Observing the Surface Termination of LaScO 3 Perovskite Using Solid-State Nuclear Magnetic Resonance

Materials with well-defined surfaces are drawing increased attention for the design of bespoke catalysts and nanomaterials. Gaining a detailed understanding of the surfaces of these materials is an important challenge, which is often complicated by surface polymorphism and dynamic restructuring. We introduce the use of surface-enhanced NMR spectroscopy for the observation of such surfaces, focusing on LaScO 3 as an example. Here, we show that double-resonance NMR experiments correlating surface oxygen and probe molecules to the 139 La and 45 Sc nuclei at the surface reveal the material to be terminated by a ScO x monolayer. Surface-selective 17 O and 45 Sc NMR experiments further showed the material to be hydroxyl terminated and that the surface may be prone to dynamic restructuring as a result of moisture exposure. Perhaps most interestingly, surface-selective 139 La NMR experiments revealed the existence of previously undetected surface lanthanum defects, suggesting that surface-enhanced NMR may be useful as a guide in the synthesis of defect-free surfaces in the design of various nanomaterials.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2023

Treasuring trash: Pt/SrTiO 3 catalysts process plastic waste into high-value materials

Single-use plastics are ubiquitous throughout modern society because they have properties that make them desirable in a wide variety of applications, including low cost of production, high thermal and chemical stability, and tunable mechanical properties. Several of the recycling methods currently used to process single-use plastic waste, such as mechanical recycling and pyrolysis, do not selectively process plastic materials into uniform products, as would be advantageous for repurposing these materials in pursuit of a circular economy. Catalytic hydrogenolysis, whereby C–C bonds in polymers are broken over a supported catalyst in the presence of H 2 , is a promising approach to converting plastics into value-added products that can be sold commercially without further purification. Here, in this account, we present some recent advances in polyolefin hydrogenolysis, with a focus on Pt nanoparticles on SrTiO 3 nanocuboid supports (Pt/STO). Current developments in this field, general challenges, and future directions are discussed.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2023

Microwave‐Assisted Synthesis of SrTiO 3 Nanocuboids without TiCl 4

Strontium titanate (STO) nanocuboids are a novel support for Pt nanoparticle catalysts (Pt/STO). The first of many steps in commercializing Pt/STO will be developing a scalable, environmentally sustainable, and cost‐effective STO nanocuboid synthesis. Herein, Sr–Ti–OH mixtures are synthesized from various Sr 2+ and Ti 4+ reagents and treated by convection‐ and microwave‐assisted heating to obtain STO nanoparticles. These experiments clarify how phase composition of the prehydrothermal Sr–Ti–OH mixture and choice of heating method affect final nanoparticle morphology. In Sr–Ti–OH mixtures synthesized with TiCl 4 , STO is the most stable phase and precipitates prior to heating, while titania sol–gels are the most stable phase when other Ti 4+ sources are used. STO nanocrystals always form when Sr–Ti–OH mixtures are treated by convection heating, though nanocuboids are only observed if STO precipitates from the Sr–Ti–OH mixture. Microwave‐assisted hydrothermal treatment more rapidly heats the precursor solution, and thus, STO nanocuboids can form from a variety of Sr–Ti–OH mixtures regardless of mixture composition. Two microwave syntheses of STO nanocuboids are reported: one which uses TiCl 4 as a Ti 4+ source, and another that uses titanium(IV) bis(ammonium lactato) dihydroxide ([NH 4 CH 3 CH(O)CO 2 ] 2 Ti(OH) 2 ), a water‐stable Ti 4+ complex.

Peczak, Ian L.↗

DOE OSTI2022

Synthesis of platinum nanoparticles on strontium titanate nanocuboids via surface organometallic grafting for the catalytic hydrogenolysis of plastic waste

Pt/SrTiO 3 (Pt/STO), prepared on small scale by atomic layer deposition (ALD), is a capable heterogeneous catalyst for the selective hydrogenolysis of polyolefins to hydrocarbon oils, providing a promising approach for upcycling plastic waste. However, because deposition by ALD is costly and resource-intensive, a new synthesis of Pt/STO is needed to effectively scale catalyst production and pursue the commercialization of upcycling processes. To that effect, this work details a scalable deposition method for Pt/STO made by surface organometallic chemistry (SOMC) techniques using Pt(II) acetylacetonate or and trimethyl(methylcyclopentadienyl)platinum. The STO support was calcined (550 °C), treated with ozone (200 °C), and finally steamed (200 °C) to afford a clean STO surface populated with only hydroxyl groups. Pt precursors were dissolved in toluene and deposited onto STO. After reduction at 300 °C, the STO support was decorated with 1.0–1.5 nm Pt nanoparticles. The size and loading of these nanoparticles were varied by employing a multi-cycle deposition and oxidation and/or reduction process designed to ALD techniques. In conclusion, these Pt/STO catalysts hydrogenolyzed isotactic polypropylene into liquid products (>95% yield) with average molecular weights of 200–300 Da (~25 carbon atoms) and narrow size distributions at 300 °C and 180 psi H 2 .

