Effects of Build Orientation and Heat Treatment on Neutron Irradiation Hardening in Inconel 625 Fabricated via Laser Powder Bed Fusion
Various Inconel 625 coupons fabricated via Laser Powder Bed Fusion (L-PBF) were neutron irradiated using the inside reflector of the reactor at the University of Missouri Research Reactor (MURR). Effects of build orientation and heat treatment on neutron-induced hardening were investigated by inspecting L-PBF samples built vertically or at a 45º angle in the following heat-treated conditions: as-built (no heat treatment), 700 ºC for 1 hour, 900 ºC for 1 hour, and 1050 ºC for 1 hour. The microhardness results of L-PBF samples before and after neutron irradiation were compared with traditional wrought Inconel 625. All samples underwent an irradiation flux of 6.61 x 1013 neutrons/cm²/s for 310 hours for an estimated damage of 0.012 dpa. Results indicate that as-built L-PBF specimens are less prone to radiation hardening relative to their wrought counterparts. As-printed diagonal specimens were shown to harden by 8% as compared to 1.2% hardening in as-printed vertical specimens.
Experiments with a prototype titanium hot cavity surface ionization source intended for electromagnetic separation of radioactive samarium and other lanthanide elements
This paper reports experimental results of a prototype titanium surface ionization source. For the first time, a lanthanide ion beam has been produced with a surface ionizer composed completely of titanium metal. Titanium does not readily activate with neutron irradiation. This offers the potential for inserting an ion source made of titanium directly into a reactor with a pre-loaded non-radioactive lanthanide target. This seamlessly integrates target irradiation with isotope separation, eliminating post irradiation sample manipulation. Samarium ion beam currents up to 960 nA have been produced in an off-line test bench equipped with rudimentary beam optics. This is a crucial step toward the development of an ionization source adopted for the electromagnetic isotope separator (EMIS) facility, which has been designed for high throughput separations of radioactive 153 Sm and other lanthanides of interest in the field of nuclear medicine. The ion current and important factors affecting the performance of the ion source, such as the ionizer temperature and thermal gradient, are discussed. Lastly, the experimental results are presented together with a discussion of future modifications to optimize the overall surface ionization source performance.