Engineering topics
Publications and source records attributed to Pei, Allen.
An anode includes: (1) a current collector; and (2) an interfacial layer disposed over the current collector. The interfacial layer includes an ion-conductive organic network including anionic coordination units, organic linkers bonded through the anionic coordination units, and counterions dispersed in the ion-conductive organic network.
Poor fast-charge capabilities limit the usage of rechargeable Li metal anodes. Understanding the connection between charging rate, electroplating mechanism, and Li morphology could enable fast-charging solutions. In this report we develop a combined electroanalytical and nanoscale characterization approach to resolve the current-dependent regimes of Li plating mechanisms and morphology. Measurement of Li + transport through the solid electrolyte interphase (SEI) shows that low currents induce plating at buried Li||SEI interfaces, but high currents initiate SEI-breakdown and plating at fresh Li||electrolyte interfaces. The latter pathway can induce uniform growth of {110}-faceted Li at extremely high currents, suggesting ion-transport limitations alone are insufficient to predict Li morphology. At battery relevant fast-charging rates, SEI-breakdown above a critical current density produces detrimental morphology and poor cyclability. Thus, prevention of both SEI-breakdown and slow ion-transport in the electrolyte is essential. This mechanistic insight can inform further electrolyte engineering and customization of fast-charging protocols for Li metal batteries.
In lithium-sulfur (Li-S) chemistry, the electrically/ionically insulating nature of sulfur and Li 2 S leads to sluggish electron/ion transfer kinetics for sulfur species conversion. Sulfur and Li 2 S are recognized as solid at room temperature, and solid-liquid phase transitions are the limiting steps in Li-S batteries. Here, we visualize the distinct sulfur growth behaviors on Al, carbon, Ni current collectors and demonstrate that (i) liquid sulfur generated on Ni provides higher reversible capacity, faster kinetics, and better cycling life compared to solid sulfur; and (ii) Ni facilitates the phase transition (e.g., Li 2 S decomposition). Accordingly, light-weight, 3D Ni-based current collector is designed to control the deposition and catalytic conversion of sulfur species toward high-performance Li-S batteries. This work provides insights on the critical role of the current collector in determining the physical state of sulfur and elucidates the correlation between sulfur state and battery performance, which will advance electrode designs in high-energy Li-S batteries.
Lithium (Li) metal is the ultimate anode material for Li batteries because of its highest capacity among all candidates. Recent research has focused on stable interphase and host materials to address its low stability and reversibility. Here, we discover that tortuosity is a critical parameter affecting the morphology and electrochemical performances of hosted Li anodes. In three types of hosts—vertically aligned, horizontally aligned, and random reduced graphene oxide (rGO) electrodes with tortuosities of 1.25, 4.46, and 1.76, respectively—we show that high electrode tortuosity causes locally higher current density on the top surface of electrodes, resulting in thick Li deposition on the surface and degraded cycling performance. Low electrode tortuosity in the vertically aligned rGO host enables homogeneous Li transport and uniform Li deposition across the host, realizing greatly improved cycling stability. Furthermore, using this principle of low tortuosity, the designed electrode shows through-electrode uniform morphology with anodic Coulombic efficiency of ~99.1% under high current and capacity cycling conditions.
It has recently been shown that sulfur, a solid material in its elementary form S8, can stay in a supercooled state as liquid sulfur in an electrochemical cell. We establish that this newly discovered state could have implications for lithium–sulfur batteries. Here, through in situ studies of electrochemical sulfur generation, we show that liquid (supercooled) and solid elementary sulfur possess very different areal capacities over the same charging period. To control the physical state of sulfur, we studied its growth on two-dimensional layered materials. We found that on the basal plane, only liquid sulfur accumulates; by contrast, at the edge sites, liquid sulfur accumulates if the thickness of the two-dimensional material is small, whereas solid sulfur nucleates if the thickness is large (tens of nanometres). Correlating the sulfur states with their respective areal capacities, as well as controlling the growth of sulfur on two-dimensional materials, could provide insights for the design of future lithium–sulfur batteries.