Engineering topics
Publications and source records attributed to Niiro, T..
Fabrication method produces unidirectional, multi-ply, transparent birefringent fibrous composite laminates for use in macromechanical stress analysis conducted by means of anisotropic photoelasticity. New laminates glass-fiber-reinforced plastics for which matrix and fibers have same index of refraction. Method utilized in structural applications of composites.
Materials were selected and fabrication procedures developed for orthotropic birefringent materials. An epoxy resin (Maraset 658/558 system) was selected as the matrix material. Fibers obtained from style 3733 glass cloth and type 1062 glass roving were used as reinforcement. Two different fabrication procedures were used. In the first one, layers of unidirectional fibers removed from the glass cloth were stacked, impregnated with resin, bagged and cured in the autoclave at an elevated temperature. In the second procedure, the glass roving was drywound over metal frames, impregnated with resin and cured at room temperature under pressure and vacuum in an autoclave. Unidirectional, angle-ply and quasi-isotropic laminates of two thicknesses and with embedded flaws were fabricated. The matrix and the unidirectional glass/epoxy material were fully characterized. The density, fiber volume ratio, mechanical, and optical properties were determined. The fiber volume ratio was over 0.50. Birefringent properties were in good agreement with predictions based on a stress proportioning concept and also, with one exception, with properties predicted by a finite element analysis. Previously announced in STAR as N81-26183
Materials were selected and fabrication procedures developed for orthotropic birefringent materials. An epoxy resin (Maraset 658/558 system) was selected as the matrix material. Fibers obtained from style 3733 glass cloth and type 1062 glass roving were used as reinforcement. Two different fabrication procedures were used. In the first one, layers of unidirectional fibers removed from the glass cloth were stacked, impregnated with resin, bagged and cured in the autoclave at an elevated temperature. In the second procedure, the glass roving was drywound over metal frames, impregnated with resin and cured at room temperature under pressure and vacuum in an autoclave. Unidirectional, angle-ply and quasi-isotropic laminates of two thicknesses and with embedded flaws were fabricated. The matrix and the unidirectional glass/epoxy material were fully characterized. The density, fiber volume ratio, mechanical, and optical properties were determined. The fiber volume ratio was over 0.50. Birefringent properties were in good agreement with predictions based on a stress proportioning concept and also, with one exception, with properties predicted by a finite element analysis.
The tooling and techniques used in the fabrication of composite laminate tubes of any desired ply orientation and stacking sequence are described along with techniques for cutting ring specimens under internal pressure. The method consists of laying up the tube on a central circular mandrel, and by means of internal pressure, expanding the prepreg tube against the cavity wall of an external mold tool, which forms the geometric curing envelope for the tube. Tube quality is assessed by laminate wall thickness measurement, by hoop strength measurement on rings cut from the ends of the tube, and by ultrasonic inspection.