DOE OSTI2022

4D evolution of Cr 23 C 6 precipitates in neutron-irradiated and annealed HT-UPS steel observed via synchrotron micro-computed tomography

High-temperature-ultrafine precipitate strengthened (HT-UPS) steel is a potential structural material for advanced nuclear reactors; however, its irradiation response is not well understood. This research provides insight into irradiation-induced effects, such as precipitate evolution mechanisms and four-dimensional morphological evolution, in HT-UPS steel using synchrotron micro-computed tomography. Identical specimens were characterized pre-irradiation and post-irradiation following neutron exposure up to 0.3 displacements per atom at 600 °C. Irradiation effects were also differentiated from the annealing response of precipitates. Following neutron irradiation, the average Cr 23 C 6 precipitate size reduced, affected by the synergy of nucleation and growth, ballistic dissolution, and inverse coarsening, which was observed at fluences an order of magnitude lower than previously observed. Annealing at 600 °C for 32 h increased the average Cr 23 C 6 precipitate size and decreased the phase fraction, attributed to precipitate coarsening. The precipitate morphology evolution and resultant mechanisms can be utilized to parameterize and validate microstructural models simulating radiation damage or annealing.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Revealing the chemical environment of Cr, Fe, and Ni in high temperature-ultrafine precipitate strengthened steel subjected to low fluence neutron irradiation

High-temperature ultrafine-precipitate-strengthened (HT-UPS) steel has potential applications in advanced nuclear reactors as a structural material. However, little is currently known about its response to neutron irradiation. This research provides insight into the neutron irradiation-induced physicochemical changes of the major constituents in HT-UPS steels, including Fe, Cr, and Ni, using synchrotron X-ray absorption near edge structure (XANES) and diffraction. This study is the first known investigation using XANES to characterize HT-UPS steel to analyze the evolution of the atomic level chemistry. It was found that following irradiation, nucleation, ballistic dispersion, and/or coarsening of Cr 23 C 6 precipitates occurred at very low neutron irradiation fluences, from 0.003 displacements per atom (dpa) up to 0.3 dpa, at ~600°C, which were at least an order of magnitude lower than previous studies. Calculations of the angular momentum projections, partial density of states, and the XANES spectra confirmed the experimental findings of the Cr 23 C 6 precipitate evolution. In contrast, the local atomic structure around Fe and Ni atoms demonstrated irradiation resistance.

36 MATERIALS SCIENCE↗

DOE OSTI2020

The application of synchrotron micro-computed tomography to characterize the three-dimensional microstructure in irradiated nuclear fuel

This research demonstrated the first time that synchrotron X-ray micro-computed tomography (μ-CT) was utilized to analyze the three-dimensional (3-D) morphology of the microstructure of irradiated nuclear fuel. Both absorption contrast and propagation-based phase contrast enhanced μ-CT techniques were evaluated. Porosity and phase region volumes were determined in neutron irradiated uranium 10 wt.% zirconium (U-10Zr) using propagation-based phase contrast enhanced μ-CT. Volumes were determined by image processing software and algorithms, with the porosity volume subsequently compared to the ASTM E562 method. The 3-D porosity of a small region (~ 8 x 10 5 µm 3 ) located in the intermediate fuel redistribution zone that was removed via a focused ion beam was determined to be 7.2% via image processing. A detailed 3-D analysis of the porosity with respect to volume and morphology was provided. Five growth stages of pore evolution were observed including: nucleation, growth, coalescence, interconnected porosity, and extended/interconnected porosity. Four distinct phase regions were identified, including the pores, via both absorption contrast and propagation-based phase contrast enhanced μ-CT. A quantitative comparison of fuel swelling between this localized microscopic U-10Zr fuel region, previously irradiated in the Fast Flux Test Facility, and historic U-10Zr fuels irradiated in the Experimental Breeder Reactor-II (EBR-II) was conducted. It was determined that for similar burnups, the localized swelling in this microscopic fuel region was 7.7%, which was approximately one-half of the value of the macroscopic swelling reported in EBR-II irradiated fuel. With the advent of new specimen preparation tools for irradiated materials, as well as advances in characterization techniques, researchers can now obtain previously inaccessible microstructural insight into irradiated fuels. This possibility naturally lends itself to improved fuel performance models for the nuclear community.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