Engineering topics

Pauly, Magnus

Publications and source records attributed to Pauly, Magnus.

7 records

DOE OSTI2024

Coordination of copper within a crystalline carbon nitride and its catalytic reduction of CO 2

Inherently disordered structures of carbon nitrides have hindered an atomic level tunability and understanding of their catalytic reactivity. Starting from a crystalline carbon nitride, poly(triazine imide) or PTI/LiCl, the coordination of copper cations to its intralayer N-triazine groups was investigated using molten salt reactions. The reaction of PTI/LiCl within CuCl or eutectic KCl/CuCl 2 molten salt mixtures at 280 to 450 °C could be used to yield three partially disordered and ordered structures, wherein the Cu cations are found to coordinate within the intralayer cavities. Local structural differences and the copper content, i.e., whether full or partial occupancy of the intralayer cavity occurs, were found to be dependent on the reaction temperature and Cu-containing salt. Crystallites of Cu-coordinated PTI were also found to electrophoretically deposit from aqueous particle suspensions onto either graphite or FTO electrodes. As a result, electrocatalytic current densities for the reduction of CO 2 and H 2 O reached as high as ∼10 to 50 mA cm −2 , and remained stable for >2 days. Selectivity for the reduction of CO 2 to CO vs. H 2 increases for thinner crystals as well as for when two Cu cations coordinate within the intralayer cavities of PTI. Mechanistic calculations have also revealed the electrocatalytic activity for CO 2 reduction requires a smaller thermodynamic driving force with two neighboring Cu atoms per cavity as compared to a single Cu atom. These results thus establish a useful synthetic pathway to metal-coordination in a crystalline carbon nitride and show great potential for mediating stable CO 2 reduction at sizable current densities.

Chemistry↗

DOE OSTI2023

Discovery of a Hybrid System for Photocatalytic CO 2 Reduction via Attachment of a Molecular Cobalt-Quaterpyridine Complex to a Crystalline Carbon Nitride

While recent reports have demonstrated the attachment of molecular catalysts to amorphous, graphitic carbon nitrides (g-CN) for light-driven CO 2 reduction, approaches to the utilization of crystalline carbon nitrides have remained undiscovered. Herein, a functional hybrid photocatalyst system has been found using a crystalline carbon nitride semiconductor, poly(triazine imide) lithium chloride (PTI-LiCl), with a surface-attached CoCl 2 (qpy-Ph-COOH) catalyst for CO 2 reduction. The molecular catalyst attaches to PTI-LiCl at concentrations from 0.10 to 4.30 wt % and exhibits ∼96% selectivity for CO production in a CO 2 -saturated, aqueous 0.5 M KHCO 3 solution. Optimal loadings were found to be within 0.42–1.04 wt % with rates between 1,400 and 1,550 μmol CO/g·h at an irradiance of 172 mW/cm 2 (λ = 390 nm) and apparent quantum yields of ∼2%. This optimized loading is postulated to represent a balance between maximal turnover frequency (TOF; 300+ h –1 ) and excess catalyst that can limit excited-electron lifetimes, as probed via transient absorption spectroscopy. An increase in the incident irradiance yields a concomitant increase in the TOFs and CO rates only for the higher catalyst loadings, reaching up to 2,149 μmol CO/g·h with a more efficient use of the catalyst surface capacity. The lower catalyst loadings, by comparison, already function at maximal TOFs. Higher surface loadings are also found to help mitigate deactivation of the molecular catalysts during extended catalytic testing (>24 h) owing to the greater net surface capacity for CO 2 reduction, thus representing an effective strategy to extend lifetime. The hybrid particles can be deposited onto an FTO substrate to yield ∼60% Faradaic efficiency for photoelectrochemical CO production at −1.2 V vs Ag/AgCl bias. In conclusion, these results demonstrate the synergistic combination of a crystalline carbon nitride with a molecular catalyst that achieves among the highest known rates in carbon-nitride systems for the light-driven CO 2 reduction to CO in aqueous solution with >95% selectivity.

CO2 reduction↗

DOE OSTI2023

Well-Defined Iron Sites in Crystalline Carbon Nitride

Carbon nitride materials can be hosts for transition metal sites, but Mössbauer studies on iron complexes in carbon nitrides have always shown a mixture of environments and oxidation states. Here we describe the synthesis and characterization of a crystalline carbon nitride with stoichiometric iron sites that all have the same environment. The material (formula C 6 N 9 H 2 Fe 0.4 Li 1.2 Cl, abbreviated PTI/FeCl 2 ) is derived from reacting poly(triazine imide)·LiCl (PTI/LiCl) with a low-melting FeCl 2 /KCl flux, followed by anaerobic rinsing with methanol. X-ray diffraction, X-ray absorption and Mössbauer spectroscopies, and SQUID magnetometry indicate that there are tetrahedral high-spin iron(II) sites throughout the material, all having the same geometry. As a result, the material is active for electrocatalytic nitrate reduction to ammonia, with a production rate of ca. 0.1 mmol cm –2 h –1 and Faradaic efficiency of ca. 80% at −0.80 V vs RHE.

