Fiber-matrix interface failures

Interface fractures of aluminum-graphite composites under transverse loading are expected to occur within the graphite fibers, but very near the interface. Residual stresses in aluminum, reinforced with the new high modulus pitch-based fibers, are much lower than would be expected based on simple elasticity calculations. The excess stress may be relaxed by shearing internal to the fibers or at the interface rather than by plastic flow of the matrix. The internal shearing also occurs during repeated thermal cycling of these composites; the fibers are repeatedly intruded, then extruded, during repeated temperature excursions.

Rabenberg, Lew↗

NASA NTRS1988

Residual stresses in continuous graphite fiber Al metal matrix composites

The residual stresses in graphite fiber reinforced aluminum (Gr/Al) composites with various thermal histories are measured using X-ray diffraction (XRD) methods. The XRD stress analysis is based on the determination of lattice strains by precise measurements of the interplanar spacings in different directions of the sample. The sample is a plate consisting of two-ply P 100 Gr/Al 6061 precursor wires and Al 6061 overlayers. Prior to XRD measurement, the 6061 overlayers are electrochemically removed. In order to calibrate the relationship between stress magnitude and lattice spacing shift, samples of Al 6061 are loaded at varying stress levels in a three-point bend fixture, while the stresses are simultaneously determined by XRD and surface-attached strain gages. The stresses determined by XRD closely match those determined by the strain gages. Using these calibrations, the longitudinal residual stresses of P 100 Gr/Al 6061 composites are measured for various heat treatments, and the results are presented.

Park, Hun Sub↗