DOE OSTI2024

Electrical property enhancement of non-heat-treatable wrought aluminum alloys using graphene additives

With growing efforts of electrification, aluminum’s role as a light-weight conductor material has become increasingly prominent. There is a critical need to improve the electrical performance of aluminum at room temperature and high operating temperatures. In this study, the effect of graphene nanoparticle additives on the electrical performance of a non-heat treatable alloy were (AA3003) explored. Graphene’s unusual structure and electronic properties were used to improve AA3003 properties. Here, in this work, the effects of graphene on the evolution of electrical properties and microstructural features have been explored on lab scale hot extruded AA3003-graphene composites. Hot pressing schedules and extrusion temperatures were varied to investigate changes in intermetallic dispersion characteristics in the presence of dispersed graphene. We measured a reduction of 10.3 % in the temperature coefficient of resistance in the AA3003 sample with 0.05 wt% graphene extruded at 400 °C, along with a maximum increase of 1.1 % in electrical conductivity at 20 °C. Increasing the hot-pressing times up to 8 hours was also found to consistently increase the electrical conductivity, due to increased precipitation of intermetallic phases. Despite being a non-heat treatable alloy, AA3003 displays interesting precipitation dynamics and grain recrystallization trends that can be modulated with varying levels of heat treatment, graphene concentrations, and hot extrusion process parameters.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Solid Phase Processing of Lead-Free Brass with Carbon Additives

Currently, “lead-free” brass alloys (like C27450/C27451/C6930), used extensively in drinking water fixtures and automotive, electrical, and electronic applications contain maximum 0.25% lead to maintain mechanical performance and machinability. Adding graphite to brass as an alternative to lead, using casting, powder metallurgy, and extrusion methods, has been explored previously. However, all these methods have proven to be energy-, time-, and resource-intensive, while not enabling performance equivalent to that of C36000 brass. In this project, we developed a one-step approach using friction extrusion and ShAPE to make lead-free brass/graphite components such as wires, rods and tubes with mechanical performance equivalent to commercial lead-free brass alloys. Manufacturing temperatures were maintained ~550-730 °C with feed rates ranging between 4 – 25 mm/min. Results show larger grains at the center of the rods and wires with smaller grains developing at the edges. Graphite particles were sheared in the direction of extrusion with higher strains observed towards the edges. Hardness of the brass/graphite samples was over 25% higher than that of the corresponding brass-only samples (rods and wires), also friction extruded. Our results show that the sub-micron graphite plays an important role in limiting process temperature and restraining grain growth during friction extrusion, thus reducing grain size in composites.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Macro copper-graphene composites with enhanced electrical conductivity

Composites demonstrating simultaneously enhanced-electrical conductivity, current density and lowered-temperature coefficient of resistance (TCR) compared to copper have been highly sought after for their advantages in efficient energy transport behavior. While such conductors have been demonstrated in 1D (nanowires) and 2D (films) samples, achieving similar behavior in 3D has been challenging owing to the limitations of the synthesis techniques used. In this paper, novel macro-scale 3D copper conductors were demonstrated with simultaneously increased electrical conductivity and decreased temperature coefficient of resistance (TCR) through the addition of graphene. Hot-extrusion was used to manufacture over 1-m-long, 2-mm-diameter copper-graphene composites with varying graphene content and defect density. Results showed that the electrical conductivity and current density in composites with low defect density graphene increased monotonically as a function of graphene content. They also demonstrated a significant decrease of over 17% in TCR with the addition of only 15 ppm graphene along with over 52% improvement in current density. Comparatively composites with high defect density graphene demonstrated lower electrical conductivity and current density. This study provides first-of-its-kind evidence of 3D metal composites whose bulk electrical performance has been enhanced using graphene additive in minute quantities. Further developments in this area are essential to achieve high performance composite conductors that can improve energy transport efficiency and pave way for industrial adoption of such materials in the future.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Evaluating Effects of Shear Processing on 2D Crystalline Materials in 3D Metal Matrices: Atomistic Understanding of High Shear Deformation of Copper Graphene Composites

Composites made of copper and graphene demonstrate high strength, lubricity and enhanced electrical and thermal conductivity compared pure copper. However, manufacturing these composites at bulk volumes for industrial applications has been a big challenge. Shear deformation assisted processing is an effective method for manufacturing materials such as copper-graphene composites demonstrating ultra-fine grain structures and compositional homogeneity. Nevertheless, microstructural evolution of the composites and their property development under such conditions is not clearly understood currently. To rectify this gap in literature, high strain shear deformation of copper coated graphene foils was performed using a tribometer pin in this study. Changes in microstructure of the composite as well as the constituent components under shear deformation was correlated to process conditions. A sharp increase in the coefficient of friction attributed to rupture and smearing of graphene layer into copper substrate was observed during the shear processing. The coefficient of friction of the sheared copper/graphene composite was lower than that of pure copper, suggesting that partially worn graphene is effectively lubricious at the macroscale. A multimodal characterization of the processed region further revealed a shear deformation-induced ultrafine two-phase grain-structure consisting of copper and graphitic domains. Shear deformation reduced the copper grain size from around 50 – 100 µm to ~200 nm on an average and ~2 – 5 nm in some locations. The semicrystalline graphene films were observed to fracture into 10 – 50 µm size flakes. Oxygen enrichment was observed in the processed region. Finally, graphitic domain were identified for the first time in the copper matrix and not just at the grain boundaries providing evidence for a metastable composite microstructure as a result of solid phase processing at room temperature.

36 MATERIALS SCIENCE↗