Synthesis and characteristics of porous ceramic tubes: a comparison of centrifugal casting and cold isostatic pressing methods
Short porous ceramic tubes in small quantities are needed for membrane-related research and development efforts and can be synthesized by centrifugal casting (CC) or cold isostatic pressing (CIP) methods. Here, this work evaluates the characteristics of porous ceramic tubes prepared by both methods and provides a strategy for selecting the proper method for ceramic tube fabrication, depending on its application. Samarium-doped ceria (SDC) with an average crystallite size of 10 nm was synthesized by a citrate method and used to make porous SDC tubes by the CC and CIP methods under different conditions. Porous SDC tubes were prepared from an aqueous suspension of the SDC powder with polyvinyl alcohol (PVA) using a cylindrical metallic mold, centrifugated at 4000–6000 rpm, followed by sintering in 1200–1500 °C. SDC tubes were also made by the CIP method from the SDC powder placed inside a cylindrical rubber bag followed by isostatic compression at 1379 bar. The pore structure of the SDC tubes was characterized by helium permeation and liquid nitrogen Archimedes method. Due to high compression pressure giving a low porosity green tube, the CIP method with lower sintering temperature produces SDC tubes with much lower porosity and average pore size and similar tortuosity compared to the CC methods. The CIP method should be used to prepare low porosity or dense ceramic tubes, and the CC method should be used for preparing high-porosity ceramic tubes or tubes with pore gradient tube wall.
36 MATERIALS SCIENCE↗
Dual-phase ionic-conducting membranes: Pressure dependence of gas permeation flux
Not Available
Lin, Jerry Y. S. (ORCID:0000000159058336)↗
Water-gas shift reaction in ceramic-carbonate dual-phase membrane reactor at high temperatures and pressures
Water-gas-shift (WGS) reaction is a critical step in integrated gasification combined cycles (IGCC) power plants with CO 2 capture. Membrane reactors made with a CO 2 -permselective ceramic-carbonate dual-phase (CCDP) membrane offers the potential to enhance hydrogen yield with simultaneous CO 2 capture for WGS reaction. The present work studies operation of WGS reaction in a tubular membrane reactor made of samarium-doped ceria infiltrated with lithium/sodium molten carbonate mixture. The WGS reaction was performed in the membrane reactor with and without a high-temperature WGS catalyst at 800–850 °C, feed pressure of 7 bar, the space velocity of 150–3000 h –1 , and a feed gas mixture of 45.7/13.1/41.3 mol% CO/CO 2 /N 2 with steam to carbon ratio of 4. The results show that the catalyst-free membrane reactor can convert 92% of carbon monoxide into CO 2 and H 2 and recover 29% CO 2 at 850 °C and a space velocity of 150 h –1 . However, in the catalyst-free membrane reactor, a significant amount of unwanted carbon deposition is observed. The side reactions can be minimized by reducing the operating pressure and increasing the operating temperature and space velocity, and completely avoided using a high-temperature catalyst at space velocity>500 h –1 . The membrane reactor with a WGS catalyst achieves CO conversion of about 85%, above the equilibrium conversion, and 40% CO 2 recovery without carbon deposition at high temperature and pressure. Finally, the membrane remains in the same structure and gas-tightness after the WGS reaction tests.
20 FOSSIL-FUELED POWER PLANTS↗
High-pressure CO 2 permeation properties and stability of ceramic-carbonate dual-phase membranes
CO 2 permeation properties and stability of ceramic-carbonate dual-phase membranes at high pressures/temperatures are critical to their CO 2 separation and membrane reactor applications, but such data are not available in the literature. Here, this work aims to study the effect of high transmembrane pressure on CO 2 permeation flux and the stability of molten carbonate in the dual-phase samarium-doped ceria (SDC) and molten-carbonate (MC) membranes. Dead-end porous SDC tubular supports were made by a cold isostatic press (CIP)/sintering method with a low porosity (below 7%), and gas-tight SDC-MC membranes were prepared by direct infiltration of molten lithium and sodium carbonate mixture into SDC pores, with a MC volume fraction less than 7%. CO 2 permeation/separation tests were performed on the SDC-MC membranes using feed gas of equal molar CO 2 /N 2 mixture at feed pressures up to 15 atm and sweep gas of helium at 1 atm. CO 2 permeation flux for the SDC-MC membranes depends logarithmically on feed/permeate CO 2 pressure ratio in 660–810°C. The temperature dependence of CO 2 permeation shows activation energy of 30 kJ/mol. Due to the small MC volume fraction and hence low effective carbonate conductivity, CO 2 permeation of the SDC-MC membranes is dominated by the carbonate ionic conduction in the MC phase. The SDC-MC membranes remain in the same structure, morphology, and gas-tightness after CO 2 separation tests at high feed pressures and temperatures, showing high stability of SDC-MC membranes for high-temperature, high-pressure separation and chemical reaction applications.
36 MATERIALS SCIENCE↗