Effect of Nanoscale Ce 0.8 Gd 0.2 O 2–δ Infiltrant and Steam Content on Ni–(Y 2 O 3 ) 0.08 (ZrO 2 ) 0.92 Fuel Electrode Degradation during High-Temperature Electrolysis
Studies of Ni–yttria-stabilized zirconia (YSZ) fuel electrode degradation mechanisms in solid oxide electrolysis cells (SOECs) are complicated by the different possible Ni–YSZ microstructures and compositions, and the variations in the H 2 /H 2 O ratio encountered in an electrolysis stack. Here, in this study, we describe a life testing scheme aimed at providing survey results on degradation as a function of the H 2 O–H 2 composition, with life tests carried out at five different steam contents from 90% to 10%. A Ni–YSZ-supported symmetric cell geometry is employed both with and without infiltrated nanoscale gadolinia-doped ceria (GDC). Impedance spectroscopy is utilized to observe changes in electrochemical characteristics during the life test, and a transmission-line-based equivalent circuit is used to model the data. Post-test electrode microstructures were observed. The results suggest that the GDC infiltrant reduces the electrode polarization resistance and provides more stable electrode polarization over a range of conditions.