Direct Mapping of Fluorine in Cation Disordered Rocksalt Cathodes

Cation-disordered rocksalt (DRX) oxides are promising candidates as next-generation cathodes for lithium-ion batteries. Partial fluorination of the DRX oxides enhances their cyclability. However, the lattice position, concentration, and spatial distribution of fluorine within DRX lattices remain elusive. Here, in this work, we use atom location by channeling-enhanced microanalysis, energy-dispersive X-ray spectroscopy, electron energy loss spectroscopy, and integrated differential phase contrast imaging in a scanning transmission electron microscope to gain atomic-level insights into DRX with nominal composition of Li 1.2 Mn 0.7 Ti 0.1 O 1.7 F 0.3 and Li 1.15 Ni 0.45 Ti 0.3 Mo 0.1 O 1.85 F 0.15 . We reveal that fluorine substitutes oxygen in the DRX lattices. The O/F ratio in terms of O+F = 2 is in the range from 1.92:0.08 to 1.82:0.18. Spatially, fluorine is distributed in the proximity of the Li-rich regions but distinct from lithium fluoride. Additionally, we observe that incorporation of fluorine in the DRX lattice induces a larger variation in cation–anion separation. These observations provide insight into the guided design of oxyfluoride DRX cathodes for high-performance batteries.

(S)TEM↗

Enhanced Electrochemical Performance of Disordered Rocksalt Cathodes Enabled by a Graphite Conductive Additive

Cobalt-free cation-disordered rocksalt (DRX) cathodes are a promising class of materials for next-generation Li-ion batteries. Although they have high theoretical specific capacities (>300 mA h/g) and moderate operating voltages (~3.5 V vs Li/Li + ), DRX cathodes typically require a high carbon content (up to 30 wt %) to fully utilize the active material which has a detrimental impact on cell-level energy density. To assess pathways to reduce the electrode’s carbon content, the present study investigates how the carbon’s microstructure and loading (10–20 wt %) influence the performance of DRX cathodes with the nominal composition Li 1.2 Mn 0.5 Ti 0.3 O 1.9 F 0.1 . While electrodes prepared with conventional disordered carbon additives (C65 and ketjenblack) exhibit rapid capacity fade due to an unstable cathode/electrolyte interface, DRX cathodes containing 10 wt % graphite show superior cycling performance (e.g., reversible capacities ~260 mA h/g with 85% capacity retention after 50 cycles) and rate capability (~135 mA h/g at 1000 mA/g). Furthermore, a suite of characterization tools was employed to evaluate the performance differences among these composite electrodes. Overall, these results indicate that the superior performance of the graphite-based cathodes is largely attributed to the: (i) formation of a uniform graphitic coating on DRX particles which protects the surface from parasitic reactions at high states of charge and (ii) homogeneous dispersion of the active material and carbon throughout the composite cathode which provides a robust electronically conductive network that can withstand repeated charge–discharge cycles. Overall, this study provides key scientific insights on how the carbon microstructure and electrode processing influence the performance of DRX cathodes. Based on these results, exploration of alternative routes to apply graphitic coatings is recommended to further optimize the material performance.

25 ENERGY STORAGE↗

Enhancing the Electrode Gravimetric Capacity of Li 1.2 Mn 0.4 Ti 0.4 O 2 Cathode Using Interfacial Carbon Deposition and Carbon Nanotube-Mediated Electrical Percolation

