NASA NTRS2010

Titanium Hydroxide - a Volatile Species at High Temperature

An alternative method of low-temperature plasma functionalization of carbon nanotubes provides for the simultaneous attachment of molecular groups of multiple (typically two or three) different species or different mixtures of species to carbon nanotubes at different locations within the same apparatus. This method is based on similar principles, and involves the use of mostly the same basic apparatus, as those of the methods described in "Low-Temperature Plasma Functionalization of Carbon Nanotubes" (ARC-14661-1), NASA Tech Briefs, Vol. 28, No. 5 (May 2004), page 45. The figure schematically depicts the basic apparatus used in the aforementioned method, with emphasis on features that distinguish the present alternative method from the other. In this method, one exploits the fact that the composition of the deposition plasma changes as the plasma flows from its source in the precursor chamber toward the nanotubes in the target chamber. As a result, carbon nanotubes mounted in the target chamber at different flow distances (d1, d2, d3 . . .) from the precursor chamber become functionalized with different species or different mixtures of species.

Nguyen, QuynhGiao N.↗

NASA NTRS2004

Oxidation of Ultra High Temperature Ceramics in Water Vapor

Ultra High Temperature Ceramics (UHTCs) including HfB2 + 20v/0 SiC (HS), ZrB2 + 20v/0 SiC (ZS), and ZrB2 + 30v/0 C + 14v/0 SiC (ZCS) have been investigated for use as potential aeropropulsion engine materials. These materials were oxidized in water vapor (90 percent) using a cyclic vertical furnace at 1 atm. The total exposure time was 10 h at temperatures of 1200, 1300, and 1400 C. CVD SiC was also evaluated as a baseline for comparison. Weight change, X-ray diffraction analyses, surface and cross-sectional SEM and EDS were performed. These results are compared with tests ran in a stagnant air furnace at temperatures of 1327 C for 100 min, and with high pressure burner rig (HPBR) results at 1100 and 1300 C at 6 atm for 50 h. Low velocity water vapor does not make a significant contribution to the oxidation rates of UHTCs when compared to stagnant air. The parabolic rate constants at 1300 C, range from 0.29 to 16.0 mg(sup 2)cm(sup 4)/h for HS and ZCS, respectively, with ZS results between these two values. Comparison of results for UHTCs tested in the furnace in 90 percent water vapor with HPBR results was difficult due to significant sample loss caused by spallation in the increased velocity of the HPBR. Total recession measurements are also reported for the two test environments.

Nguyen, QuynhGiao N.↗

NASA NTRS2003

Oxidation of Ultra-High Temperature Ceramics in Water Vapor

Ultra high temperature ceramics (UHTCs) including HfB2 + SiC (20% by volume), ZrB2 + SiC (20% by volume) and ZrB2 + SiC (14% by volume) + C (30% by volume) have historically been evaluated as reusable thermal protection systems for hypersonic vehicles. This study investigates UHTCs for use as potential combustion and aeropropulsion engine materials. These materials were oxidized in water vapor (90%) using a cyclic vertical furnace at 1 atm. The total exposure time was 10 hours at temperatures of 1200, 1300, and 1400 C. CVD SiC was also evaluated as a baseline comparison. Weight change measurements, X-ray diffraction analyses, surface and cross-sectional SEM and EDS were performed. These results will be compared with tests ran in static air at temperatures of 1327, 1627, and 1927 C. Oxidation comparisons will also be made to the study by Tripp. A small number of high pressure burner rig (HPBR) results at 1100 and 1300 C will also be discussed. Specific weight changes at all three temperatures along with the SIC results are shown. SiC weight change is negligible at such short duration times. HB2 + SiC (HS) performed the best out of all the tested UHTCS for all exposure temperatures. ZrB2 + Sic (ZS) results indicate a slightly lower oxidation rate than that of ZrBl + SiC + C (ZCS) at 1200 and 1400 C, but a clear distinction can not be made based on the limited number of tested samples. Scanning electron micrographs of the cross-sections of all the UHTCs were evaluated. A representative area for HS is presented at 1400 C for 26 hours which was the composition with the least amount of oxidation. A continuous SiO2 scale is present in the outer most edge of the surface. An image of ZCS is presented at 1400 C for 10 hours, which shows the most degradation of all the compositions studied. Here, the oxide surface is a mixture of ZrSiO4, ZrO2 and SO2.

