DOE OSTI2024

Impact of polymer additives on crack mitigation of rod-coated fuel cell cathode catalyst layers

Cracks in catalyst layers (CLs) are a potential source of long-term failure in a fuel cell membrane electrode assembly (MEA). While modifications to the CL ink formulation can affect the degree of cracking, these changes may lead to lower initial performance than their cracked analogues due to the established link between formulation and performance. In this work, we explored the use of polymeric additives to mitigate CL cracks. Small quantities of poly (acrylic acid), poly (ethylene oxide), poly (methyl methacrylate), or poly (vinyl alcohol) - 5 wt% relative to ionomer mass - were added to the ink prior to its final mixing. Poly (vinyl alcohol) resulted in crack-free CLs, whereas the other polymers resulted in CLs with similar crack percentages as the control CL. Through a combination of transmission electron microscopy, X-ray computed tomography, and infrared spectroscopy, we ascribed the crack-mitigating mechanism of poly (vinyl alcohol) to its ability to hydrogen-bond with Nafion, the ion conducting polymer binder in the catalyst ink. Initial performance of this non-cracked electrode exhibited nearly identical electrochemical behavior to its cracked counterpart, demonstrating that PVA additives successfully reduce cracks while maintaining cell initial performance.

30 DIRECT ENERGY CONVERSION↗

DOE OSTI2023

A scalable membrane electrode assembly architecture for efficient electrochemical conversion of CO2 to formic acid

Abstract The electrochemical reduction of carbon dioxide to formic acid is a promising pathway to improve CO 2 utilization and has potential applications as a hydrogen storage medium. In this work, a zero-gap membrane electrode assembly architecture is developed for the direct electrochemical synthesis of formic acid from carbon dioxide. The key technological advancement is a perforated cation exchange membrane, which, when utilized in a forward bias bipolar membrane configuration, allows formic acid generated at the membrane interface to exit through the anode flow field at concentrations up to 0.25 M. Having no additional interlayer components between the anode and cathode this concept is positioned to leverage currently available materials and stack designs ubiquitous in fuel cell and H 2 electrolysis, enabling a more rapid transition to scale and commercialization. The perforated cation exchange membrane configuration can achieve >75% Faradaic efficiency to formic acid at <2 V and 300 mA/cm 2 in a 25 cm 2 cell. More critically, a 55-hour stability test at 200 mA/cm 2 shows stable Faradaic efficiency and cell voltage. Technoeconomic analysis is utilized to illustrate a path towards achieving cost parity with current formic acid production methods.

08 HYDROGEN↗

DOE OSTI2023

Baselining Activity and Stability of ORR Catalysts and Electrodes for Proton Exchange Membrane Fuel Cells for Heavy-Duty Applications

Activity and stability of electrodes with Pt and PtCo alloy catalysts supported on high surface area carbon, hereafter to as a-Pt/C and d-PtCo/C, were evaluated for heavy-duty applications. Both catalysts had nearly identical Pt loading (50-wt% Pt on carbon and 0.25 mg Pt cm −2 ) and had undergone thermal treatment to stabilize them by growing the average particle size to 4–5 nm. Both were subjected to 90,000 (90 k) standard accelerated stress tests (AST) cycles consisting of 0.6–0.95 V square wave potentials, 3-s hold at upper and lower potential limits in H 2 /N 2 at 1.5 atm, 80 °C and 100% RH. Test protocols were developed to monitor the performance losses and characterize them in terms of activity for the oxygen reduction reaction (ORR), oxygen transport in the electrode and proton transport in the membrane and cathode catalyst layer. Despite the nearly double initial ORR activity, the PtCo/C electrode degraded faster due to the leaching of Co from the catalyst that had started even before the imposition of the AST potential cycles. Commensurate with Co leaching, Co poisoning of ionomer is responsible for the inferior performance of d-PtCo/C electrode at high current densities both before and after AST.

30 DIRECT ENERGY CONVERSION↗

DOE OSTI2022

Electrochemical characterization of evolving ionomer/electrocatalyst interactions throughout accelerated stress tests

Here, the degradation of polymer electrolyte membrane fuel cells (PEMFCs) catalyst layers used for heavy-duty vehicles was examined using a catalyst-specific accelerated stress test (AST). High surface area carbon supported dispersed Pt (Pt/HSC), annealed Pt (a-Pt/HSC) and PtCo (PtCo/HSC) alloy catalysts were examined over the course of 90,000 cycles by measuring changes in mass activity, O 2 transport resistance, electrochemical active surface area (ECSA), catalyst accessibility and ionomer-electrocatalyst interactions. Compared to a-Pt/HSC and Pt/HSC catalyst, the PtCo/HSC showed better initial mass activity, a larger initial mass transport loss, and faster degradation after the first 30k AST cycles, as a large portion of Co leached out during potential cycling. Pt/HSC showed higher initial performance relative to a-Pt/HSC but had faster degradation. STEM characterizations show that the ECSA losses are largely related to Pt dissolution resulting in either catalyst particle growth via the Ostwald ripening mechanism or redeposition in the membrane. Catalyst accessibility measurements showed decreased RH sensitivity for all three samples, while CO impedance measurements revealed a decrease in both Pt-water and carbon-water interactions. This implies that, Pt is either preferentially redepositing on the exterior of the carbon support, or that the ionomer is undergoing morphological changes enabling the enhanced intrusion of mesopores.

25 ENERGY STORAGE↗

DOE OSTI2020

Elucidating the Role of Ionomer in the Performance of Platinum Group Metal-free Catalyst Layer via in situ Electrochemical Diagnostics

The ionomer content in platinum group metal (PGM)-free polymer electrolyte fuel cell (PEFC) cathode catalyst layer (CCL) plays an important role in the electrode gas transport properties, proton conductivity, and hence, membrane electrode assembly (MEA) performance. In this work, the ionomer content in the CCL is varied, influencing electrode microstructure by altering porosity, tortuosity, as well as ionomer distribution and coverage of the catalyst particles. A novel technique consisting of a H 2 pump, combined with a Pt black sensor layer, is used to measure the bulk mass transport resistance of a series of PGM-free CCL prepared with different ionomer contents. The values for bulk electrode mass transport resistance are contrasted with electrode proton transport resistance in the cathode catalyst layer, establishing a clearly defined trade-off between two key performance limiting phenomena and identifying a need for novel PGM-free electrode fabrication strategies.

25 ENERGY STORAGE↗