DOE OSTI2024

Self-aligned fabrication of vertical, fin-based structures

Modern power devices rely on complex, three-dimensional, vertical designs to increase their power density, ease their thermal management, and improve their reliability. However, fabrication techniques have historically relied on 2D processes for patterning lateral features. This work presents a new technology that uses multiple steps of angled depositions to fabricate self-aligned vertical, fin-based devices that avoid fundamental lithography resolution and alignment limitations. The fabrication flows of two devices, the self-aligned vertical finFET and the high-κ dielectric fin diode, are presented to demonstrate how angled depositions can readily achieve transistors with submicrometer, vertical gates in a source-first process and also create high-aspect ratio GaN fins with a record 70:1 aspect ratio.

Perozek, Joshua (ORCID:0000000251519131)↗
DOE OSTI2024

High temperature stability of regrown and alloyed Ohmic contacts to AlGaN/GaN heterostructure up to 500 °C

This Letter reports the stability of regrown and alloyed Ohmic contacts to AlGaN/GaN-on-Si high electron mobility transistors (HEMTs) for high temperature applications up to 500 °C. Transfer length method (TLM) measurements from 25 to 500 °C in air show that the regrown contacts appear to be stable up to 500 °C during short term (approximately 1 h) testing, while alloyed contacts appear to decrease in contact resistance from 300 to 500 °C though increases in the error bounds due to increase sheet resistance make it difficult to conclude definitely. Additionally, longer term testing shows both technologies remain stable at least up to 48 h at 500 °C, after which the large increase in sheet resistance makes the measurement uncertainty too large to conclude definitively. Advanced microscopy images indicate both the regrown and alloyed contact regions remain structurally intact after prolonged high temperature exposure with no visible degradation in crystallinity or metal composition.

Physics↗
DOE OSTI2024

Device and material investigations of GaN enhancement-mode transistors for Venus and harsh environments

This Letter reports the device and material investigations of enhancement-mode p-GaN-gate AlGaN/GaN high electron mobility transistors (HEMTs) for Venus exploration and other harsh environment applications. The GaN transistor in this work was subjected to prolonged exposure (11 days) in a simulated Venus environment (460 °C, 94 bar, complete chemical environment including CO2/N2/SO2). The mechanisms affecting the transistor performance and structural integrity in harsh environment were analyzed using a variety of experimental, simulation, and modeling techniques, including in situ electrical measurement (e.g., burn-in) and advanced microscopy (e.g., structural deformation). Through transistor, Transmission Line Method (TLM), and Hall-effect measurements vs temperature, it is revealed that the mobility decrease is the primary cause of reduction of on-state performance of this GaN transistor at high temperature. Material analysis of the device under test (DUT) confirmed the absence of foreign elements from the Venus atmosphere. No inter-diffusion of the elements (including the gate metal) was observed. The insights of this work are broadly applicable to the future design, fabrication, and deployment of robust III-N devices for harsh environment operation.

Physics↗
DOE OSTI2023

Investigation of vertical GaN-on-GaN p – n diode with regrown p -GaN for operation in Venus and other extreme environments

This Letter reports the performance of vertical GaN-on-GaN p–n diodes with etch-then-regrown p-GaN after exposure to a simulated Venus environment (460 °C, ∼94 bar, containing CO2/N2/SO2 etc., atmosphere) for over 10 days, and compared them to the performance of GaN p–n diodes without the etch-then-regrow process. After the above-mentioned Venus test, temperature-dependent I–V and microscopy investigation were conducted to study the robustness of etch-then-regrow p-GaN and vertical GaN p–n diodes under harsh environments and operation up to 500 °C. p-electrode degradation is found to be the main issue of the device's performance. This is the highest temperature at which such characterization has been conducted for vertical GaN p–n diodes, therefore establishing a critical reference for the development of p-GaN regrown and vertical GaN-based electronics for extreme environments.

Physics↗