Nguyen, QuynhGiao N.↗

NASA NTRS2002

Oxidation of a Silica-Containing Material in a Mach 0.3 Burner Rig

A primarily silica-containing material with traces of organic compounds, as well as aluminum and calcium additions, was exposed to a Mach 0.3 burner rig at atmospheric pressure using jet fuel. The sample was exposed for 5 continuous hours at 1370 C. Post exposure x-ray diffraction analyses indicate formation of cristobalite, quartz, NiO and Spinel (Al(Ni)CR2O4). The rig hardware is composed of a nickel-based superalloy with traces of Fe. These elements are indicated in the energy dispersive spectroscopy (EDS) results. This material was studied as a candidate for high temperature applications under an engine technology program.

Nguyen, QuynhGiao N.↗

NASA NTRS2001

Volatility and Wear Characteristics of a Variety of Liquid Lubricants for Space Applications

The vapor pressures and wear characteristics are critical properties for liquid lubricants to assure long-term reliability and performance in space applications. Vapor pressures, obtained using a Knudsen cell technique, and wear properties, obtained using a vacuum four-ball apparatus, were measured for a series of unformulated liquid lubricants. These included two multiply alkylated cyclopentanes (MACs) (X-1000 and X2000), two linear perfluoropolyalkylethers (PFPAEs) (Z-25 and 815Z), and four silahydrocarbons (a tri, a tetra, and two pentas). Vapor pressures were measured at three elevated temperatures (423, 448, and 498 K) and extrapolated to room temperature 298 K. The lowest 298 K vapor pressure of 5.7 x 10(exp -14) Pa was obtained with the PFPAE fluid (815Z) and the highest value with the low molecular weight MAC (X-1000) at 3.6 x 10(exp -7) Pa. In addition, vacuum wear rates were determined for some of the lubricants. The lowest wear rates (approximately 3 x 10(exp -11) cubic mm/mm) were observed for three of the silahydrocarbons while the highest wear rates (approximately 2 x 10(exp -9) cubic mm/mm) were observed with the two PFPAE fluids (Z-25 and 815Z). The MAC (X-2000) yielded a wear rate of about 10(exp -10) cubic mm/mm. The results indicated that the silahydrocarbon class of liquid lubricants offers the better potential for space applications.

Nguyen, QuynhGiao N.↗

NASA NTRS2000

A New Apparatus to Evaluate Lubricants for Space Applications: The Spiral Orbit Tribometer (SOT)

Lubricants used in space mechanisms must be thoroughly tested prior to their selection for critical applications. Traditionally, two types of tests have been used: accelerated and full-scale. Accelerated tests are rapid, economical, and provide useful information for gross screening of candidate lubricants. Although full-scale tests are more believable, because they mimic actual spacecraft conditions, they are expensive and time consuming. The spiral orbit tribometer compromises between the two extremes. It rapidly determines the rate of tribochemically induced lubricant consumption, which leads to finite test times, under realistic rolling/pivoting conditions that occur in angular contact bearings.

Jones, William R., Jr.↗

NASA NTRS1998

Oxidation of Chemically-Vapor-Deposited Silicon Carbide in Carbon Dioxide

Chemically-vapor-deposited silicon carbide (CVD SiC) was oxidized in carbon dioxide (CO2) at temperatures of 1200-1400 C for times between 96 and 500 h at several gas flow rates. Oxidation weight gains were monitored by thermogravimetric analysis (TGA) and were found to be very small and independent of temperature. Possible rate limiting kinetic mechanisms are discussed. Passive oxidation of SiC by CO2 is negligible compared to the rates measured for other oxidants that are also found in combustion environments, oxygen and water vapor.

Opila, Elizabeth J.↗