Publications and source records attributed to Parker, Cory.

4 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Interface stability of ultrasonic additively manufactured Zircaloy-4 during hydrothermal corrosion

Simulated pressurized water reactor conditions (330 °C, 15.6 MPa, ~20 ppb oxygen) without irradiation were used to investigate the hydrothermal corrosion behavior of ultrasonic additively manufactured Zircaloy-4 up to 1000 h. X-ray computed tomography allowed for visualization of defects from processing and their progression after corrosion experiments. The specimens were found to have clear variability in the mass change data, compared to typical wrought Zircaloy-4 specimens. The variation in the mass change after exposure was attributed to weld defects connected to the specimen surface which allowed ingress of oxidant into the samples. Defects visualized by computed tomography were found via metallography and characterized. In conclusion, ultrasonic additively manufactured Zircaloy-4 was found to have comparable corrosion behavior as wrought Zircaloy-4 for specimens which did not have clear surface defects along weld interfaces.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Steam oxidation and microstructural evolution of rare earth silicate environmental barrier coatings

A primary failure mode for environmental barrier coatings (EBCs) on SiC ceramic matrix composites (CMCs) is the oxidation of the intermediate Si-bond coating, where the formation of SiO 2 at the bond coating–EBC interface results in debonding and spallation. This work compares the microstructure evolution and steam oxidation kinetics of the Si-bond coating beneath yttrium/ytterbium disilicate ((Y/Yb)DS) and ytterbium disilicate/monosilicate (YbDS/YbMS) EBCs to better understand the impact of EBC composition on oxidation kinetics. After 500 1-h cycles at 1350°C, (Y/Yb)DS displayed a decreasing concentration of the monosilicate minor phase and increasing concentration of porosity as furnace cycling time increased, whereas the YbDS/YbMS EBC displayed negligible microstructural evolution. For both EBC systems, thermally grown oxide growth rates in steam were found to increase by approximately an order magnitude compared to dry air oxidation. The (Y/Yb)DS EBC displayed a reduced steam oxidation rate compared to YbDS/YbMS.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Evaluating steam oxidation kinetics of environmental barrier coatings

Environmental barrier coatings (EBCs) are a commercially proven means of protecting SiC-based materials in gas turbine environments. However, there are little specific data in the literature on the impact of coatings like Yb 2 Si 2 O 7 on preventing accelerated SiO 2 growth in the presence of H 2 O. Quantification of reduced rates are necessary for evaluating and comparing EBC effectiveness and incorporation of silica growth rates into future EBC lifetime models. In this study, baseline kinetics of silica formation on bare Si and chemically vapor deposited (CVD) SiC in the 1250–1425 °C range were obtained via 100 h isothermal exposures in dry air and steam environments utilizing a SiC reaction tube to mitigate specimen volatility. An Arrhenius plot of the resulting rates was constructed, representing baseline minimum and maximum rates for Si and SiC oxidation at ambient pressure. Various EBC systems on CVD SiC substrates including air plasma sprayed (APS) EBCs with and without a Si bond coating and with surface roughening to enhance Yb 2 Si 2 O 7 adhesion were subjected to 1-h furnace cycle testing in air with 90vol%H 2 O at 1250–1350°C for up to 500 cycles. After exposure, silica formation rates were measured and compared to the baseline rates to assess EBC effectiveness, where EBC effectiveness is gauged as the propensity to reduce underlying rates of silica formation. With a Si bond coating, a ~180 µm Yb 2 Si 2 O 7 (YbDS) top coating reduced rates over the entire 1250°-1350°C range. Without a Si bond coating, ~60 µm (YbDS) coatings deposited directly onto CVD SiC exhibited poor adhesion, and had to be deposited onto substrates with enhanced roughness at 1350°C. Finally, while exhibiting good adhesion at 1350°C, overall the single layer YbDS coating exhibited a decreasing effectiveness from 1250° to 1350°C.

36 MATERIALS SCIENCE↗