Ex situ bismuth doping for efficient CdSeTe thin-film solar cells with open-circuit voltages exceeding 900 mV
We dope CdTe solar cells with Bi after the device structure is completed using a solution process.
CdTe solar cell↗
Engineering topics
Neupane, Sabin
Publications and source records attributed to Neupane, Sabin.
Evaporated CdSe for Efficient Polycrystalline CdSeTe Thin-Film Solar Cells
Recent progress has shown that alloying cadmium telluride (CdTe) with cadmium selenide (CdSe) to create a CdSexTe1-x (CdSeTe) gradient region can significantly boost the performance of polycrystalline CdSeTe thin-film solar cells. However, improper CdSeTe alloying might introduce problematic band alignment and deleterious voids at the front interface, limiting the benefit maximization of this technique. Here, we show that the CdSe layers deposited by thermal evaporation result in CdSeTe cells with a higher performance than the sputtered CdSe. This is because evaporated CdSe can avoid the formation of voids at the front interface, producing improved front junction quality with suppressed front junction nonradiative recombination. The champion cell using evaporated CdSe demonstrated a power conversion efficiency (PCE) of 19.7%, much higher than 18.1% in the cell using sputtered CdSe.
cadmium selenide↗
Four–Terminal Perovskite–CdSeTe Tandem Solar Cells: From 25% toward 30% Power Conversion Efficiency and Beyond
Thin-film tandem photovoltaic (PV) technology has emerged as a promising avenue to enhance power conversion efficiency beyond the radiative efficiency limit of single-junction devices. Combining a tunable wide-bandgap perovskite cell with a commercially established narrow-bandgap cadmium selenium telluride (CdSeTe) cell in a comparatively easy-to-fabricate four-terminal (4-T) arrangement is a great step in that direction. Herein, the impact of the transparent back contact and the perovskite absorber bandgap on the performance of 4-T perovskite–CdSeTe tandem solar cells is investigated. 4-T perovskite–CdSeTe tandem device architecture with ≈25% efficiency is demonstrated and a feasible pathway is shown to improve the tandem efficiency to more than 30%. Furthermore, the results show that the integration of CdSeTe with perovskite in 4-T tandem PV configurations represents a significant advancement toward achieving higher efficiency and low-cost tandem PVs.
14 SOLAR ENERGY↗
Comprehensive Study of Carrier Recombination in High‐Efficiency CdTe Solar Cells Using Transient Photovoltage
Cadmium telluride (CdTe) solar cells represent a commercially successful photovoltaic technology, with an annual production capacity approaching 20 GW. However, improving the open-circuit voltage (V OC ) remains challenging. This study aims to deepen the understanding of charge carrier recombination in CdTe solar cells and to explore alternative dynamical characterization methods that address the limitations found in conventionally used time-resolved photoluminescence for CdTe solar cells. Transient photovoltage and transient photocurrent techniques are utilized to investigate charge carrier dynamics under conditions resembling real-world solar cell operation. The results reveal that an effective nonradiative recombination lifetime of 580 ns dominates the charge dynamics at VOC values below 850 mV. Above this threshold, radiative recombination becomes significant, with a radiative recombination coefficient of 1.1 × 10 −9 cm 3 s −1 . Additionally, the stationary charge carrier density at 1 sun is determined to be around 1 × 10 14 cm −3 . By accurately determining both radiative and nonradiative recombination, this work provides a comprehensive understanding of carrier dynamics in high-performing CdTe devices and paves the way for improving the V OC and performance of CdTe solar cells.
CdTe solar cells↗
Incorporating Potassium Citrate to Improve the Performance of Tin‐Lead Perovskite Solar Cells
Abstract Easy‐to‐form tin vacancies at the buried interface of tin‐lead perovskites hinder the performance of low‐bandgap perovskite solar cells (PSCs). Here, a synergistic strategy by incorporating potassium citrate (PC) into the poly(3,4‐ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) hole‐transport layer to passivate the buried interface of Sn‐Pb PSCs is reported. PC neutralizes the acidity of PEDOT:PSS and stabilizes the perovskite front surface, enhancing device stability. Citrate moieties coordinate with Sn 2+ on the buried perovskite surface, preventing Sn 2+ oxidation and suppressing defect formation. Additionally, potassium cations incorporate into Sn‐Pb perovskites, enhancing crystallinity and passivating halide defects. The combined benefits enable efficient low‐bandgap Sn‐Pb PSCs with a power conversion efficiency of 22.7% and a high open‐circuit voltage of 0.894 V. Using this method, 26.1% efficiency for all‐perovskite tandem solar cells is demonstrated. These results emphasize the significance of buried interface passivation in developing efficient and stable Sn‐Pb PSCs and all‐perovskite tandem solar cells.
