DOE OSTI2024

Creep Degradation of Austenitic Steels in CO2 Environments

Steels have a proven track record of safe operation in steam power plants for decades. Interest in developing supercritical CO2 power cycles as a more efficient and sustainable alternative to steam cycles has driven a need to understand steel performance in these new environments. In particular, the potential of the high temperature CO2 environment to influence the creep behavior of the steel must be determined. Prior research on this topic between the 1960s and 1980s found conflicting conclusions, but nevertheless raised the possibility that carburization during CO2 exposure may strongly affect the creep behavior. This raises concerns particularly for thin-sectioned components such as compact heat exchangers, where even small rates of carburization can become problematic over long operating lifetimes. To shed light on this issue, this research investigates the creep behavior of austenitic stainless steel 347H and 309H (a higher Cr alternative) at 650°C. Specimens of 0.5, 1.0, and 2.0 mm thickness were tested to further assess the effect of steel thickness. Both steels show a reduction in creep life in CO2 relative to air, with 309H showing slightly better performance than 374H. Analysis is ongoing to determine the reason for degraded creep properties.

Rozman, Kyle A.↗
DOE OSTI2024

Creep behavior of austenitic steels in CO2 and the effect of specimen thickness

Steels have a proven track record of safe operation in steam power plants for decades. Interest in developing supercritical CO2 power cycles as a more efficient and sustainable alternative to steam cycles has driven a need to understand steel performance in these new environments. In particular, the potential of the high temperature CO2 environment to influence the creep behavior of the steel must be determined. Prior research on this topic between the 1960s and 1980s found conflicting conclusions, but nevertheless raised the possibility that carburization during CO2 exposure may strongly affect the creep behavior. This raises concerns particularly for thin-sectioned components such as compact heat exchangers, where even small rates of carburization can become problematic over long operating lifetimes. To shed light on this issue, this research investigates the creep behavior of austenitic stainless steel 347H and 309H (a higher Cr alternative) at 650°C. Specimens of 0.5, 1.0, and 2.0 mm thickness were tested to further assess the effect of steel thickness. Both steels show a reduction in creep life in CO2 relative to air, with 309H showing slightly better performance than 374H. Analysis is ongoing to determine the reason for degraded creep properties.

Rozman, Kyle A.↗
DOE OSTI2024

Phase-Field Modeling of Thermally-Grown Oxide and the Induced Damage Evolution in Environmental Barrier Coatings

The advent of next-generation hydrogen-based engines necessitates materials capable of withstanding temperatures beyond the reach of current superalloys. SiC-based ceramic matrix composites, augmented with environmental barrier coatings (EBCs), present a promising materials solution. Given the active search for effective and durable EBCs, there is a pressing need for modeling tools to understand and predict damage evolution in these materials to help accelerate their development. This study introduces a phase-field model (PFM) designed to simulate the critical role of thermally grown oxides (TGO) in the degradation and failure of EBCs. The model accounts for the severe volume expansion due to oxidation, alongside phase transformations and microstructural evolution during thermal cycling, offering a comprehensive view of the damage processes. Simulation results are validated against experimental findings reported in the literature, establishing the model's potential as a significant tool for understanding and improving the resilience of EBCs in cyclic oxidative environments.

Cheng, Tianle↗
DOE OSTI2024

High-Temperature Oxidation Behavior of Wrought and Additive Manufactured H282 in Direct-Fired Supercritical CO2 Power Cycle Environments

Materials selection is a key concern for corrosion resistance in high temperature and pressure direct-fired supercritical CO2 power cycles. The effect of elevated pressure on corrosion resistance can be critical, as impurities within the supercritical fluid such as H2O and O2 can result in additional corrosion behaviors. Utilizing additive manufacturing (AM) methods for construction of power cycle components requiring both compact and complex designs could be advantageous. AM H282 produced by laser powder bed fusion was exposed to direct-fired conditions (95CO2 – 4H2O – 1 O2) at 750 °C at both atmospheric pressure and supercritical conditions (20 MPa) for up to 4,000 hours. Oxidation behavior, sub-surface carbide formation, and chromia scale volatilization was dependent upon AM preparation techniques and surface modifications. These results are discussed in terms of the potential compatibility issues that may arise when using AM alloys in high temperature regions of direct-fired sCO2 power cycles, particularly for thin-walled components.

Carney, Casey↗
DOE OSTI2024

Phase-Field Modeling of Mechanical Damages in Ceramic Matrix Composites

Developed a phase-field model for mechanical damages in CMCs, which incorporates the CMC microstructures, matrix cracking, fiber breakage, and interfacial sliding. Two types of mechanisms, fiber bridging and fiber pull-out, are considered. The obtained simulation results agree with experimental observations and an analytical solution. Simulation results suggest that the performance of CMCs would be enhanced with thicker fibers, longer fibers, and higher fiber density. Opposite trends of interfacial sliding resistances are suggested for the two types of situations. In reality, a mixture of the two situations may exist, and then an intermediate interfacial sliding resistance may be optimal.

