In the Acknowledgements section of this article the grant number relating to NSF was incorrectly given as DMR 2045826 and should have been DMR-2045826. The original article has been corrected.
Abstract Skyrmions and antiskyrmions are nanoscale swirling textures of magnetic moments formed by chiral interactions between atomic spins in magnetic noncentrosymmetric materials and multilayer films with broken inversion symmetry. These quasiparticles are of interest for use as information carriers in next-generation, low-energy spintronic applications. To develop skyrmion-based memory and logic, we must understand skyrmion-defect interactions with two main goals—determining how skyrmions navigate intrinsic material defects and determining how to engineer disorder for optimal device operation. Here, we introduce a tunable means of creating a skyrmion-antiskyrmion system by engineering the disorder landscape in FeGe using ion irradiation. Specifically, we irradiate epitaxial B20-phase FeGe films with 2.8 MeV Au 4+ ions at varying fluences, inducing amorphous regions within the crystalline matrix. Using low-temperature electrical transport and magnetization measurements, we observe a strong topological Hall effect with a double-peak feature that serves as a signature of skyrmions and antiskyrmions. These results are a step towards the development of information storage devices that use skyrmions and antiskyrmions as storage bits, and our system may serve as a testbed for theoretically predicted phenomena in skyrmion-antiskyrmion crystals.
Abstract The drive toward non‐von Neumann device architectures has led to an intense focus on insulator‐to‐metal (IMT) and the converse metal‐to‐insulator (MIT) transitions. Studies of electric field‐driven IMT in the prototypical VO 2 thin‐film channel devices are largely focused on the electrical and elastic responses of the films, but the response of the corresponding TiO 2 substrate is often overlooked, since it is nominally expected to be electrically passive and elastically rigid. Here, in‐operando spatiotemporal imaging of the coupled elastodynamics using X‐ray diffraction microscopy of a VO 2 film channel device on TiO 2 substrate reveals two new surprises. First, the film channel bulges during the IMT, the opposite of the expected shrinking in the film undergoing IMT. Second, a microns thick proximal layer in the substrate also coherently bulges accompanying the IMT in the film, which is completely unexpected. Phase‐field simulations of coupled IMT, oxygen vacancy electronic dynamics, and electronic carrier diffusion incorporating thermal and strain effects suggest that the observed elastodynamics can be explained by the known naturally occurring oxygen vacancies that rapidly ionize (and deionize) in concert with the IMT (MIT). Fast electrical‐triggering of the IMT via ionizing defects and an active “IMT‐like” substrate layer are critical aspects to consider in device applications.
The layered square-planar nickelates, Nd n+1 Ni n O 2n+2 , are an appealing system to tune the electronic properties of square-planar nickelates via dimensionality; indeed, superconductivity was recently observed in Nd 6 Ni 5 O 12 thin films. Here, we investigate the role of epitaxial strain in the competing requirements for the synthesis of the n = 3 Ruddlesden-Popper compound, Nd 4 Ni 3 O 10 , and subsequent reduction to the square-planar phase, Nd 4 Ni 3 O 8 . We synthesize our highest quality Nd 4 Ni 3 O 10 films under compressive strain on LaAlO 3 (001), while Nd 4 Ni 3 O 10 on NdGaO 3 (110) exhibits tensile strain-induced rock salt faults but retains bulk-like transport properties. A high density of extended defects forms in Nd 4 Ni 3 O 10 on SrTiO 3 (001). Films reduced on LaAlO 3 become insulating and form compressive strain-induced c-axis canting defects, while Nd 4 Ni 3 O 8 films on NdGaO 3 are metallic. This work provides a pathway to the synthesis of Nd n+1 Ni n O 2n+2 thin films and sets limits on the ability to strain engineer these compounds via epitaxy.