Mn-based cation disordered rocksalt oxides (Mn-DRX) are emerging as promising cathode materials for next-generation Li-ion batteries due to their high specific capacities and cobalt and nickel free characteristic. However, to reach the theoretical capacity, solid-state method synthesized Mn-DRX materials require activation via post-synthetic ball milling, typically incorporating more than 20 wt.% conductive carbon that adversely reduces the electrode level gravimetric capacity. To solve this issue, we firstly deposit amorphous carbon on the surface of the Li 1.2 Mn 0.4 Ti 0.4 O 2 (LMTO) particles to increase the electrical conductivity by a five order of magnitude. Although the cathode material gravimetric first charge capacity reaches 180 mAh/g, its highly irreversible behavior leads to a 70 mAh/g first discharge capacity. Subsequently, to ensure a good electrical percolation network, the LMTO material is ball milled with multi-wall carbon nanotube (CNT) to obtain a 78.7 wt.% LMTO active material loading in the cathode electrode (LMTO-CNT). As a result, a 210 mAh/g cathode electrode gravimetric first charge and 165 mAh/g first discharge capacity are obtained, compared to the respective capacity values of 222 mAh/g and 155 mAh/g for the LMTO ball milled with 20 wt.% SuperP C65 electrode (LMTO-SP). After 50 cycles, the LMTO-CNT delivers a 121 mAh/g electrode gravimetric discharge capacity, largely outperforming the 44 mAh/g value of the LMTO-SP. In conclusion, our study demonstrates that while ball milling is necessary to achieve the theoretical capacity of LMTO, a careful selection of the additive, such as CNT, effectively reduces the required carbon quantity to achieve a higher electrode gravimetric discharge capacity.

25 ENERGY STORAGE↗

Alternate Synthesis Method for High-Performance Manganese Rich Cation Disordered Rocksalt Cathodes

Cation-disordered rocksalt (DRX) cathodes have recently emerged as a promising class of cobalt-free, high-capacity cathodes for lithium-ion batteries. To facilitate their commercialization, the development of scalable synthesis techniques providing control over composition and morphology is critical. To this end, a sol-gel synthesis route to prepare Mn-rich DRX cathodes with high capacities is presented here. Several compositions with varied Mn content and nominal F doping are successfully prepared using this technique. In-situ X-ray diffraction measurements demonstrate that DRX formation proceeds at moderate temperature (800 °C) through the sol-gel route, which enables intimate mixing among reactive intermediate phases that form at lower temperatures. All synthesized compositions possess cation short-range order, as evidenced by neutron pair distribution function and electron diffraction analysis. These DRX materials demonstrate promising electrochemical performance with reversible capacities up to 275 mAh g. Compared to the baseline oxide (Li 1.2 Mn 0.4 Ti 0.4 O 2 ), the Mn-rich compositions exhibit improved cycling stability, with some showing an increase in capacity upon cycling. Finally, this study demonstrates the feasibility of preparing high-capacity DRX cathodes through a sol-gel based synthesis route, which may be further optimized to provide better control over the product morphology compared to traditional synthesis methods.

25 ENERGY STORAGE↗

Understanding the Fluorination of Disordered Rocksalt Cathodes through Rational Exploration of Synthesis Pathways

Here, we have designed and tested several synthesis routes targeting a highly fluorinated disordered rocksalt (DRX) cathode, Li 1.2 Mn 0.4 Ti 0.4 O 1.6 F 0.4 , with each route rationalized by thermochemical analysis. Precursor combinations were screened to raise the F chemical potential and avoid the formation of LiF, which inhibits fluorination of the targeted DRX phase. MnF 2 was used as a reactive source of F, and Li 6 MnO 4 , LiMnO 2 , and Li 2 Mn 0.33 Ti 0.66 O 3 were tested as alternative Li sources. Each synthesis procedure was monitored using a multi-modal suite of characterization techniques including X-ray diffraction, nuclear magnetic resonance, thermogravimetric analysis, and differential scanning calorimetry. From the resulting data, we advance the understanding of oxyfluoride synthesis by outlining the key factors limiting F solubility. At low temperatures, MnF 2 consistently reacts with the Li source to form LiF as an intermediate phase, thereby trapping F in strong Li-F bonds. LiF can react with Li 2 TiO 3 to form a highly lithiated and fluorinated DRX (Li 3 TiO 3 F); however, MnO is not easily incorporated into this DRX phase. Although higher temperatures typically increase solubility, the volatility of LiF above its melting point (848 °C) inhibits fluorination of the DRX phase. Based on these findings, metastable synthesis techniques are suggested for future work on DRX fluorination.

36 MATERIALS SCIENCE↗