Xue, Fei↗
DOE OSTI2024

Environmental Compatibility Issues for Ni-Based Alloys in Direct-Fired Supercritical CO2 Power Cycles

Direct-fired supercritical CO2 (sCO2) power cycles offer potential for high-efficiency power generation from natural gas and other fossil fuels with built-in carbon capture. Ni-based superalloys are the leading candidates for the hottest portions of these systems, where they must endure long-term exposure to high-temperature, high-pressure, high-velocity, impure CO2-rich environments. Herein we describe results of various experimental testing campaigns conduced at NETL showing that under such conditions, several simultaneously occurring degradation modes may be active including surface oxidation, alloy carburization, and oxide volatilization. It will be shown that the rates of degradation can be strongly affected by the alloy composition, impurities in the CO2, manufacturing method (wrought vs additive), and other factors. The influence of these factors in controlling alloy degradation are discussed in the context of potential compatibility issues for components in real sCO2 systems, such as compact heat exchangers. Finally, as a potential remedial measure, ongoing work involving protective coatings suitable for complex geometries is presented.

alloy oxidation↗
DOE OSTI2024

Accelerated Design of Cost-Effective Thermal/Environmental Barrier Coatings based on High-Entropy Rare Earth Disilicates: A First-Principles Study

This project aims to design cost-effective thermal/environmental barrier coatings (TEBC) based on high entropy rare earth disilicates to protect SiC-based ceramic matrix composites from chemical and thermal attack for better performance of components in the hot section of gas turbine engines. To accelerate the alloy design, we utilize first-principles density functional theory (DFT) together with combinatorial chemistry methodology to predict key properties including phase stability, apparent bulk coefficient of thermal expansion (ABCTE), intrinsic lattice thermal conductivity, and temperature-dependent elastic constants. Specifically, this project focuses on β-RE2Si2O7 (RE=Yb, Y, Er, Lu, La, Ce,) with β-Yb2Si2O7 and β-Y2Si2O7 as the benchmark. Our DFT calculations predict that Er1/4Lu1/4Y3/4Yb3/4Si2O7 and Er1/2Lu1/2Y1/2Yb1/2Si2O7 have ultralow lattice thermal conductivity < 0.23 W/m/K at 1500 K and a good match of average ABCTE (5.1 - 5.2×10-6 K-1) with SiC. Owing to the low cost and abundant supply of Ce and La, the A- and G-La2Si2O7/Ce2Si2O7 disilicates are also studied. Our study shows that G-phase Ce2Si2O7 has an ultralow thermal conductivity (0.26 W/m/K at 1500 K) and the apparent bulk ABCTE (≈6.9×10-6 K-1) slightly higher than SiC, demonstrating great potential as low-cost high-performance T/EBC. However, La2Si2O7 and Ce2Si2O7 undergo an A-phase to G-phase polymorphic transition at around 1470 K.

environmental barrier coatings↗
DOE OSTI2024

Design and Evaluation of Environmental Barrier Coatings for Protection of Ceramic Matrix Composites in Hydrogen-Based Turbines

This presentation at the 2024 FECM Spring Project Review Meeting summarizes ongoing work at NETL aimed at enabling the use of ceramic matrix composite (CMC) materials in next-generation high-efficiency power generation turbines fueled by hydrogen, natural gas, or other fuels. The work broadly involves three aspects (1) phase-field damage modeling of CMCs and the environmental barrier coatings (EBCs) used to protect them (2) computational design of new and improved EBCs and (3) performance testing of EBCs using a novel gas turbine combustion simulation rig developed at NETL. An overview on current status and next steps for each aspect of the project are presented.

ceramic matrix composite (CMC)↗
DOE OSTI2024

Phase-Field Model Incorporating Large Inelastic Strain with Application to the Oxidation of High-Temperature Coating Systems

Structural metallic and ceramic materials at high temperatures often suffer from creep, fatigue and oxidation, which typically involves local large inelastic strain. The large strain is usually approached by Lagrangian-description-based finite deformation theory. Here we develop an efficient, Eulerian-description-based, Incremental Realization of Inelastic Deformation (IRID) algorithm to deal with large inelastic strain with small elastic strain. We apply this algorithm to simulate high temperature oxidation with severe volume expansion using a phase-field approach. The oxidation and deformation of bond coat can lead to spallation and failure of the thermal barrier coatings (TBC) and environmental barrier coatings (EBC), which is a critical concern in design of these coatings. We simulate the growth of thermally grown oxide (TGO) in these coating systems, with phase transformations and microstructure evolution incorporated. The simulation results are compared with relevant experimental reports in the literature.

