DOE OSTI2023

Effects of Encapsulant Properties on the Thermo-Mechanical Reliability of Double-Side Cooled Power Modules for Traction Inverters

Double-side cooled power modules are being developed for next-generation traction inverters due to their better heat extraction, lower profile, and lower parasitic inductances. However, due to their rigid structure, they cause reliability concerns arising from high thermo-mechanical stresses at the interconnection joints in the module. In this work, a materials-based approach using rigid encapsulants is presented for reducing thermo-mechanical fatigue. Finite-element thermo- mechanical simulations were performed to examine the effects of the elastic modulus and coefficient of thermal expansion of epoxy- based encapsulants on the bond deformation inside a double-side cooled power module. It was found that a rigid encapsulant with a high modulus of 6.0 GPa or above and a coefficient of thermal expansion around 20 ppm/oC would improve the thermo- mechanical reliability of double-side cooled power modules by decreasing the permanent bond deformation inside the modules by 50-60%.

ADVANCED PROPULSION SYSTEMS↗

DOE OSTI2023

PCB-on-DBC GaN Power Module Design with High-Density Integration and Double-Sided Cooling

Lateral gallium nitride (GaN) high-electron-mobility transistors (HEMTs) present better electrical characteristics compared to silicon or silicon carbide devices such as high switching speed and low gate charge, but also present additional challenges on the module design. Here, this paper discusses a high-density GaN power module with double-sided cooling, low inductance, on-package decoupling capacitors, and integrated gate drivers. The GaN dies as well as the gate drive are sandwiched between the printed circuit board (PCB) and direct bonded copper (DBC) substrate to achieve compact loop and double-sided cooling effect. Design considerations and thermal performance are analyzed. A module assembly procedure is presented utilizing the layer-by-layer attachment process. Finally, a 2.7 cm x 1.8 cm half-bridge GaN power module is fabricated and tested, achieving a low power-loop inductance of 1.03 nH, and the overshoot voltage of the switching waveform is less than 5% under a 400-V/25-A double-pulse test. The thermal resistance is 0.32 K/W, verified by simulation and experimental results. The design and assembly process can be generalized and applied to high power applications to achieve high power density and high performance.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2022

Artificial Intelligence for Power Electronics in Electric Vehicles: Challenges and Opportunities

We report progress in the field of power electronics within electric vehicles has generally been driven by conventional engineering design principles and experiential learning. Power electronics is inherently a multidomain field where semiconductor physics and electrical, thermal, and mechanical design knowledge converge to achieve a practical realization of desired targets in the form of conversion efficiency, power density, and reliability. Due to the promising nature of artificial intelligence in delivering rapid results, engineers are starting to explore the ways in which it can contribute to making power electronics more compact and reliable. Here, we conduct a brief review of the foray of artificial intelligence in three distinct subtechnologies within a power electronics system in the context of electric vehicles: semiconductor devices, power electronics module design and prognostics, and thermal management design. The intent is not to report an exhaustive literature review, but to identify the state of the art and opportunities for artificial intelligence to play a meaningful role in power electronics design from a mechanical and thermal standpoint, as well as to discuss a few promising future research directions.

33 ADVANCED PROPULSION SYSTEMS↗

DOE OSTI2022

Reliability and Lifetime Prediction Model of Sintered Silver Under High-Temperature Cycling

Although excellent reliability has been reported for sintered silver as a die-attach material under both thermal and power cycling loads in power electronics applications, the promise of this material as a large-area attachment at temperatures beyond 200 degrees C needs to be investigated. This paper presents insights into the thermomechanical behavior and reliability of sintered silver under extreme thermal cycling conditions. In this study, we bonded sintered silver samples and subjected it to a thermal cycling profile of -40 °C to 200 °C with high ramp rates. We periodically monitored samples under thermal cycling to detect the presence of any failure mechanisms using a scanning acoustic microscope. We also included 95Pb5Sn solder in the study to obtain reference data. Results show the occurrence of cracks in sintered silver followed by a rapid rate of crack growth that exceeded the failure criterion in just 50 cycles. The predominant failure mechanism we observed was adhesive failure. As a large-area attachment, solder exhibited a higher reliability than sintered silver but failed within 100 cycles. Finally, we performed thermomechanical modeling to compute strain energy density values and correlated these with the experimentally observed crack growth rates to formulate a lifetime prediction model for sintered silver.

30 DIRECT ENERGY CONVERSION↗

DOE OSTI2021

Reliability Analysis of Large-Area, Low Pressure-Assisted Silver Sintering for Medium-Voltage Power Modules

Multi-layer insulating ceramic substrates can enable medium-voltage (MV) power modules with reduced peak electric field. This benefit is particularly important for MV silicon carbide (SiC) MOSFETs due to their higher operating voltages. Large-area, low-pressure assisted silver sintering is a potential solution for bonding substrates to create a multi-layer structure. The voiding content and defect density of the bond used to create the multi-layer substrate stack-up is critical to the reliability of the power module and the thermal performance, as this bond is in the primary path for heat dissipation in the power module structure. Here, samples of two-layer direct bonded aluminum (DBA) stacks have been fabricated and subjected to thermal cycling to analyze their reliability. Passive thermal cycling from -40 degrees C to 200 degrees C was performed. Cross-sections were cut at pre-determined intervals and imaged with Scanning Electron Microscopy (SEM). After 1000 thermal cycles, adhesive failures are observed between the sintered silver and the DBA surface. Cross-sections were cut and imaged via optical microscope and SEM. Thermal analyzer measurements are recorded on a 10-kV SiC power module utilizing the sintered DBA substrate stacks.

30 DIRECT ENERGY CONVERSION↗

DOE OSTI2020

Electrification Annual Progress Report (FY2019)

During fiscal year 2019 (FY 2019), the U.S. Department of Energy (DOE) Vehicle Technologies Office (VTO) funded early stage research & development (R&D) projects that address Batteries and Electrification of the U.S. transportation sector. The VTO Electrification Sub-Program is composed of Electric Drive Technologies, and Grid Integration activities. The Electric Drive Technologies group conducts R&D projects that advance electric motors and power electronics technologies. The Grid and Charging Infrastructure group conducts R&D projects that advance grid modernization and electric vehicle charging technologies. This document presents a brief overview of the Electrification Sub-Program and progress reports for its R&D projects. Each of the progress reports provide a project overview and highlights of the technical results that were accomplished in FY 2019.

25 ENERGY STORAGE↗