Nick Spangler | Search NASA

NASA NTRS2024

Passively Cooled Superconductors in Space

The objective of this project was to determine to what extent (as a function of distance from the Sun) our “Solar White” coatings could passively chill a high temperature superconductor (HTS) and maintain it in a superconducting state. The end goal is to enable the use of superconductors in space for active radiation shielding and highly efficient energy storage and retrieval. The best we were able to demonstrate during this testing was a coating with a solar absorptivity of 2.6%, which is sufficient to keep the superconductor we chose cold enough for these purposes at distances of 1.25 astronomical units (AU) from the Sun. Computations and modeling show that we would need samples with solar absorptivities of less than 1.5% for 1 AU and beyond operation. Our best tile to date was measured as having 1% absorption, which is still an order of magnitude higher than our theoretical limit. This should be achievable once manufacturing consistency is achieved. We are in the process of commercializing production of Solar White, and are hopeful that more consistent and improved results will be achieved within the coming year.

Mark Nurge↗

NASA NTRS2023

Passively Cooled Superconductors Final Report

A highly reflective spray-on coating and tile material has been under development at Kennedy Space Center (KSC) that scatters away most of the Sun’s energy, thereby allowing coated objects to remain cool in space. The best performing tile material has achieved 1% solar absorptivity while the best performing spray-on coating has achieved around 4%. Both versions passively maintain cryogenic temperatures below 120 K at 1 astronomical unit (AU) from the Sun, but the tile material consistently sustains temperatures below 90 K, which is low enough to preserve oxygen and methane in a liquid state. Besides keeping propellants cold, this “solar white” material has the potential to passively maintain high-temperature superconductors (HTS) in a superconducting state without the support of liquid nitrogen cooling. If superconductors can be operated without the added infrastructure of liquid nitrogen cooling, it may enable them to be used in space for applications like magnetic radiation shielding and efficient energy management. Long duration exposure to both galactic cosmic radiation and coronal mass ejections can pose health risks for the astronauts and increase the potential for damage to electronics. This makes shielding essential to accomplish long duration missions, particularly when astronauts are onboard. The objective of this project was to determine the extent we could keep a high-temperature superconducting (HTS) material passively chilled to maintain its superconducting state. Both the tile and spray-on versions of solar white were investigated. We focused on finding a version that could support passive cooling at 1 AU from the Sun and determined the closest operating distances for samples that were unable to perform at 1 AU. Early in the project, we selected bismuth strontium calcium copper oxide (BSCCO) as the HTS to test based on its reputable usage in superconducting wires. The version we selected was Bi-2223, which has a critical temperature of about 108 K. Sample bars with contacts for a four-point probe were obtained from Quantum Levitation: https://quantumlevitation.com/product/superconductor-bar-for-4-point-tc-experiment/.

superconductors↗