NASA NTRS2005

Electrospinning of Polyvinylidene Fluoride and Polyetherimide From Mixed Solvents

Polyvinylidene fluoride and Ultem(TradeMark) polyetherimide were dissolved in 50/50 acetone/N,N dimethylformamide (DMF) and 80/20 tetrahydrofuran/DMF, respectively, and electrospun. Polymer solution concentrations and molecular weights were changed while other spinning parameters (voltage, distance, solution feed rate) were held constant. Fiber diameters in the resulting electrospun mats varied from 0.25 to 4.4 microns, increasing with polymer concentration and molecular weight; trends in diameter were compared with trends in viscosities and surface tensions of the spinning solutions.

Morgret, Leslie D.↗

NASA NTRS2003

Electrospun Electroactive Polymers for Aerospace Applications

Electrospun piezoelectric polymers are being developed for use as a component on lightweight wings for micro-air vehicles (MAV). The goal is to incorporate fibers with tailored properties to permit dynamic control and maneuverability during flight. In particular, electrospun fiber mats of two piezoelectric polymers were investigated to ascertain their potential for the MAV application. In the work reported here, the typical experimental set-up for electrospinning was modified to induce fiber orientation in the spun mats. The morphologies of the resulting fibers and fiber mats were evaluated for various experimental conditions, and a comparison between oriented and unoriented fiber mats was carried out.

Pawlowski, Kristin J.↗