14 SOLAR ENERGY↗
Oxygen Management to Avoid Photo-Inactive Cd(S,Se) for Efficient Cd(Se,Te) Solar Cells
Our previous work has demonstrated that the formation of a penternary cadmium chalcogenide Cd(O,S,Se,Te) region can significantly reduce the front interface recombination in Cd(Se,Te)-based thin-film solar cells. In this work, we have shown that oxygen management during the device fabrication is crucial to form this region. While both the CdS and CdSe layer depositions and the postdeposition CdCl2 treatment should be conducted in the presence of oxygen, the CdTe deposition should be conducted in an oxygen-free atmosphere. Improper oxygen management leads to low device performance due to the formation of a photoinactive Cd(S,Se) region and reduced absorber quality. Additionally, we investigated the carrier transport and collection properties in devices with photoinactive Cd(S,Se) and photoactive Cd(O,S,Se,Te) at the front interface to gain comprehensive understanding of the mechanisms that resulted in improved efficiencies approaching 20%.
CdTe deposition↗
Water-Assisted Lift-Off Process for Flexible CdTe Solar Cells
In recent years, various lift-off methods have been developed to fabricate lightweight and flexible cadmium telluride (CdTe)-based solar cells. In this work, we report flexible cadmium sulfide (CdS)/CdTe solar cells using a water-assisted lift-off approach. Here we demonstrate that an additional cadmium chloride treatment for the CdS film is critical to improve the grain size of CdS and the post-deposited CdTe film and the electron conductivity of the CdS film. As a result, the quality of the CdS/CdTe front junction is significantly improved with reduced nonradiative recombination. Finally, our lightweight and flexible polycrystalline CdTe solar cells demonstrate a champion power conversion efficiency of 12.6%.
14 SOLAR ENERGY↗
Post‐Annealing Treatment on Hydrothermally Grown Antimony Sulfoselenide Thin Films for Efficient Solar Cells
Herein, antimony sulfoselenide (Sb 2 (S, Se) 3 ) thin‐film solar cells are fabricated by a hydrothermal method followed by a post‐deposition annealing process at different temperatures and the impact of the annealing temperature on the morphological, structural, optoelectronic, and defect properties of the hydrothermally grown Sb 2 (S, Se) 3 films is investigated. It is found that a proper annealing temperature leads to high‐quality Sb 2 (S, Se) 3 films with large crystal grains, high crystallinity, preferred crystal orientation, smooth and uniform morphology, and reduced defect density. These results show that suppressing deep‐level defects is crucial to enhance solar cell performance. After optimizing the annealing process, Sb 2 (S, Se) 3 solar cells with an improved power conversion efficiency 2.04 to 8.48% are obtained.
14 SOLAR ENERGY↗
20%-efficient polycrystalline Cd(Se,Te) thin-film solar cells with compositional gradient near the front junction
Bandgap gradient is a proven approach for improving the open-circuit voltages (V OC s) in Cu(In,Ga)Se 2 and Cu(Zn,Sn)Se 2 thin-film solar cells, but has not been realized in Cd(Se,Te) thin-film solar cells, a leading thin-film solar cell technology in the photovoltaic market. Here, we demonstrate the realization of a bandgap gradient in Cd(Se,Te) thin-film solar cells by introducing a Cd(O,S,Se,Te) region with the same crystal structure of the absorber near the front junction. The formation of such a region is enabled by incorporating oxygenated CdS and CdSe layers. We show that the introduction of the bandgap gradient reduces the hole density in the front junction region and introduces a small spike in the band alignment between this and the absorber regions, effectively suppressing the nonradiative recombination therein and leading to improved VOCs in Cd(Se,Te) solar cells using commercial SnO 2 buffers. A champion device achieves an efficiency of 20.03% with a V OC of 0.863 V.
14 SOLAR ENERGY↗
Effects of Cu Precursor on the Performance of Efficient CdTe Solar Cells
Not provided.
Materials Science↗