Olds, Travis | Search NASA

DOE OSTI2024

Trebiskyite, the First Titanium-Decavanadate Mineral

Abstract Trebiskyite, Na3Mg2[TiV9O28]·22H2O, from the Pickett Corral mine, Bull Canyon, Montrose County, Colorado, USA, is the first mineral containing essential Ti as a component of a decavanadate polyanion. Crystals are thin prisms or needles up to ∼0.3 mm in length, occurring as individuals and in divergent sprays. Trebiskyite crystals are translucent yellow with vitreous luster and pale-yellow streak and are non-fluorescent under both longwave and shortwave ultraviolet illumination. The crystals exhibit elongation on [001] and are modified by several 0kl prism forms, possibly corresponding to {010}, {011}, and {012}. The Mohs hardness is ca. 2 based on scratch tests. Crystals have brittle tenacity with irregular fracture. No apparent cleavage, nor twinning, was evident, and the mineral is readily soluble in H2O. The density measured by flotation in methylene iodide-toluene mixture is 2.38(2) g/cm3. The calculated density is 2.352 g/cm3 for the empirical formula and 2.343 g/cm3 for the ideal formula. Electron microprobe analyses provided the empirical formula Na3.39Mg1.87V8.75Ti1.25O50H44.00, based on Ti + V = 10 apfu, O = 50 apfu, with the Na content having been determined from the refined crystal structure. Trebiskyite is monoclinic, space group P21/c, a = 9.478(4), b = 21.426(11), c = 11.267(5) Å, β = 114.572(7)°, V = 2080.8(13) Å3, Z = 2. The structure was refined from 6642 reflections to a final R1 = 0.0517 for reflections I > 2σ(I). The structural unit of trebiskyite, (TiV9O28)7−, is built from a Ti-substituted decavanadate polyanion, (V10O28)6−, found in other members of the pascoite family. Chemically, trebiskyite is closely related to lasalite, Na2Mg2[V10O28]·20H2O, and huemulite, Na4Mg[V10O28]·24H2O; however, trebiskyite contains a novel structural arrangement that is unique among the decavanadate minerals. The interstitial complex in trebiskyite has the ideal formula {[Na3Mg2(H2O)19](H2O)3} and consists of chains of distorted octahedrally coordinated Na+ and regular Mg[O(H2O)5] octahedra. The observed low incident bond valence to the V1 site (4.45 vu) and marked deviation in vanadyl and V–Oeq bond lengths indicate that this site is host to the essential Ti4+ identified during chemical analyses.

Mineralogy↗

DOE OSTI2022

Benefits of using multiple Raman laser wavelengths for characterizing defects in a UO 2 matrix

Abstract Raman spectroscopy is one of the most useful techniques for studying the structure of UO 2 and changes due to specific defects caused by doping, changes in stoichiometry, irradiation, or heating under oxidizing conditions. In this paper, we illustrate several aspects of the application of Raman techniques to the study of UO 2 , including the use of wavelength‐dependent excitation (455, 532, and 785 nm) to assess the effects of doping (Nd, Th, and Zr), ion irradiation, and in situ heating and oxidation (UO 2 to U 3 O 8 ). Additionally, we show examples of how correlative microscopy is possible using electron backscatter diffraction combined with Raman maps of specific vibration bands or of laser‐induced luminescence generated by rare‐earth dopants in the matrix. For each of these applications, we suggest optimal excitation wavelengths that vary depending on the desired data. Blue (455 nm) excitation tends to promote oxidation even at low powers, but because Raman spectra change little with doping, irradiation‐induced changes are easier to observe. Green (532 nm) excitation is optimal for observing electron–phonon resonance effects in UO 2 and offers a good compromise for high‐temperature oxidation experiments, delivering high‐quality spectra for both UO 2 and U 3 O 8 . Infrared (785 nm) excitation is best for observing “defect” bands associated with doping in UO 2 , as changes with irradiation are small. Raman spectroscopy is particularly suited for studying the stability of UO 2 towards oxidation in the presence of dopants simulating fission products, where electron–phonon resonant effects, dopant ion luminescence, and mapping can be used together to investigate structural rearrangement as a function of temperature. These techniques can offer insight into microstructural changes in UO 2 fuels at higher burnups envisioned in future reactors.

42 ENGINEERING↗