Engineering topics

Oelrich, Jr., Robert L.

Publications and source records attributed to Oelrich, Jr., Robert L..

3 records

DOE OSTI2023

Grain boundary enhanced UN and U 3 Si 2 pellets with improved oxidation resistance

A method of forming a water resistant boundary on a fissile material for use in a water cooled nuclear reactor is described. The method comprises mixing a powdered fissile material selected from the group consisting of UN and U3Si2 with an additive selected from oxidation resistant materials having a melting or softening point lower than the sintering temperature of the fissile material, pressing the mixed fissile and additive materials into a pellet, sintering the pellet to a temperature greater than the melting point of the additive. Alternatively, if the melting point of the oxidation resistant particles is greater than the sintering temperature of UN or U3Si2, then the oxidation resistant particles can have a particle size distribution less than that of the UN or U3Si2.

Lahoda, Edward J.↗

DOE OSTI2021

Grain boundary enhanced UN and U3Si2 pellets with improved oxidation resistance

A method of forming a water resistant boundary on a fissile material for use in a water cooled nuclear reactor is described. The method comprises mixing a powdered fissile material selected from the group consisting of UN and U 3 Si 2 with an additive selected from oxidation resistant materials having a melting or softening point lower than the sintering temperature of the fissile material, pressing the mixed fissile and additive materials into a pellet, sintering the pellet to a temperature greater than the melting point of the additive. Alternatively, if the melting point of the oxidation resistant particles is greater than the sintering temperature of UN or U 3 Si 2 , then the oxidation resistant particles can have a particle size distribution less than that of the UN or U 3 Si 2 .

Lahoda, Edward J.↗

DOE OSTI2021

Duplex accident tolerant coating for nuclear fuel rods

A method is described for forming duplex layers including an interlayer and a corrosion resistant boundary layer on a nuclear fuel rod cladding tube for use in a water cooled nuclear reactor. The method includes forming, by thermal deposition or physical vapor deposition, on the exterior of a substrate, an inner interlayer with Mo, Ta, W or Nb or other particles, and forming, by thermal deposition or physical vapor deposition, on the interlayer, an outer corrosion resistant layer with particles selected from the group consisting of Cr, a Cr alloy, and combinations thereof. The interlayer prevents eutectic formation between the corrosion resistant layer and the substrate.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