DOE OSTI2023

Sub-quarter micrometer periodically poled Al 0.68 Sc 0.32 N for ultra-wideband photonics and acoustic devices

In this study, we demonstrate the ability of polarity inversion of sputtered aluminum scandium nitride thin films through post-fabrication processes with domain widths as small as 220 nm at a periodicity of 440 nm. An approach using photo- and electron-beam lithography to generate sub-quarter micrometer feature size with adjustable duty cycle through a lift-off process is presented. Here, the film with a coercive field $E_c^+$ of 5.35 MV/cm was exercised first with a 1 kHz triangular double bipolar wave and ultimately poled with a 0.5 kHz double monopolar wave using a Radiant Precision Premier II tester. The metal polar (M-polar) and nitrogen polar (N-polar) domains were identified and characterized through potassium hydroxide wet etching as well as piezoresponse force microscopy (PFM). Well-distinguished boundaries between the oppositely polarized domain regions were confirmed through the phase diagram of the PFM results. The relationship between the electrode width, poling voltage, and domain growth was experimentally studied and statistically analyzed, where 7.96 nm/V domain width broadening vs escalating poling voltage was observed. This method produces extremely high domain spatial resolution in III-nitride materials via poling and is transferable to a CMOS-compatible photolithography process. The spatial resolution of the periodically poled Al 0.68 Sc 0.32 N is suitable for second-harmonic generation of deep ultraviolet through quasi-phase-matching and RF MEMS operating in the X-Band spectrum.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Aluminum scandium nitride films for piezoelectric transduction into silicon at gigahertz frequencies

Recent advances in the growth of aluminum scandium nitride films on silicon suggest that this material platform could be applied for quantum electromechanical applications. Here, we model, fabricate, and characterize microwave frequency silicon phononic delay lines with transducers formed in an adjacent aluminum scandium nitride layer to evaluate aluminum scandium nitride films, at 32% scandium, on silicon interdigital transducers for piezoelectric transduction into suspended silicon membranes. We achieve an electromechanical coupling coefficient of 2.7% for the extensional symmetric-like Lamb mode supported in the suspended material stack and show how this coupling coefficient could be increased to at least 8.5%, which would further boost transduction efficiency and reduce the device footprint. The one-sided transduction efficiency, which quantifies the efficiency at which the source of microwave photons is converted to microwave phonons in the silicon membrane, is 10% at 5 GHz at room temperature and, as we discuss, there is a path to increase this toward near-unity efficiency based on a combination of modified device design and operation at cryogenic temperatures.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Ferroelectric behavior of sputter deposited Al 0.72 Sc 0.28 N approaching 5 nm thickness

Ferroelectric Al 1-x Sc x N has raised much interest in recent years due to its unique ferroelectric properties and complementary metal oxide semiconductor back-end-of-line compatible processing temperatures. Potential applications in embedded nonvolatile memory, however, require ferroelectric materials to switch at relatively low voltages. One approach to achieving a lower switching voltage is to significantly reduce the Al 1-x Sc x N thickness. In this work, ferroelectric behavior in 5-27 nm films of sputter deposited Al 0.72 Sc 0.28 N has been studied. We find that the 10 kHz normalized coercive field increases from 4.4 to 7.3 MV/cm when reducing the film thickness from 27.1 to 5.4 nm, while over the same thickness range, the characteristic breakdown field of a 12.5 μm radius capacitor increases from 8.3 to 12.1 MV/cm. In conclusion, the 5.4 nm film demonstrates ferroelectric switching at 5.5 V when excited with a 500 ns pulse and a switching speed of 60 ns.

30 DIRECT ENERGY CONVERSION↗
DOE OSTI2021

Neural interface methods and apparatus to provide artificial sensory capabilities to a subject

Embodiments of neural interfaces according to the present invention comprise sensor modules for sensing environmental attributes beyond the natural sensory capability of a subject, and communicating the attributes wirelessly to an external (ex-vivo) portable module attached to the subject. The ex-vivo module encodes and communicates the attributes via a transcutaneous inductively coupled link to an internal (in-vivo) module implanted within the subject. The in-vivo module converts the attribute information into electrical neural stimuli that are delivered to a peripheral nerve bundle within the subject, via an implanted electrode. Methods and apparatus according to the invention incorporate implantable batteries to power the in-vivo module allowing for transcutaneous bidirectional communication of low voltage (e.g. on the order of 5 volts) encoded signals as stimuli commands and neural responses, in a robust, low-error rate, communication channel with minimal effects to the subjects' skin.

Buerger, Stephen P.↗
DOE OSTI2021

Al 0.68 Sc 0.32 N Lamb wave resonators with electromechanical coupling coefficients near 10.28%

Aluminum scandium nitride (Al 1-x Sc x N/AlScN) (x = 0.32) Lamb wave resonators (LWR) have been fabricated and tested to demonstrate electromechanical coupling coefficients (k t 2 ) in excess of 10%. The resonators exhibited an average k t 2 and unloaded quality factor (Q u ) of 10.28% and 711, respectively, when calculated from the measured data. Applying the Butterworth Van-Dyke (BVD) model to the measured data enabled the extraction of the resonator's lumped element parameters to calculate the motional quality factor (Q m ), which neglects the contributions of the electrical traces. For the best measured resonator response, results from the BVD model showed a Q m of 1184 and a resulting figure-of-merit (FOM = K 2 ·Q m ) of 100. Comparing the response of similar AlScN and AlN resonators shows that the AlScN LWR has a significantly lower motional resistance (R m ), suggesting that AlScN has a strong potential for use in piezoelectric microelectromechanical oscillators.

42 ENGINEERING↗
DOE OSTI2020

Hybrid semiconductor-piezoacoustic radiofrequency device

An amplifying radiofrequency device includes a piezoelectric film and a semiconductor amplifier layer. The piezoelectric film is conformed as an acoustic waveguide. The piezoelectric film has a principal acoustic propagation direction parallel to the principal conduction direction of the amplifier layer. Interdigitated transducers are positioned on the piezoelectric film to respectively launch an acoustic wave in response to an input RF signal, and transduce the acoustic wave back to an output RF signal. There is a distance of less than the acoustic wavelength between the semiconductor amplifier layer and the piezoelectric film. The piezoelectric film has a thickness of less than the acoustic wavelength. According to a method for making such a device, a stack of III-V layers is epitaxially grown on a III-V substrate, wherein the stack comprises a first etch stop layer, a second etch stop layer, an amplifier layer, and a contact layer. The stack is bonded to a lithium niobate film. The III-V substrate is removed by etching down to the first etch stop layer. Deposition windows are opened by etching from the first etch stop layer down to the contact layer. Metal contact electrodes are deposited in the deposition windows.

36 MATERIALS SCIENCE↗