Long viewed as passive elements, antiferromagnetic materials have emerged as promising candidates for spintronic devices due to their insensitivity to external fields and potential for high-speed switching. Recent work exploiting spin and orbital effects has identified ways to electrically control and probe the spins in metallic antiferromagnets, especially in non-collinear or non-centrosymmetric spin structures. The rare-earth nickelate NdNiO 3 is known to be a non-collinear antiferromagnet in which the onset of antiferromagnetic ordering is concomitant with a transition to an insulating state. In this work, we find that for low electron doping, the magnetic order on the nickel site is preserved, whereas electronically, a new metallic phase is induced. We show that this metallic phase has a Fermi surface that is mostly gapped by an electronic reconstruction driven by bond disproportionation. Furthermore, we demonstrate the ability to write to and read from the spin structure via a large zero-field planar Hall effect. Our results expand the already rich phase diagram of rare-earth nickelates and may enable spintronics applications in this family of correlated oxides.
Utilizing the powerful combination of molecular-beam epitaxy (MBE) and angle-resolved photoemission spectroscopy (ARPES), we produce and study the effect of different terminating layers on the electronic structure of the metallic delafossite PdCoO 2 . Attempts to introduce unpaired electrons and synthesize new antiferromagnetic metals akin to the isostructural compound PdCrO 2 have been made by replacing cobalt with iron in PdCoO 2 films grown by MBE. Using ARPES, we observe similar bulk bands in these PdCoO 2 films with Pd-, CoO 2 -, and FeO 2 -termination. Nevertheless, Pd- and CoO 2 -terminated films show a reduced intensity of surface states. Additionally, we are able to epitaxially stabilize PdFe x Co 1– x O 2 films that show an anomaly in the derivative of the electrical resistance with respect to temperature at 20 K, but do not display pronounced magnetic order.
The rare-earth nickelates possess a diverse set of collective phenomena including metal-to-insulator transitions, magnetic phase transitions, and, upon chemical reduction, superconductivity. In this work, we demonstrate epitaxial stabilization of layered nickelates in the Ruddlesden-Popper form, Nd n +1 NinO 3 n +1 , using molecular beam epitaxy. By optimizing the stoichiometry of the parent perovskite NdNiO 3 , we can reproducibly synthesize the n = 1–5 member compounds. X-ray absorption spectroscopy at the O K and Ni L edges indicate systematic changes in both the nickel-oxygen hybridization level and nominal nickel filling from 3$d^8$ to 3$d^7$ as we move across the series from n = 1 to n = ∞. The n = 3 – 5 compounds exhibit weakly hysteretic metal-to-insulator transitions with transition temperatures that depress with increasing order toward NdNiO 3 ( n = ∞).
Abstract The prospect of 2‐dimensional electron gases (2DEGs) possessing high mobility at room temperature in wide‐bandgap perovskite stannates is enticing for oxide electronics, particularly to realize transparent and high‐electron mobility transistors. Nonetheless only a small number of studies to date report 2DEGs in BaSnO 3 ‐based heterostructures. Here, 2DEG formation at the LaScO 3 /BaSnO 3 (LSO/BSO) interface with a room‐temperature mobility of 60 cm 2 V −1 s −1 at a carrier concentration of 1.7 × 10 13 cm –2 is reported. This is an order of magnitude higher mobility at room temperature than achieved in SrTiO 3 ‐based 2DEGs. This is achieved by combining a thick BSO buffer layer with an ex situ high‐temperature treatment, which not only reduces the dislocation density but also produces a SnO 2 ‐terminated atomically flat surface, followed by the growth of an overlying BSO/LSO interface. Using weak beam dark‐field transmission electron microscopy imaging and in‐line electron holography technique, a reduction of the threading dislocation density is revealed, and direct evidence for the spatial confinement of a 2DEG at the BSO/LSO interface is provided. This work opens a new pathway to explore the exciting physics of stannate‐based 2DEGs at application‐relevant temperatures for oxide nanoelectronics.
