In-operando synchrotron experiments of flash sintering carried out in current rate mode

Here, we report first-time results for in-operando flash sintering synchrotron experiments carried out in current rate mode where the specimen, held at a constant temperature, is fed current that is increased at a constant rate. These experiments are unique because the time dependence of the sintering behavior can be stretched out over a longer period (by changing the current rate) than in voltage-to-current experiments in which sintering occurs in a burst at the onset of the flash. Two results are presented: (i) A comparison of temperatures measured with the platinum standard to those predicted by the black body radiation model leading to estimates of the emissivity as a function of porosity whereby emissivity increases from 0.65 to 0.9 as the sample sinters from its green state to full density, and (ii) measurements of the excess lattice expansion as a function of density as the sample sinters continuously while the current is increased. The present work highlights the promise of current rate experiments to obtain results while the sample sinters gradually from its green density to full density (somewhat akin to conventional sintering) for gaining further insights into the mechanisms of flash sintering.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Solid-State Sintering of Core-Shell Ceramic Powders Fabricated by Particle Atomic Layer Deposition

The properties of technical ceramics are highly dependent on their microstructure, which evolves during sintering. Sintering is the process by which ceramic parts are subjected to high temperatures to activate chemical diffusion and the consumption of porosity. During the initial stage of sintering, interparticle necks between neighboring particles form and subsequently increase in size, consuming porosity as the particle centers move closer together. To experimentally determine how this process depends on particle surface composition, particle atomic layer deposition (ALD) was used to deposit a thin film of amorphous aluminum oxide (Al2O3) onto yttria-stabilized tetragonal zirconia (3YSZ) particles, producing core-shell structured powders. The uniformity of the Al2O3 film was confirmed with transmission electron microscopy and energy dispersive spectroscopy. Scanning electron microscopy was used to observe microstructural evolution during sintering, and the dihedral angles of Al2O3 and 3YSZ grains were measured to determine the ratio of interfacial energies between the 3YSZ|3YSZ, 3YSZ|Al2O3, and Al2O3|Al2O3 interfaces. Analysis of the densification kinetics revealed that the initial stage of densification is dependent on the material at the surface of the particles (ie, the Al2O3 film) and is controlled by the diffusion of Al3+ cations through Al2O3. Once the Al2O3 film has coalesced, the sintering behavior is controlled by the densification of the core material (3YSZ). Thus, core-shell powders fabricated by particle ALD sinter by a two-step process where the kinetics are dependent on the material present at interparticle contacts.

alumina↗