Nolen, J. Ryan

Publications and source records attributed to Nolen, J. Ryan.

4 records

DOE OSTI2022

Tunable, Homoepitaxial Hyperbolic Metamaterials Enabled by High Mobility CdO

We report propagating light exhibits hyperbolicity in strongly anisotropic materials where the principal components of the dielectric tensor are opposite in sign. While hyperbolicity occurs naturally in anisotropic polar dielectrics, wherein optical phonons along orthogonal crystal axes are nondegenerate, such optical anisotropy can also be engineered in hyperbolic metamaterials (HMMs): thin film superlattices of alternating dielectric and metallic layers. Contrasted with the severely limited tunability of natural hyperbolic materials, the hyperbolic behavior of HMMs can be tailored significantly both through superlattice design and material selection. However, so far HMMs have suffered from high optical losses, hindering their performance. In this report, broadly tunable (λ = 2–5 µm) Type I and II hyperbolic modes with low losses (quality (Q)-factors up to 19.7) are observed through attenuated total reflectance measurements of monolithic, homoepitaxial superlattices of high- and low-doped cadmium oxide (CdO). Further, the low losses offered by CdO enable the first demonstration of real-space imaging of hyperbolic plasmon polaritons in nanoresonators by scattering-type scanning near-field optical microscopy—previously only possible for hyperbolic phonon polariton materials. Tunable, low-loss CdO HMMs promise designability for applications such as on-chip photonics, super-resolution imaging (hyperlensing), enhanced emission, novel emitter designs, and possibly quantum nanophotonic and time variant metasurfaces.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Collective Phonon–Polaritonic Modes in Silicon Carbide Subarrays

Localized surface phonon polaritons (LSPhPs) can be implemented to engineer light–matter interactions through nanoscale patterning for a range of midinfrared application spaces. However, the polar material systems studied to date have mainly focused on simple designs featuring a single element in the periodic unit cell. Increasing the complexity of the unit cell can serve to modify the resonant near-fields and intra- and inter-unit-cell coupling as well as to dictate spectral tuning in the far-field. In this work, we exploit more complicated unit-cell structures to realize LSPhP modes with additional degrees of design freedom, which are largely unexplored. Collectively excited LSPhP modes with distinctly symmetric and antisymmetric near-fields are supported in these subarray designs, which are based on nanopillars that are scaled by the number of subarray elements to ensure a constant unit-cell size. Moreover, we observe an anomalous mode-matching of the collective symmetric mode in our fabricated subarrays that is robust to changing numbers of pillars within the subarrays as well as to defects intentionally introduced in the form of missing pillars. This work therefore illustrates the hierarchical design of tailored LSPhP resonances and modal near-field profiles simultaneously for a variety of IR applications such as surface-enhanced spectroscopies and biochemical sensing.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

Mid-wave to near-IR optoelectronic properties and epsilon-near-zero behavior in indium-doped cadmium oxide

Indium-doped cadmium oxide (In:CdO) thin films exhibit tunable epsilon-near-zero (ENZ) modal frequencies across a wide spectral range, bridging the mid-wave and near-infrared (IR). In:CdO thin films are prepared by reactive cosputtering from metallic Cd and In targets using high-power impulse magnetron sputtering (HiPIMS) and radio frequency sputtering, respectively. Using this approach, CdO thin films with carrier concentrations ranging from 2.3 × 10 19 to 4.0 × 10 20 cm –3 and mobilities ranging from 300 to 400 cm 2 /Vs are readily achieved. UV-VIS absorption spectra are used to measure optical bandgap, revealing a Burstein-Moss shift of 0.58 eV across the doping range investigated. In this work, optical measurements demonstrate the tunability of near-perfect plasmonic ENZ absorption across the mid-wave and into the near-IR spectral ranges by controlling the carrier concentration through doping, while tuning the film thickness for impedance matching. In comparison to other dopants that can be introduced to HiPIMS-deposited CdO, In offers the largest range of carrier concentrations while maintaining high mobility, thus allowing for the widest accessibility of the IR spectrum of a single plasmonic material grown by sputtering.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Ultraviolet to far-infrared dielectric function of n -doped cadmium oxide thin films

Spectroscopic ellipsometry and Fourier transform infrared spectroscopy were applied to extract the ultraviolet to far-infrared (150 – 33333 cm -1 ) complex dielectric functions of high-quality, sputtered indium-doped cadmium oxide (In:CdO) thin crystalline films on MgO substrates possessing carrier densities (N d ) ranging from 1.1 x 10 19 cm -1 to 4.1 x 10 20 cm -1 . A multiple oscillator fit model was used to identify and analyze the three major contributors to the dielectric function and their dependence on doping density: interband transitions in the visible, free-carrier excitations (Drude response) in the near- to far-infrared, and IR-active optic phonons in the far-infrared. More specifically, values pertinent to the complex dielectric function such as the optical band gap (E g ), are shown here to be dependent upon carrier density, increasing from approximately 2.5–3 eV, while the high-frequency permittivity (ε ∞ ) decreases from 5.6 to 5.1 with increasing carrier density. The plasma frequency (ω p ) scales as $\sqrt{N_d}$, resulting in ω p values occurring within the mid- to near-IR, and the effective mass (m *) was also observed to exhibit doping density-dependent changes, reaching a minimum of 0.11 m o in unintentionally doped films (1.1 x 10 19 cm -1 ). Good quantitative agreement with prior work on polycrystalline, higher-doped CdO films is also demonstrated, illustrating the generality of the results. The analysis presented here in this paper will aid in predictive calculations for CdO-based next-generation nanophotonic and optoelectronic devices, while also providing an underlying physical description of the key properties dictating the dielectric response in this atypical semiconductor system.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