A high-performance and durable direct NH 3 tubular protonic ceramic fuel cell integrated with an internal catalyst layer

Nickel-based cermet anode-supported protonic ceramic fuel cells (PCFCs) show great potential for direct utilization of ammonia. However, the insufficient activity of anode and the deterioration of anode activity/durability caused by the undesired interaction between nickel and ammonia greatly limit the application. Here, we report tubular PCFCs embedded with a catalytic iron layer. Such cells show peak power densities of 1.507 W cm -2 and 1.078 W cm -2 at 700 °C when using H 2 and NH 3 as fuel, respectively, which are the highest tubular PCFC performance so far ever reported. In addition, the stability of cells with the catalyst layer has been dramatically enhanced when compared with that of cells without the catalyst layer. As a result, the enhancement of activity and durability is attributed to the catalytic activity of iron for ammonia decomposition, through which the direct contact between nickel and ammonia has been minimized and the anode structure has therefore been protected.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

An efficient and durable anode for ammonia protonic ceramic fuel cells

Ammonia protonic ceramic fuel cells (PCFCs) have the potential to be a highly efficient power source with high energy density. However, the inadequate catalytic activity of the existing anodes for utilization of ammonia greatly limits the performance of PCFCs. In this study, we report an Fe-modified state-of-the-art Ni cermet anode with greatly enhanced activity and durability toward utilization of ammonia. Cells with an Fe-decorated Ni-BaZr 0.1 Ce 0.7 Y 0.1 Yb 0.1 O 3 (Ni–BZCYYb) anode demonstrate an excellent performance, achieving peak power densities of 0.360, 0.723, 1.257, and 1.609 W cm –2 at 550, 600, 650, and 700 °C, respectively, which reveal the highest performance of solid oxide fuel cells fueled on ammonia. In addition, the cells show an excellent durability when operated at a constant current density of 0.5 A cm –2 (or a power density of ~0.435 W cm –2 ) at 650 °C. The superior activity and durability of the Fe-modified Ni/BZCYYb anode are attributed to the alternation of NH 3 adsorption strength and N 2 desorption barrier heights, as confirmed by first-principles based mechanistic and microkinetic modeling. Our research provides a valuable guidance for the development of efficient electro-catalysts for ammonia PCFCs.

32 ENERGY CONSERVATION, CONSUMPTION, AND UTILIZATI↗