Since the discovery of high-temperature superconductivity in the copper oxide materials, there have been sustained efforts to both understand the origins of this phase and discover new cuprate-like superconducting materials. One prime materials platform has been the rare-earth nickelates and indeed superconductivity was recently discovered in the doped compound Nd 0.8 Sr 0.2 NiO 2 . Undoped NdNiO 2 belongs to a series of layered square-planar nickelates with chemical formula Nd n+1 Ni n O 2n+2 and is known as the 'infinite-layer' (n=∞) nickelate. Furthermore, we report the synthesis of the quintuple-layer (n=5) member of this series, Nd 6 Ni 5 O 12 , in which optimal cuprate-like electron filling (d 8.8 ) is achieved without chemical doping. We observe a superconducting transition beginning at ~13 K. Electronic structure calculations, in tandem with magnetoresistive and spectroscopic measurements, suggest that Nd 6 Ni 5 O 12 interpolates between cuprate-like and infinite-layer nickelate-like behavior. In engineering a distinct superconducting nickelate, we identify the square-planar nickelates as a new family of superconductors which can be tuned via both doping and dimensionality.
Metastable polymorphs--materials with the same stoichiometry as the ground state but a different crystal structure--enable many critical technologies. This work describes the development of a stabilization approach for metastable polymorphs that are difficult to achieve through other stabilization techniques (such as epitaxy or quenching) called stromataxy. Stromataxy is a method based on controlling the precursor structure during the initial stages of material growth to dictate phase formation. To illustrate this approach, we controlled the atomic layering of the precursors of ScFeO3 and stabilized the metastable P63cm phase, under conditions that previously led to the ground-state Ia3¯ bixbyite phase. Ab initio mechanistic calculations highlight the importance of the variable oxidation state of Fe and the layer stability during layer-by-layer growth. The broad applicability of a stromataxy approach was demonstrated by stabilizing this metastable phase on substrates that have previously been shown to stabilize other polymorphs under continuous growth. Stromataxy is shown as a viable option for accessing polymorphs that are close in energy, difficult to differentiate by strain, or that lack a well epitaxially matched substrate.
Ultrawide-band-gap (UWBG) semiconductors are promising for fast, compact, and energy-efficient power-electronics devices. Their wider band gaps result in higher breakdown electric fields that enable high-power switching with a lower energy loss. Yet, the leading UWBG semiconductors suffer from intrinsic materials' limitations with regard to their doping asymmetry that impedes their adoption in CMOS technology. Improvements in the ambipolar doping of UWBG materials will enable a wider range of applications in power electronics as well as deep-UV optoelectronics. These advances can be accomplished through theoretical insights on the limitations of current UWBG materials coupled with the computational prediction and experimental demonstration of alternative UWBG semiconductor materials with improved doping and transport properties. As an example, we discuss the case of rutile GeO2 (r-GeO 2 ), a water-insoluble GeO 2 polytype, which is theoretically predicted to combine an ultra-wide gap with ambipolar dopability, high carrier mobilities, and a higher thermal conductivity than β-Ga 2 O 3 . The subsequent realization of single-crystalline r-GeO 2 thin films by molecular beam epitaxy provides the opportunity to realize r-GeO 2 for electronic applications. Future efforts toward the predictive discovery and design of new UWBG semiconductors include advances in first-principles theory and high-performance computing software, as well as the demonstration of controlled doping in high-quality thin films with lower dislocation densities and optimized film properties.
Remote epitaxy has drawn attention as it offers epitaxy of functional materials that can be released from the substrates with atomic precision, thus enabling production and heterointegration of flexible, transferrable, and stackable freestanding single-crystalline membranes. In addition, the remote interaction of atoms and adatoms through two-dimensional (2D) materials in remote epitaxy allows investigating and utilizing electrical/chemical/physical coupling of bulk (3D) materials via 2D materials (3D-2D-3D coupling). Here, we unveil the respective roles and impacts of the substrate material, graphene, substrate-graphene interface, and epitaxial material for electrostatic coupling of these materials, which governs cohesive ordering and can lead to single-crystal epitaxy in the overlying film. Further, we show that simply coating a graphene layer on wafers does not guarantee successful implementation of remote epitaxy, since atomically precise control of the graphene-coated interface is required, and provide key considerations for maximizing the remote electrostatic interaction between the substrate and adatoms. This was enabled by exploring various material systems and processing conditions, and we demonstrate that the rules of remote epitaxy vary significantly depending on the ionicity of material systems as well as the graphene-substrate interface and the epitaxy environment. The general rule of thumb discovered here enables expanding 3D material libraries that can be stacked in freestanding form.
