Calendar life of lithium metal batteries: Accelerated aging and failure analysis
Lithium metal batteries (LMBs) are prime candidates for next-generation energy storage devices characterized by their remarkable energy storage capabilities. Despite the importance of understating the calendar aging impacts in LMBs, cycle life and calendar life have received inconsistent attention across various research and development stages. For acceptance into an application, especially electric vehicles, batteries are required to have sufficient calendar life to ensure performance over the life of vehicles which often experience extended periods of inactivity. In this study, an in-depth exploration into the calendar aging of LMB (Li/ Li[Ni 0.8 Mn 0.1 Co 0.1 ]O 2 in pouch cell format) is conducted. Specifically, the impact of calendar aging factors, state-of-charge (SOC), temperature, pressure, and operating conditions (open-circuit voltage, OCV and constant voltage, CV) on the surface morphology and thickness change rate in lithium metal anode is investigated. Notably, the results show that storing LMB pouch cells at an OCV, 80 % SOC, 25 °C, and 10 psi external pressure leads to a <1% reduction in capacity over 18 months. The results also suggest routes which can be utilized in the future for accelerated aging without altering the primary degradation modes. The results also show an accelerated calendar aging at high temperatures (45 °C), 100 % SOC, and CV suggesting they may serve as key accelerated aging methods for future studies. During calendar aging, pressure mitigates dendrite growth and extends calendar life. In conclusion, the insights from this study reinforce the viability of LMBs as a compelling solution for addressing increased energy storage needs in real-world applications.