Publications and source records attributed to Neyerlin, K. C..

At least 19 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

A Three–Dimensional Nanoscale View of Electrocatalyst Degradation in Hydrogen Fuel Cells

The loss of platinum (Pt) electrochemically active surface area (ECSA) is a critical degradation mode that often becomes a limiting factor for heavy-duty proton exchange membrane fuel cell vehicles. High surface area carbon supports have been shown to improve Pt dispersion and limit detrimental ionomer-electrocatalyst interactions due to their large interior pore volume. Here, in this work, using automated scanning transmission electron tomography, the degradation of nanoparticles located on the interior versus exterior surfaces of the carbon support is compared following a catalyst-specific accelerated stress test (AST) of 90,000 voltage cycles between 0.6 V to 0.95 V. The results reveal a notable increase in median particle size for both interior and exterior Pt catalyst particles, with a slightly higher increase in particle size distribution and loss of specific surface area for the particles located on the exterior carbon surface. The fraction of Pt nanoparticles that reside within the interior of the carbon support also increased following the AST test, accompanied by evidence of an increase in average carbon mesopore size. Here, the results shed light on the degradation mechanisms affecting electrochemical properties and the enhanced particle accessibility at lower relative humidity.

08 HYDROGEN↗
DOE OSTI2024

Mitigation and Diagnosis of Pin-Hole Formation in Polymer Electrolyte Membrane Fuel Cells

In this work, we implement a calendering technique to flatten stray fibers within the gas diffusion media, thereby mitigating pin-hole formation in the hot-pressed MEAs. We have investigated the influence of calendering on the long-term durability for several types of gas diffusion electrodes (GDEs) using a combined chemical and mechanical accelerated stress test (AST). The calendered MEAs demonstrate an average AST lifetime improvement of 77% relative to the as-fabricated MEAs.

AMR↗
DOE OSTI2023

(Invited) Fuel Cell Component Durability for Million Mile Fuel Cell Trucks

While significant advances have been made and early commercial fuel cell light-duty vehicles (LDVs) are starting to be produced, fuel cells in the heavy-duty-vehicle (HDV) transportation sector (including trucks, long-haul semitrailers, maritime, trains, etc.) are nascent, despite the fact that advantages of fuel cells compared to both diesel and electric powertrains are very compelling in terms of emissions, charging time, efficiency, power-to-weight ratio, among others. However, the fuel-cell technology for HDVs requires a paradigm shift in fuel-cell research and development compared to LDVs, where the emphasis becomes efficiency and improvements in durability instead of a focus on increased power densities and lower cell costs. Heavy-duty applications require significantly longer vehicle lifetimes (>25,000 hours/1,000,000 miles for heavy-duty trucks), and therefore require improved fuel cell durability compared to light-duty vehicles. In 2020, HFTO formed the Million Mile Fuel Cell Truck Consortium (M2FCT) that includes a core team of five national laboratories to overcome durability and efficiency challenges in PEMFCs for heavy-duty applications with an initial focus on long-haul trucks. While targets and testing protocols have been developed for light-duty vehicles, the same level of targets and testing protocols have not been established for heavy-duty transportation. With operational times of greater than > 25,000 hours required, the need for well-developed accelerated stress tests (ASTs) is amplified. Results from these ASTs demonstrate the need for more durable electrode layers and well-controlled potential variations. Finally, this presentation will provide an overview of the DOE's Fuel Cell R&D approach, highlighting past and current activities, as well as strategies to enable fuel cell competiveness for heavy-duty applications.

25 ENERGY STORAGE↗
DOE OSTI2023

Effect of isopropanol cosolvent on the rheology and spinnability of aqueous polyacrylic acid solutions