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2022

Effect of Macro- and Microstructures on Catalytic Hydrogenolysis of Polyolefins

Here, polyethylenes of varying molecular weight and branch density, as well as polypropylenes of varying molecular weight and tacticity, were catalytically converted to lower-molecular-weight liquid products to showcase how these various properties in a mixed waste plastic stream could affect the final product. A Pt nanoparticle on a strontium titanate nanocuboid (Pt/STO) catalyst was used under solvent-free conditions in the presence of 170 psi of H 2 at 300 °C for hydrogenolysis. The initial molecular weight of polyethylene was found to have a moderate effect on the yield to the final product (ranging from 55 wt% for M n ~ 7600 Da to 67 wt% for M n ~ 50,950 Da). The microstructure, defined as the length and density of branches in a polymer, of higher-molecular-weight polymers was the dominant factor in determining the yield (ranging from 67 wt% for M n ~ 50,950 Da for linear low-density polyethylene (LLDPE) with C 2 branches to 97 wt% for M n ~ 38,850 Da for LLDPE with C 6 branches). The same products (M n = C 29 –C 46 , Ð = 1.1–1.6) and distribution of undesired light gases (C 1 –C 4 ≈ 90 mol%, C 5 –C 8 ≈ 10 mol%) are obtained from conversions of PE of varying molecular weight. The tacticity of polypropylene at a given molecular weight had a significant effect on the molecular weight of the final product, while not strongly affecting conversion. Hydrogenolysis of isotactic polypropylene (iPP) produced ≈C 18 with a wider polydispersity (Ð ~ 1.4) compared to the narrow ≈C 64 (Ð ~ 1.0) and ≈C 54 (Ð ~ 1.0) products from atactic (aPP) and syndiotactic (sPP) polypropylene, respectively. The stereochemistry of the methyl groups dictates the shape and structure of the polymer in the melt, which in turn affects how the hydrocarbon chain interacts with the catalyst surface, thereby impacting the number of C–C scissions. These results show how various characteristics such as the molecular weight and structure of a waste plastic stream could affect the final product.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

Scalable Synthesis of Pt/SrTiO 3 Hydrogenolysis Catalysts in Pursuit of Manufacturing-Relevant Waste Plastic Solutions

Here, an improved hydrothermal synthesis for shape-controlled, size-controlled 60 nm SrTiO 3 nanocuboid (STO NC) supports, which facilitates the scalable creation of platinum nanoparticles catalyst supported on STO (Pt/STO) for the chemical conversion of waste polyolefins, is reported herein. This synthetic method: 1) produces STO NC supports with average sizes ranging from 25 – 80 nm with narrow size distributions 2) demonstrates how SrCO 3 formation and variation in solution pH prevent the formation of STO NCs, and 3) establishes that STO nucleation prior to the hydrothermal treatment favors nanocuboid formation. The updated hydrothermal synthesis was scaled-up and conducted in a 4L batch reactor, resulting in STO NCs of comparable size and morphology (m = 22.5 g, d avg = 58.6 ± 16.2 nm) to those synthesized under standard hydrothermal conditions in a lab-scale 125 mL autoclave reactor. Size-controlled STO NCs, ranging in roughly 10 nm increments from the 25 nm to 80 nm, were used to support Pt deposited through strong electrostatic adsorption (SEA), a practical and scalable solution-based method. Using SEA techniques and a STO support with an average size of 39.3 ± 6.3 nm, a Pt/STO catalyst with 3.6 wt% Pt was produced and used for high-density polyethylene hydrogenolysis under previously-reported conditions (170 psi H 2 , 300°C, 96h; final product: M w = 2400, Ð = 1.03). As a well-established model system for studying the behavior of heterogeneous catalysts and their supports in reactions, the Pt/STO system detailed in this work presents a unique opportunity to simultaneously convert waste plastic into commercially-viable products while gaining fundamental insight into the mechanism of polyethylene hydrogenolysis.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