Engineering topics
Publications and source records attributed to Pavlov, Tsvetoslav R.
Thermophysical Property Characterization of Irradiated TRISO Compacts to include motivation, experiment background, TCM Experimental Method, TCM Results, Summary, and future work.
Thermophysical Property Characterization of Irradiated TRISO Compacts to include motivation, experiment background, TCM Experimental Method, TCM Results, Summary, and future work.
Department of Energy’s (DOE’s) Microreactor program (MRP) aims to provide the fundamental data to enable the development of microreactors. As such, material property data of critical materials for microreactor technologies are researched. Because substoichiometric yttrium dihydride (YHx, where x<2) is considered as a potential solid neutron moderator, its material property data has been combined in the Advanced Moderator Material Handbook which includes thermodynamic and thermophysical properties of YHx with the exception of irradiated material’s properties due to limited PIE. To fill the knowledge gap for the irradiated YHx, specimens and irradiation capsules were prepared at Los Alamos National Laboratory (LANL). Specimens were irradiated in the Advanced Test Reactor (ATR) at Idaho National Laboratory’s (INL’s). post-irradiation examination (PIE) was performed at INL’s Materials and Fuels Complex (MFC). This report compiles the PIE results of irradiated YHx specimens through fiscal years 2022 and 2023 (FY22-23) . The PIE data will directly be incorporated into the newer version of the Advanced Moderator Material Handbook. The main takeaways include that (i) the geometrical stability and mechanical integrity of YHx was intact with couple exceptions after high-temperature irradiations (600-800°C), (ii) hydrogen content variation due to manufacturing or irradiation in YHx caused visible surface discoloration, that is also related to the microstructural changes, (iii) qualitative comparisons of PIE methods implied that H retention was significantly higher at 600°C as compared to 800°C, (iv) thermal properties included signatures correlated with the H loss or re-gain, (v) importance of manufacturing readiness and initial as-manufactured specimens history was emphasized, (vi) the needs of targeted irradiations focusing on temperature and time parameters and very targeted PIE were specified.
Department of Energy’s (DOE’s) Microreactor program (MRP) aims to provide the fundamental data to enable the development of microreactors. As such, material property data of critical materials for microreactor technologies are researched. Because substoichiometric yttrium dihydride (YHx, where x<2) is considered as a potential solid neutron moderator, its material property data has been combined in the Advanced Moderator Material Handbook which includes thermodynamic and thermophysical properties of YHx with the exception of irradiated material’s properties due to limited PIE. To fill the knowledge gap for the irradiated YHx, specimens and irradiation capsules were prepared at Los Alamos National Laboratory (LANL). Specimens were irradiated in the Advanced Test Reactor (ATR) at Idaho National Laboratory’s (INL’s). post-irradiation examination (PIE) was performed at INL’s Materials and Fuels Complex (MFC). This report compiles the PIE results of irradiated YHx specimens through fiscal years 2022 and 2023 (FY22-23) . The PIE data will directly be incorporated into the newer version of the Advanced Moderator Material Handbook. The main takeaways include that (i) the geometrical stability and mechanical integrity of YHx was intact with couple exceptions after high-temperature irradiations (600-800°C), (ii) hydrogen content variation due to manufacturing or irradiation in YHx caused visible surface discoloration, that is also related to the microstructural changes, (iii) qualitative comparisons of PIE methods implied that H retention was significantly higher at 600°C as compared to 800°C, (iv) thermal properties included signatures correlated with the H loss or re-gain, (v) importance of manufacturing readiness and initial as-manufactured specimens history was emphasized, (vi) the needs of targeted irradiations focusing on temperature and time parameters and very targeted PIE were specified.
Results are presented on the mechanical and thermophysical property characterization of U-10Mo as part of the MP-1 qualification campaign. The thermal diffusivity, specific heat and thermal conductivity of as fabricated U-10Mo fuel foils and plates were measured using the thermal conductivity microscope (TCM), differential scanning calorimeter (DSC) and laser flash analyzer (LFA) all of which located in a shielded glove box – thermal property cell (TPC). A novel inverse method based on finite element analysis was developed to evaluate the thermal diffusivity of composite/layered materials via the LFA technique such as the 5-lyered U-10Mo monolithic fuel mini-plates.
Results are presented on the mechanical and thermophysical property characterization of U-10Mo as part of the MP-1 qualification campaign. The thermal diffusivity, specific heat and thermal conductivity of as fabricated U-10Mo fuel foils and plates were measured using the thermal conductivity microscope (TCM), differential scanning calorimeter (DSC) and laser flash analyzer (LFA) all of which located in a shielded glove box – thermal property cell (TPC). A novel inverse method based on finite element analysis was developed to evaluate the thermal diffusivity of composite/layered materials via the LFA technique such as the 5-lyered U-10Mo monolithic fuel mini-plates.
The safe and efficient operation of nuclear reactors require accurate knowledge of peak temperatures in the fuel assemblies. The temperature profiles are governed by the thermal transport properties of the fuel, namely the thermal conductivities (k) and thermal diffusivities (D). These values can be very difficult to measure as they are known to vary considerably from the measured bulk values of the fresh fuel, and quickly degrade with increasing burnup [1 -3] . Laser-based techniques have been effectively used for non-destructive and non-contact thermal transport measurements of a wide variety of materials, including nuclear materials [4-6] that would otherwise prove too hazardous or difficult to measure otherwise. In this study, a new thermoreflectance technique known as square-pulse transient thermoreflectance (SPTR) is described and used to determine the mesoscale thermal diffusivity of both uranium sesquisilicide (U3Si2) and uranium nitride (UN) phases in a composite fuel with micron level spatial resolution [7]. This technique employs a rapid train of square-wave pulses from an excitation laser to create a periodic heat flux on a gold coated sample surface. Surface adsorption results in transient film temperatures and hence rapid fluctuations in thermoreflectance that can be measured via a detection laser coupled with a digital oscilloscope. The lasers are coaxially focused on the sample surface, allowing for a sample measurement area of a single convolved laser spot size (~2 µm). A sensitivity analysis was conducted to identify key measurement parameters of this technique using reference materials with a range of thermal conductivities comparable to those of both ceramic, composite, and metal nuclear fuel types (1.4 – 27.2 W/m-K). The reference materials were measured using the new technique as well as a spatial-domain thermoreflectance technique (SDTR) previously reported for a comparison [8]. Additionally, measurements of several U3Si2 and UN phase regions of a polished UN/U3Si2 (70/30 vol.%) sample were taken, and the resulting calculated D values are reported, with both techniques showing excellent agreement between samples. This technique was used to scan a multiphase region at 5 micron increments to generate a local diffusivity map, demonstrating the utility of the techniques for measuring thermal transport properties in specimens with precipitates and secondary phases. Furthermore, the technique is currently being applied to measure thermal properties of Fast Flux Test Reactor (FFTR) irradiated metal fuel specimens whose porous microstructure make it very difficult to measure using other techniques. Comparison of the local scale measurements are compared with the pre-irradiated fuel samples to show the degradation of thermal transport in fuels due to pores from fission gas bubbles and other irradiation induced defects.