Electrical passivation of III-V multijunction solar cells with luminescent coupling effect
Perimeter recombination is one of the causes identified for having a nonuniform luminescent coupling effect in III-V multijunction solar cells. A potential solution could be the electrical passivation of the multijunction solar cell perimeter. To test this hypothesis, electrical passivation of InGaP/GaAs/Ge 3-junction solar cells was done by the atomic layer deposition of thin Al2O3 films. Further, perimeter passivation of a 3-junction solar cell relatively increased current collection measured at luminescent coupling and direct subcell excitation by as much as 11.4% and 29.8%, respectively. Meanwhile, the current homogeneity improved relatively by as much as 7.9% after electrical passivation. At 1-sun global standard illumination (AM 1.5G), 0.2% absolute conversion efficiency increase was achieved. Therefore, electrical passivation of fully working III-V multijunction solar cells is a non-invasive, post-treatment process that can recover losses due to surface defects caused by oxidation.