DOE OSTI2023

Water vapor transmission rate measurement for moisture barriers using infrared imaging

Here, in this work, we demonstrate a spatially resolved imaging methodology for water vapor transmission rate (WVTR) testing that relies on quantified infrared characterization at water absorption bands. This technique is validated using a moisture barrier on a polymer substrate via calibration of the infrared image intensity with moisture content in the polymer substrate from images taken at different times. The method is compared to existing state of the art techniques such as membrane permeation measurement with coulometric phosphorous pentoxide sensor and optical calcium film testing. This fast, non-destructive and in-situ method enables defect visualization and shows the WVTR with a sensitivity limit of 5·10 –5 g/m 2 /day.

47 OTHER INSTRUMENTATION↗

DOE OSTI2021

Low-temperature sprayed SnO x nanocomposite films with enhanced hole blocking for efficient large area perovskite solar cells

Scalable fabrication of charge transport layers with high uniformity and compactness is essential for the commercialization of perovskite solar cells (PSCs). Cost-effective deposition of high-quality electron transport layers (ETLs) is a particularly important step to achieve low-cost, efficient and large-area PSCs. Here, an open-air (relative humidity of 40–50%) and low-temperature (≤100 °C) ultrasonic spray coating of tin oxide (SnO 2 ) nanocomposite films incorporating nanocrystalline SnO 2 nanoparticles in an amorphous SnO x matrix is demonstrated to fabricate large-area ETLs for planar PSCs. The optimized SnO 2 /SnO x nanocomposite exhibits significantly enhanced hole-blocking and high-power conversion efficiencies of 18% and 16% for planar PSCs with an active area of 0.2 cm 2 and 1 cm 2 , respectively. More importantly, the devices show little current–voltage hysteresis as well as good shelf-life stability by maintaining ~90% of the initial performance without encapsulation after 2500 hours storage under inert conditions. Additionally, high voltages of >6.0 V have been obtained for solar modules of 2.1 cm 2 aperture area comprising six sub-cells in series, suggesting that the low-temperature, open-air and fast spray coating is suitable and transferable to deposit large-area charge transport layers for scalable PSCs or other optoelectronic devices.

32 ENERGY CONSERVATION, CONSUMPTION, AND UTILIZATI↗