Abstract We investigate the effect of alcohol fraction (isopropanol, IPA) in a binary water‐alcohol solvent mixture on the shear and extensional rheological properties, as well as the role of viscoelasticity on fiber formation of poly(acrylic acid) (PAA) in electrospinning. Comparison of the scaling of both specific viscosities η sp and extensional relaxation times λ E of PAA in water–IPA mixtures, showed stronger scaling compared to salt‐free aqueous polyelectrolyte solutions, except for the η sp in the unentangled regime displaying a polyelectrolyte‐like scaling η sp ~ c 0.5 for all IPA%. Such deviation suggested IPA induces association/aggregation of PAA. However, the trends between η sp and λ E magnitudes as a function of IPA% differ for concentrations compared in the entangled regime. The η sp as well as their elastic moduli exhibit a maximum, whereas λ E increases monotonically with IPA%, suggesting a complex interplay of various interactions are dictating their structure in water‐IPA mixtures, affecting their shear and extensional response differently. Electrospinning experiments showed increasing IPA% reduces the onset of both beaded and uniform fibers. Analysis using dimensionless numbers indicated the enhancement of their elasticity by IPA, and the consequent stabilizing effect on their jets/filaments against break‐up during electrospinning, plays a role in the improvement of their fiber formation.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Anolyte Enhances Catalyst Utilization and Ion Transport Inside a CO 2 Electrolyzer Cathode

Electrochemical CO 2 reduction is a promising technology to capture and convert CO 2 to valuable chemicals. High Faradaic efficiencies of CO 2 reduction products are achieved with zero-gap alkaline CO 2 electrolyzers with a supporting electrolyte at the anode (anolyte). Herein, we investigate the effect of anolyte on the electrode properties such as catalyst utilization, ionic accessibility etc. of a CO 2 reduction cathode using electrochemical techniques and cell configurations that avoid the complexities related to co-electrolysis. Using 1M KOH as the anolyte and a Cu gas-diffusion-electrode with low Nafion content as the model CO 2 reduction electrode, we find that electrode capacitance (proxy for electrochemically active surface area) and ionic conductivity inside the cathode increase approximately 4 and 447 times, respectively, in presence of KOH. Liquid anolyte wets the electrode’s pore structure more efficiently than capillary condensation of feed water vapor. The ionomer coverage is very low, and its distribution inside the electrode is highly fragmented. Surface ion conduction mechanisms inside the electrode are orders of magnitude lower than the bulk ion conduction in presence of anolyte. This study shows that when an anolyte (e.g., KOH) is used, catalyst utilization and ionic accessibility inside the electrode increase significantly.

30 DIRECT ENERGY CONVERSION↗
DOE OSTI2022

Design of Graded Cathode Catalyst Layers with Various Ionomers for Fuel Cell Application

Proton exchange membrane fuel cells (PEMFCs) powered by green hydrogen (H2) have become a promising alternative to conventional hydrocarbon-fueled power generators. Despite technological advancements, further improvements in efficiency, durability, and low-cost production are required for the widespread adoption of PEMFCs. Though numerous approaches to improve PEMFC electrodes have been reported, most strategies utilize a single material set (e.g., one combination of catalyst and ionomer) to improve performance. Alternatively, anisotropic (graded) electrode structures with locally tunable properties may yield superior electrode performance due to improved ionic and gas phase transport. In this work, graded cathode catalyst layers (CCLs) incorporating different ionomers (Nafion D2020, Aquivion D79-25BS, and HOPI) were designed and prepared. Performance screening shows that some of these graded electrode structures have comparable performance to optimized single-ionomer electrode structures (D2020) suggesting some synergistic benefit. Additionally, we show that electrodes with lower equivalent weight (EW) D79 ionomer near the membrane and D2020 ionomer near the gas diffusion media outperformed electrodes with the inverted configuration. Finally, EIS analysis shows some graded ionomer structures (e.g. D79/D2020) have better than expected H+ conductivity, generally leading to better electrode performance. However, further optimization of ionomer content and catalyst ink formulations is needed to improve overall PEMFC performance.

