry on thermal aging behavior of Celion/LARC-160 composites

Laminates of Celion/LARC-160, fabricated in thicknesses from 4 to 16 ply and in unidirectional, x-ply and fabric ply configurations, were isothermally aged at temperatures of 204, 260 and 316 C for periods up to 15,000 hours. Weight-loss of the test panels was measured at selected intervals during aging. At the lower aging temperatures, it was observed that panel thickness and ply arrangement influenced the apparent stability: i.e., thicker panels degraded less than thin panels and unidirectional panels degraded less than x-ply or fabric reinforced panels. At higher aging temperatures, all panel configurations and thicknesses converged toward the same behavior.

Nelson, James B.↗

NASA NTRS1987

Effect of long-term thermal aging on coated Celion/LARC-160 composites

Coated and uncoated unidirectional laminates of Celion (Trademark)/LARC-160 graphite/polyimide were thermally aged in air at temperatures of 204, 260, and 316 C for various times up to 15,000 hours. Selected panels were coated with a high temperature coating resin (polyphenyl quinoxaline--PPQ): 1) edges only; 2) top and bottom only; 3)completely; or 4) not at all. Periodically during aging, panels were removed from the ovens, weighed, and short beam shear (SBS) specimens cut from selected locations in the panels. The protective coating did not influence the retention of SBS strength during thermal aging but did not lessen the amount of weight-loss incurred. The integrity of the PPQ coating was completely destroyed during aging at 316 C.

Nelson, James B.↗