Interlocking metasurfaces
Abstract Interlocking metasurfaces (ILMs) are architected arrays of mating features that enable joining of two bodies. Complementary to traditional joining technologies such as bolts, adhesives, and welds, ILMs combine ease of assembly, removal, and reassembly with robust mechanical properties. Structural in nature, they act in a quasi-continuous manner across a surface and enable joining of complex surfaces, e.g., lattices. In this perspective, we define an ILM, begin exploring the design domain and illustrate its breath, and pragmatically evaluate mechanical performance and manufacturability. ILMs will find applications in various fields from aerospace to micro-robotics, civil engineering, and prosthetics.
Ductile failure and damage localization in Al6061-T6 characterized by in situ X-ray computed tomography and neural network segmentation
Damage initiation and localization in uniaxial tension tests of an Al6061-T6 alloy are evaluated and quantified using in situ X-ray computed tomography and a neural network segmentation strategy. This segmentation strategy offers significant advantages over traditional thresholding in quantifying microstructural and damage evolution metrics. Void nucleation was observed to occur throughout the deformation process, whereas void volume did not grow significantly until later stages of deformation. Localized analysis determined that void nucleation begins in and around the necked region during the early stages of deformation, whereas limited damage nucleation occurs outside of the neck until late stages of deformation. Lastly, inhomogeneities in void and particle spacing in the initial undeformed state of the material are observed to correlate well with the location of damage localization and necking during deformation. These results provide new insights into the ductile failure of Al alloys and how preexisting defects influence damage and rupture.