Anions↗

DOE OSTI2023

Ethanol Upgrading to n -Butanol Using Transition-Metal-Incorporated Poly(triazine)imide Frameworks

The upgrading of ethanol to n-butanol was performed using a molecular catalyst integrated into a carbon nitride support, one of the first examples of a supported molecular catalyst performing the Guerbet process. Initial studies using crystalline poly(triazine)imide (PTI) with lithium or transition-metal cations imbedded in the support together with a base as the catalyst system did not produce any significant amounts of n-butanol. However, when using the catalyst material formed by treatment of PTI-LiCl with [(Cp*)IrCl 2 ] 2 (Cp* = pentamethylcyclopentadienyl) along with sodium hydroxide, a 59% selectivity for butanol (13% yield) was obtained at 145 °C. This PTI-(Cp*)Ir material exhibited distinct UV–vis absorption features and powder X-ray diffractions which differ from those of the parent PTI-LiCl and [(Cp*)IrCl 2 ] 2 . Here, the PTI-(Cp*)Ir material was found to have a metal loading of 27% iridium per empirical unit of the framework. Along with the formation of n-butanol from the Guerbet reaction, the presence of higher chain alcohols was also observed.

Guerbet↗

DOE OSTI2023

Photoelectrochemical materials for solar energy conversion

Research and development on semiconductors for applications in solar energy conversion has witnessed rapid growth over the past several decades. With the aim of producing chemical fuels from sunlight, intense research efforts have focused on the discovery of semiconductors with crystalline structures and chemical compositions that have the potential to satisfy the complex set of required photoelectrochemical properties. This chapter focuses on the foundational structure-property relationships of selected oxide and nitride semiconductors relevant to their uses as n-/p-type photoelectrodes and as photocatalysts. Their solid-state structures and compositions are described, with a special emphasis on strategies proven effective at targeting suitable band gaps with strong visible-light absorption, efficient charge separation and diffusion of charge carriers, and optimal band edge energies for driving surface redox reactions for water splitting.

O’Donnell, Shaun↗

DOE OSTI2022

Monolayer Molecular Functionalization Enabled by Acid–Base Interaction for High-Performance Photochemical CO 2 Reduction

We report the development of a hybrid catalyst consisting of carbon nitride (CN x ) and cobalt phthalocyanine tetracarboxylic acid (CoPc-COOH), which converts CO 2 to CO with high reaction rate (1067 μmol/g·h) and high selectivity (over 98%), under simulated solar irradiation. The carboxylic acid substituents on the phthalocyanine ligands play a critical role as they bind to the amine groups of CN x to enable nearly ideal monolayer coverage of the molecular co-catalyst on the semiconductor surface and promote catalytic activity from the molecular complex. Specifically, the CN x /CoPc-COOH hybrid material achieves a reaction rate 16 times higher than a CN x material containing unsubstituted CoPc molecules. We further show that activation and deactivation of the CN x /CoPc-COOH composite, which are associated with the reduction and decomposition of CoPc-COOH, respectively, both proceed at a nearly constant rate regardless of the CO 2 reduction reaction rate. Here, the decoupling of charge carrier injection and CO 2 reduction catalysis has important mechanistic implications for future performance optimization and materials design of photocatalysts for CO 2 reduction.

14 SOLAR ENERGY↗

DOE OSTI2022

Unveiling the complex configurational landscape of the intralayer cavities in a crystalline carbon nitride

The in-depth understanding of the reported photoelectrochemical properties of the layered carbon nitride, poly(triazine imide)/LiCl (PTI/LiCl), has been limited by the apparent disorder of the Li/H atoms within its framework. To understand and resolve the current structural ambiguities, an optimized one-step flux synthesis (470 °C, 36 h, LiCl/KCl flux) was used to prepare PTI/LiCl and deuterated-PTI/LiCl in high purity. Its structure was characterized by a combination of neutron/X-ray diffraction and transmission electron microscopy. The range of possible Li/H atomic configurations was enumerated for the first time and, combined with total energy calculations, reveals a more complex energetic landscape than previously considered. Experimental data were fitted against all possible structural models, exhibiting the most consistency with a new orthorhombic model (Sp. Grp. Ama2) that also has the lowest total energy. In addition, a new Cu(I)-containing PTI (PTI/CuCl) was prepared with the more strongly scattering Cu(I) cations in place of Li, and most closely matching with the partially-disorder structure in Cmc2 1 . Thus, a complex configurational landscape of PTI is revealed to consist of a number of ordered crystalline structures that are new potential synthetic targets, such as with the use of metal-exchange reactions.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