DIRECT ENERGY CONVERSION↗
DOE OSTI2021

Influence of Ink Formulation and Drying Conditions on Ionomer Distribution in High-Performance Roll-to-Roll-Coated Gas-Diffusion Electrodes

To enable mass production of fuel cell membrane electrode assemblies (MEAs) catalyst layers production will require continuous roll-to-roll (R2R) coating processes. Gas diffusion electrodes (GDEs) are advantageous for mass production because the catalyst layer can be directely coated on the microporous layer of the gas diffusion media without the need for a decal-transfer process. It is known that the water-to-alcohol ratio in the catalyst ink influences the interactions of the ionomer with the catalyst leading to different distributions of ionomer in spray-coated catalyst layers. It is also known that during drying of colloidal mixtures, like fuel cell inks, factors such as drying rate, particle size, and agglomeration influence how the materials distribute themselves throughout the thickness of the dired film. Thus far there have only been limited studies to understand how process conditions such as ink formulation and drying temperature influence the distribution of ionomer and catalyst coated using scalable methods. This understanding is especially important for GDEs since it is known that having a sufficient amount of ionomer at the catalyst layer-membrane interface is critical for high performance. In this study we have focused on determining how the ratio of water to 1-propanol in the catalyst ink ink and drying temperature influence the distribution of ionomer throughout the thickness of the catalyst layer. Using a combination of Kelvin probe and x-ray photoelectron spectroscopy we show that an ionomer-rich surface is promoted by a higher drying rate and a water-rich catalyst ink. In contrast, a 1-propanol catalyst ink leads to a lower concentration of ionomer on the top surface. Using x-ray computed tomography, we are able to characterize the ionomer distribution throughout the thickness of the layer. We find that, in addition to promoting an ionomer-rich top surface, water-rich inks lead to a more homogenous distribution of ionomer, whereas a 1-propanol-rich ink leads to a more irregular distribution. It is found that MEA performance is improved by selecting conditions and ink formulations that promote ionomer enrichment at the top surface to facilitate a good interface with the membrane. MEAs prepared with a 75 wt% water catalyst ink with a 0.9 I/C have equivalent performance to spray-coated GDEs. Critically, these R2R-coated GDEs do not need an additional ionomer overlayer like the spray-coated GDEs do, reducing the number of processing steps in a manufacturing setting. This work shows that with the appropriate selection of materials, ink formulation, and processing conditions gas-diffusion electrodes are a viable pathway for fuel cell manufacturing.

ENERGY CONSERVATION, CONSUMPTION, AND UTILIZATION↗
DOE OSTI2021

Development of high-performance roll-to-roll-coated gas-diffusion-electrode-based fuel cells

This study focuses on determining fabrication conditions to create high-performance roll-to-roll-coated (R2R-coated) gas-diffusion electrodes (GDEs) for proton-exchange-membrane fuel cells (PEMFCs). Here, we examine how process conditions influence the distribution of ionomer in the electrode, which is shown to be critical for high performance. Using a combination of Kelvin probe, X-ray photoelectron spectroscopy, and nano-scale X-ray computed tomography we show that formation of an ionomer-rich surface is promoted by using a higher drying rate. We show that R2R-coated GDEs have higher surface ionomer concentration than spray-coated GDEs, which enables these R2R-coated GDEs to not need an additional ionomer overlayer, as is typically the case for spray-coated GDEs. This will reduce the number of processing steps and lower material costs in a manufacturing setting. This work shows that with the appropriate selection of materials, ink formulation, and processing conditions, direct-coated GDEs are a viable pathway for fuel cell manufacturing.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2021

New roads and challenges for fuel cells in heavy-duty transportation

The recent release of hydrogen economy roadmaps for several major countries emphasizes the need for accelerated worldwide investment in research and development activities for hydrogen production, storage, infrastructure and utilization in transportation, industry and the electrical grid. Due to the high gravimetric energy density of hydrogen, the focus of technologies that utilize this fuel has recently shifted from light-duty automotive to heavy-duty vehicle applications. Decades of development of cost-effective and durable polymer electrolyte membrane fuel cells must now be leveraged to meet the increased efficiency and durability requirements of the heavy-duty vehicle market. This Review summarizes the latest market outlooks and targets for truck, bus, locomotive and marine applications. Required changes to the fuel-cell system and operating conditions for meeting Class 8 long-haul truck targets are presented. The necessary improvements in fuel-cell materials and integration are also discussed against the benchmark of current passenger fuel-cell electric vehicles.