Cheng, Tianle↗
DOE OSTI2024

Effect of Silicon on High Temperature Oxidation of Fe-Cr-Si Alloys in Carbon Dioxide Environments

Supercritical carbon dioxide offers the potential for efficient and sustainable power generation. Identifying materials that can be used to construct the high temperature portions of the cycle is a barrier to developing this technology. Various Fe-Cr alloys have been identified as promising construction materials due to a favorable combination of high temperature strength, commercial availability, and cost. The effect of minor alloying elements, particularly Si, has been shown to significantly impact the oxidation and carburization processes for these alloys after relatively short duration exposures in hot carbon dioxide. The long-term impact is less understood, making it challenging to predict performance of real components that will be in service for many years. The objectives in this project are to better understand the long-term oxidation and carburization behavior of Fe-Cr alloys and the important role of Si; to enhance the existing body of literature on the long-term exposure of alloys to hot carbon dioxide; and enable lifetime predictions for future supercritical carbon dioxide power cycle components.

Menna, Valerie↗
DOE OSTI2024

Effect of Minor Ce Additions on Corrosion Behavior of Experimental Pipeline Steel

Minor additions of rare earth elements (REEs) have been shown to improve various steel properties. In particular, Cerium (Ce), as a relatively abundant and inexpensive element, has received attention as a potentially beneficial minor alloying addition for a variety of steel applications, including pipelines materials. The objective of this work is to investigate the effect of Ce on corrosion performance of experimental high-strength pipeline steel. Electrochemical corrosion experiments were carried out on steel without and with 0.006, 0.018, and 0.03 wt.% of Ce in 3.5 wt.% NaCl saturated with CO2 at 20 oC. For comparison purposes, X100 carbon steel specimens machined from an experimental pipe with a yield strength of 731 MPa were tested under the same conditions. The electrochemical techniques employed included: potentiodynamic polarization (PDP), linear polarization resistance (LPR), and electrochemical impedance spectroscopy (EIS). In addition, post-corrosion surface characterization was performed using scanning electron microscopy (SEM) equipped with energy dispersive X-ray spectroscopy (EDS), while crystalline phases were determined by X-ray diffraction (XRD). The corrosion of base metal without Ce was lower (0.15 mm/y) compared to carbon steel X100 (0.9 mm/yr). The electrochemical results showed that adding Ce accelerates corrosion rates compared to base metal without Ce. No pitting corrosion of tested steel was detected.

Belarbi, Zineb↗
DOE OSTI2024

High-Temperature Oxidation Behavior of Wrought and Additive Manufactured Ni-based Alloys in Direct-Fired Supercritical CO2 Power Cycle Environments

Materials selection is a key concern for corrosion resistance in elevated temperature and pressure direct-fired supercritical CO2 (sCO2) power cycles. Herein, the wrought product form of alloy H282, as well as several additional nickel-based commercial alloys (230, 263, 617, 625, 740H), were exposed to direct-fired supercritical CO2 conditions (95CO2 – 4H2O – 1O2) at 750 °C and 20 MPa for over 2,000 h. Additionally, additive manufactured (AM) 282 produced by laser powder bed fusion (LPBF) were also included in the exposures. This paper focuses primarily on the differences observed in the degradation behavior of the wrought and additively manufactured materials. AM samples in the as-printed state were found to form less protective oxide scales resulting in higher oxidation rates compared to wrought samples. However, applying a 600 grit surface finish to the AM samples modified the oxidation behavior to closely resemble that of the wrought material. The AM samples formed Mo-rich carbides in the alloy beneath the oxide following sCO2 exposure, implying potentially higher levels of carbon uptake relative to the wrought material. Conversely, the AM samples seemed to be less affected by water-assisted oxide volatilization compared to the wrought material. The results are discussed in terms of the potential compatibility issues that may arise when using Ni-based alloys in the hot portions of direct-fired sCO2 power cycles, particularly in the case of thin-walled components.

Carney, Casey↗
DOE OSTI2024

High-Temperature Oxidation Behavior of Wrought and Additive Manufactured Alloys in Direct-Fired Supercritical CO2 Power Cycle Environments

Materials selection is a key concern for corrosion resistance in elevated temperature and pressure direct-fired supercritical CO2 (sCO2) power cycles. The effect of elevated pressure on corrosion resistance can be critical, as impurities within the supercritical fluid such as H2O and O2 can have additional corrosion effects than found at ambient pressure conditions. Several wrought nickel-based commercial alloys (230, 263, 282, 617, 625, 740H) were exposed to direct-fired conditions (95CO2 – 4H2O – 1 O2) at 750 °C at both atmospheric pressure (0.1 MPa) and supercritical conditions (20 MPa) for over 2,000 h. Additionally, additive manufactured (AM) 282 produced by laser powder bed fusion (LPBF) were also included in the exposures. Supercritical conditions affected the oxidation behavior of several alloys. Most notably, water-vapor assisted Cr-oxide volatilization was observed at 750 °C supercritical conditions. Many alloys did not form sufficient protective Cr-oxide scales at supercritical conditions, leading to increased oxidation at elevated pressure. Differences in oxidation behavior were also observed for 282 AM samples compared to their wrought counterparts, with the differences also dependent on the LPBF build parameters and post-production treatments (heat treatment and surface finishing procedures). The AM samples formed Mo-rich carbides in the alloy beneath the oxide following sCO2 exposure, implying potentially higher levels of carbon uptake relative to the wrought

Carney, Casey↗