Abstract Straining the vanadium dimers along the rutile c ‐axis can be used to tune the metal‐to‐insulator transition (MIT) of VO 2 but has thus far been limited to TiO 2 substrates. In this work VO 2 /MgF 2 epitaxial films are grown via molecular beam epitaxy (MBE) to strain engineer the transition temperature ( T MIT ). First, growth parameters are optimized by varying the synthesis temperature of the MgF 2 (001) substrate ( T S ) using a combination of X‐ray diffraction techniques, temperature dependent transport, and soft X‐ray photoelectron spectroscopy. It is determined that T S values greater than 350 °C induce Mg and F interdiffusion and ultimately the relaxation of the VO 2 layer. Using the optimized growth temperature, VO 2 /MgF 2 (101) and (110) films are then synthesized. The three film orientations display MITs with transition temperatures in the range of 15–60 °C through precise strain engineering.
The metal to insulator transition of NbO 2 has been predicted to be a result of a structural phase transition (SPT) governed by Peierls physics. However, direct observation of the SPT using experimental techniques is still restricted by the extremely high transition temperature (810 °C) and the proclivity for NbO 2 to oxidize into Nb 2 O 5 above 400 °C when exposed to air. In this work, we address these issues and employ temperature-dependent X-ray spectroscopy to describe the SPT of NbO 2 from the bulk to surface. Temperature-dependent extended X-ray absorption fine structure spectroscopy (T-EXAFS) reveals a gradual weakening of the bulk Nb dimers over a large temperature range, which is indicative of a second-order Peierls mechanism. From these measurements, we determine the critical dimer distance to be 2.77 Å. Our T-EXAFS observations are supported by density functional theory of the phonon dispersion and the electronic density of states of NbO 2 , which conclude that the dimerization is responsible for the insulating phase. The dimerization does not extend to the topmost layers, where an oxygen rich surface reconstruction is preferred irrespective of temperature even in extremely reducing environments; changes in the low-energy electron diffraction patterns are attributed to oxygen concentration and are independent of the underlying bulk phase transitions of NbO 2 .
The synthesis of fully epitaxial ferroelectric Hf 0.5 Zr 0.5 O 2 (HZO) thin films through the use of a conducting pyrochlore oxide electrode that acts as a structural and chemical template is reported. Such pyrochlores, exemplified by Pb 2 Ir 2 O 7 (PIO) and Bi 2 Ru 2 O 7 (BRO), exhibit metallic conductivity with room-temperature resistivity of <1 mΩ cm and are closely lattice matched to yttria-stabilized zirconia substrates as well as the HZO layers grown on top of them. Evidence for epitaxy and domain formation is established with X-ray diffraction and scanning transmission electron microscopy, which show that the c-axis of the HZO film is normal to the substrate surface. The emergence of the non-polar-monoclinic phase from the polar-orthorhombic phase is observed when the HZO film thickness is ≥≈30 nm. Furthermore, thermodynamic analyses reveal the role of epitaxial strain and surface energy in stabilizing the polar phase as well as its coexistence with the non-polar-monoclinic phase as a function of film thickness.
Epitaxial films of vanadium dioxide (VO 2 ) on rutile TiO 2 substrates provide a means of strain-engineering the transition pathways and stabilizing of the intermediate phases between monoclinic (insulating) M1 and rutile (metal) R end phases. In this work, we investigate structural behavior of epitaxial VO 2 thin films deposited on isostructural MgF 2 (001) and (110) substrates via temperature-dependent Raman microscopy analysis. The choice of MgF 2 substrate clearly reveals how elongation of V–V dimers accompanied by the shortening of V–O bonds triggers the intermediate M2 phase in the temperature range between 70–80 °C upon the heating–cooling cycles. Consistent with earlier claims of strain-induced electron correlation enhancement destabilizing the M2 phase our temperature-dependent Raman study supports a small temperature window for this phase. The similarity of the hysteretic behavior of structural and electronic transitions suggests that the structural transitions play key roles in the switching properties of epitaxial VO 2 thin films.