08 HYDROGEN↗
DOE OSTI2021

Stability of Atomically Dispersed Fe–N–C ORR Catalyst in Polymer Electrolyte Fuel Cell Environment

We have investigated the durability of a platinum group metal (PGM-)free Fe–N–C catalyst in which the Fe sites are atomically dispersed (AD), and found it to be quite stable in standard accelerated stress test (AST) cycles normally used for low-PGM catalysts: a square wave with 0.6 V lower potential limit (LPL)—0.95 V upper potential limit (UPL) with 3-s holds at UPL and LPL in H 2 /N 2 , at 1.5 atm, 80 °C and 100% RH. Considering the metrics normally employed to characterize the durability of the low-PGM catalysts after 30,000 AST cycles, this PGM-free catalyst lost <50% catalyst activity, <50% H 2 /air performance at 0.8 V, and 40 mV at 1.5 A cm -2 . However, it is less stable in H 2 /air, losing ~50% catalyst activity after just 7.5 h of polarization measurements (load cycles). In combined cycles, the majority of the loss in catalyst activity occurred during the load cycles in H 2 /air rather than AST cycles in H 2 /N 2 . We have concluded that, unlike low-PGM catalysts that lose electrochemically active surface area (ECSA) through potential cycling-induced processes, (AD)Fe–N–C catalysts degrade by processes associated with the presence of oxygen.

25 ENERGY STORAGE↗
DOE OSTI2020

Tailoring electrode microstructure via ink content to enable improved rated power performance for platinum cobalt/high surface area carbon based polymer electrolyte fuel cells

Improvements in polymer electrolyte fuel cell (PEFC) electrode performance have primarily focused on catalyst and ionomer developments, marginalizing the importance of catalyst ink formulation. In this study, the effect of ink formulation is examined across a series of cathodes comprised of PtCo supported on high surface area carbon (PtCo/ HSC ) and Nafion ionomer using an array of in situ electrochemical and ex situ characterization techniques. In contrast to prior work on Pt/Vu systems, ink water content had little effect on the electrochemically determined ionomer coverage for the PtCo/HSC electrocatalyst examined here. Characterization using nano-scale resolution X-ray computed tomography (nano-CT) demonstrated that water-rich ink formulations lead to a reduction in aggregate size (ionomer + PtCo/HSC), improving local O 2 transport. This understanding, combined with the use of a commercially-available electrocatalyst was used to produced state-of-the-art membrane electrode assemblies with Pt loadings of 0.03/0.08 mg Pt /cm 2 on the anode and cathode respectively, having; i) > 1 A/mg Pt (0.9 V iR-free , 150 kPa, 80 °C, 100% RH, H 2 /O 2 ), ii) 320 mA/cm 2 at 0.8 V, 150 kPa, 80 ° C, 100% RH, H 2 /Air), and iii) > 1 W/cm 2 elec at rated power (0.67 V, 250 kPa, 94 °C, 65% RH, H 2 /Air) or < 0.11 g Pt /kW rated .

25 ENERGY STORAGE↗
DOE OSTI2020

Utilizing ink composition to tune bulk-electrode gas transport, performance, and operational robustness for a Fe-N-C catalyst in polymer electrolyte fuel cell

With lower site density and turnover frequency, platinum group metal (PGM)-free catalysts based electrodes are often greater than 50 mu m thick in order to increase performance across the fuel cell operating range. Consequently, PGM-free electrodes have an additional bulk electrode transport resistance beyond the local or aggregate level transport in thin platinum-based electrodes. In parallel to the development of more active and durable PGM-free catalysts, advancements in understanding the interplay between PGM-free electrode fabrication, bulk-electrode transport, proton conductivity and performance are needed. Here, the relationship between ionic and gas phase transport through the electrode thickness is modified by adjusting electrocatalyst and ionomer flocculation/interaction at the ink level. The influence of the ink composition (water/n-propanol content) is examined via various in-situ electrochemical and ex-situ characterization techniques and the resulting electrode structure/performance relationship contrasted with electrode performance robustness across a range of relative humidity (RH). For the electrocatalyst examined here, a water-rich (82 wt% H2O) ink formulation was favorable for operation at high RH due to improved molecular diffusion through larger electrode pores. In contrast, the improved interactions between ionomer and electrocatalyst enabled a more robust electrode and higher performance during low RH operation for the 50 wt% H2O content ink.

08 HYDROGEN↗