Intrinsically Conductive {pi}‑d Conjugated Layers with Co–N4 Active Sites for Efficient Nitrate Electrocatalysis and Zinc-Nitrate Batteries
Electrochemical synthesis of ammonia from nitrate has been extensively investigated as a potential alternative to the energy-intensive Haber-Bosch process. This approach not only operates under ambient conditions but also simultaneously removes nitrate contaminants while producing ammonia as a value-added product. However, the ongoing quest lies in designing an efficient electrocatalyst that achieves a high ammonia yield rate, high selectivity, and long-term stability. Herein, we report the outstanding performance of a Co–N4 coordinated π-d layered Co3(HITP)2 (HITP = 2,3,6,7,10,11-hexaiminotriphenylene) in nitrate electrocatalysis. The unique combination of abundant Co–N4 active sites and superior electrical conductivity enables significant electrocatalytic activity, delivering a maximum ammonia yield rate of 56.8 mg cm–2 h–1 at −0.8 V vs RHE and a Faradaic efficiency of ∼91% at −0.4 V vs RHE. Mechanistic analysis reveals that alkaline conditions accelerate water dissociation to generate adsorbed hydrogen intermediates (H*), which are utilized by Co–N4 sites to drive the stepwise hydrogenation of nitrate to ammonia while suppressing competing hydrogen evolution reaction (HER) pathways. Furthermore, integration of this catalyst into a zinc-nitrate battery resulted in a maximum power density of 5.3 mW cm–2 and an open-circuit potential of ∼1.45 V. These results highlight the potential of π-d conjugated Co–N4 materials as an efficient catalyst for both environmental remediation and energy conversion.