Environmental effects on high strain rate properties of graphite/epoxy composite
The effects of hygrothermal conditions on the high-strain-rate properties of a unidirectional graphite/epoxy material, AS4/3501-6, were evaluated using standard physical and mechanical tests to determine the properties of the lamina. A time-temperature-moisture equivalence principle was applied to obtain master curves for the longitudinal, transverse, and in-plane shear moduli and corresponding strengths and ultimate strains of the specimens. It was found that the longitudinal properties of the material remained unchanged at all conditions, except for the longitudinal modulus, which showed a slight increase with temperature, moisture, and strain rate. On the other hand, all transverse and intralaminar shear properties were found to decrease with increasing temperature and moisture contents at a fixed strain rate.