DOE OSTI2023

Grain size dependence of thermally induced oxidation in zirconium carbide

Here complementary analytical approaches were employed to probe the effect of grain size on thermally induced oxidation of zirconium carbide (ZrC) utilizing thermogravimetric analysis, differential scanning calorimetry, and Raman spectroscopy, as well as synchrotron-based and laboratory-based X-ray diffraction (XRD) experiments. The oxidation mechanism and phase behavior of nanocrystalline ZrC (grain size ~ 20 nm) were compared with that of the more documented microcrystalline ZrC (grain size ~ 1 µm). Synchrotron XRD at the Advanced Photon Source with a hydrothermal diamond anvil cell (HDAC) used as a sample chamber revealed that the onset of oxidation is at ~ 380 °C for microcrystalline ZrC which is in agreement with previous work. In contrast, the critical oxidation temperature was ~ 330 °C for nanocrystalline ZrC. Additional high-temperature synchrotron XRD experiments at the National Synchrotron Light Source II using a lamp furnace in combination with Raman analysis showed that tetragonal ZrO 2 forms as an initial oxidation product and transforms at higher temperatures to the monoclinic phase. Thermogravimetric analysis (TGA) coupled with differential scanning calorimetry (DSC) confirmed the X-ray results of a lower critical oxidation temperature for the nanocrystalline sample. The phase transformations in the oxide phase with associated critical temperatures were also evident in the thermodynamic data as exothermic heat events.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2022

Cation Short-Range Ordering of MgAl 2 O 4 and NiAl 2 O 4 Spinel Oxides at High Temperatures via In Situ Neutron Total Scattering

Complex oxides that adopt the isometric spinel structure (AB 2 O 4 ) are important for numerous technological applications and are relevant for certain geological processes, which involve exposure to extreme environments such as high pressures and temperatures. Recent studies have shown that the changes to the spinel structure caused by these environments are complex and depend on the material length scale under consideration. In this study we have expanded this approach to the behavior of spinels under high temperature. In situ neutron total scattering experiments, coupled with pair distribution function analysis, performed on two spinel compositions with various levels of pre-existing disorder (MgAl 2 O 4 and NiAl 2 O 4 ) revealed that both compositions trend to a state of maximum disorder where the A and B cations are randomly distributed amongst the two available sites. Temperature-induced cation inversion, conventionally understood as exchange of cations on the A and B sites, is locally expressed as an atomic rearrangement to a tetragonal symmetry, a correlation that is retained up to the maximum temperature studied (1000 °C). Furthermore, a complex thermal expansion behavior is revealed wherein the oxide materials expand heterogeneously at the level of coordination polyhedral with an apparent dependence on bond strength.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Defining the Structural Stability Field of Disordered Fluorite Oxides

Fluorite-structured oxides constitute an important class of materials for energy technologies. Despite their high level of structural symmetry and simplicity, these materials can accommodate atomic disorder without losing crystallinity, making them indispensable for uses in environments with high temperature, changing chemical compositions, or intense radiation fields. In this contribution, we present a set of simple rules that predict whether a compound may adopt a disordered fluorite structure. This approach is closely aligned with Pauling’s rules for ionic crystal structures and Goldschmidt’s rules for ionic substitution.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Transformations to amorphous and X-type phases in swift heavy ion-irradiated Ln 2 O 3 and Mn 2 O 3

The intense, highly localized electronic excitation resulting from swift heavy ion irradiation induces phase transformations in many materials, including the lanthanide sesquioxides (Ln 2 O 3 ). To explore the effects of chemical composition on radiation-induced transformations, the structural responses of several related sesquioxides to swift heavy ion irradiation were compared. Polycrystalline Nd 2 O 3 , Eu 2 O 3 , Yb 2 O 3 , and Mn 2 O 3 were irradiated by 946 MeV Au ions to a range of ion fluences up to 2 × 10 13 cm -2 , and structural modifications were characterized using beamline-based in situ x-ray diffraction (XRD) and Rietveld refinement. Amorphization was induced in Nd 2 O 3 , Eu 2 O 3 , and Mn 2 O 3 , with the extent of the induced transformation following a clear dependence on cation ionic radius. Nd 2 O 3 and Eu 2 O 3 , having the largest cations, rapidly amorphized, whereas Mn 2 O 3 , having the smallest cation, experienced only a slight loss of crystallinity at the highest fluences studied. The radiation response was different for Yb 2 O 3 , which underwent a sluggish transformation to a nonequilibrium X-type phase. Furthermore, the crystalline-to-amorphous transformations proceeded by direct-impact mechanisms, while the C-to-X transformation proceeded by a multi-impact mechanism.

73 NUCLEAR PHYSICS AND RADIATION PHYSICS↗
DOE OSTI2021

Comparison of short-range order in irradiated dysprosium titanates

Abstract The structural response of Dy 2 TiO 5 oxide under swift heavy ion irradiation (2.2 GeV Au ions) was studied over a range of structural length scales utilizing neutron total scattering experiments. Refinement of diffraction data confirms that the long-range orthorhombic structure is susceptible to ion beam-induced amorphization with limited crystalline fraction remaining after irradiation to 8 × 10 12 ions/cm 2 . In contrast, the local atomic arrangement, examined through pair distribution function analysis, shows only subtle changes after irradiation and is still described best by the original orthorhombic structural model. A comparison to Dy 2 Ti 2 O 7 pyrochlore oxide under the same irradiation conditions reveals a different behavior: while the dysprosium titanate pyrochlore is more radiation resistant over the long-range with smaller degree of amorphization as compared to Dy 2 TiO 5 , the former involves more local atomic rearrangements, best described by a pyrochlore-to-weberite-type transformation. These results highlight the importance of short-range and medium-range order analysis for a comprehensive description of radiation behavior.

73 NUCLEAR PHYSICS AND RADIATION PHYSICS↗