DOE OSTI2024

Identification and Suppression of Point Defects in Bromide Perovskite Single Crystals Enabling Gamma‐Ray Spectroscopy

Abstract Methylammonium lead tribromide (MAPbBr 3 ) stands out as the most easily grown wide‐band‐gap metal halide perovskite. It is a promising semiconductor for room‐temperature gamma‐ray ( γ ‐ray) spectroscopic detectors, but no operational devices are realized. This can be largely attributed to a lack of understanding of point defects and their influence on detector performance. Here, through a combination of crystal growth design and defect characterization, including positron annihilation and impedance spectroscopy, the presence of specific point defects are identified and correlated to detector performance. Methylammonium (MA) vacancies, MA interstitials, and Pb vacancies are identified as the dominant charge‐trapping defects in MAPbBr 3 crystals, while Br vacancies caused doping. The addition of excess MABr reduces the MA and Br defects and so enables the detection of energy‐resolved γ ‐ray spectra using a MAPbBr 3 single‐crystal device. Interestingly, the addition of formamidinium (FA) cations, which converted to methylformamidinium (MFA) cations by reaction with MA + during crystal growth further reduced MA defects. This enabled an energy resolution of 3.9% for the 662 keV 137 Cs line using a low bias of 100 V. The work provides direction toward enabling further improvements in wide‐bandgap perovskite‐based device performance by reducing detrimental defects.

Ni, Zhenyi↗

DOE OSTI2024

Unraveling radiation damage and healing mechanisms in halide perovskites using energy-tuned dual irradiation dosing

Perovskite photovoltaics have been shown to recover, or heal, after radiation damage. Here, we deconvolve the effects of radiation based on different energy loss mechanisms from incident protons which induce defects or can promote efficiency recovery. We design a dual dose experiment first exposing devices to low-energy protons efficient in creating atomic displacements. Devices are then irradiated with high-energy protons that interact differently. Correlated with modeling, high-energy protons (with increased ionizing energy loss component) effectively anneal the initial radiation damage, and recover the device efficiency, thus directly detailing the different interactions of irradiation. We relate these differences to the energy loss (ionization or non-ionization) using simulation. Dual dose experiments provide insight into understanding the radiation response of perovskite solar cells and highlight that radiation-matter interactions in soft lattice materials are distinct from conventional semiconductors. These results present electronic ionization as a unique handle to remedying defects and trap states in perovskites.

14 SOLAR ENERGY↗

DOE OSTI2024

Surface-Defect-Passivation-Enabled Near-Unity Charge Collection Efficiency in Bromide-Based Perovskite Gamma-Ray Spectrum Devices

Hybrid lead halide perovskites have superior charge transport properties to all-inorganic perovskites, but high-resolution spectroscopic radiation detectors have not been realized. Here we show that surface deep traps severely limit charge collection in formamidinium lead bromide (FAPbBr3) single-crystal devices, despite having a good bulk transport property. Three types of defect on the crystal surface, namely, FA vacancies, uncoordinated lead and Pb-Pb dimers caused by bromide loss, are found to form deep traps, resulting in non-radiative charge recombinations at the metal/perovskite interface. By tailoring the passivation functional groups, we find that ammonium bromide can passivate all these three deep traps on FAPbBr3 surfaces, improving the charge collection efficiency to near unity. The comparable bulk and surface recombination lifetimes indicate that all the surface defects are effectively passivated. Surface passivation also reduces the dark current by 10 times and decreases the dark counts by ~60 times. The energy resolution of the 137Cs spectra acquired using the FAPbBr3 detectors is improved from 5.7% to 1.7% when all the surface defects are passivated without changing the bulk properties, which is the best among solution-grown semiconductor detectors. Surface passivation is stable for more than six months, and FAPbBr3 spectroscopic detectors can operate at unprecedented high temperatures of more than 130 degrees C.