Publications and source records attributed to Peralta, Pedro.

4 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2021

Micro-cantilever beam experiments and modeling in porous polycrystalline UO 2

Understanding the impact of microstructure on the thermo-mechanical behavior of oxide nuclear fuels is vital to predicting their performance through multiscale models. Evaluating the mechanical properties at the sub-grain length scale is key to developing these multiscale models. In this work, 3D finite element (FE) models were constructed to simulate the micrometer-scale bending of micro-cantilever beams fabricated using porous polycrystalline uranium dioxide (UO 2 ) and tested at room temperature. Here, the results showed that the porosity and elastic anisotropy of individual grains can play a significant role in determining the effective mechanical properties of the material deduced from the tests. Specifically, the porosity had a non-negligible effect, given that the pore size was of the same order of magnitude as the dimensions of the micro-beams. Correlations between load-deflection data, pore location, and elastic properties (effective Young's modulus) were investigated using UO 2 micro-beam FE models, where pore clusters were included and placed at different locations along the length of the beam. Results indicated that the presence of pore clusters near the substrate, i.e., the clamp of the micro-cantilever beam, has the strongest effect on the load-deflection behavior, with the porosity leading to a reduction of stiffness that is the largest for any location of the pore clusters. Furthermore, it was also found that pore clusters located towards the middle of the span and close to the end of the beam have a comparatively small effect on the load-deflection behavior. Therefore, it is concluded that accurate estimates of Young's modulus can be obtained from micro-cantilever experiments after accounting for porosity on the one third of the beam length close to the clamp. This, in turn, provides an avenue to improve microscale experiments and their analysis in porous, anisotropic elastic materials.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2021

Probing High-Pressure Structural Evolution in Polyurea with In Situ Energy-Dispersive X-ray Diffraction and Molecular Dynamics Simulations

Polyurea, an elastomer with a phase-segregated microstructure, has been proven as an effective coating in defense applications. To gain a more complete understanding of the high-pressure atomic-level morphology of these phases and to validate molecular dynamics (MD) simulations, multi-angle energy-dispersive X-ray diffraction experiments were performed in situ up to pressures of ~6 GPa at room temperature. Structure factors were obtained and compared to MD simulations with an average error of less than 5% between major peak positions. The first sharp diffraction peak shifted from 4.56 Å to lower d-spacing with pressure, indicating compression between hard segments. This was further supported by the behavior of a peak at ~3.86 Å from the pair distribution function (PDF), suspected to represent π-stacking and separation between soft segments. Compression within the hard segments themselves is minimal as low-r peaks in the PDF are not greatly affected by pressure.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2020

Nucleation and growth of voids in shock loaded copper bicrystals

Understanding the evolution of damage and deformation due to spall at grain boundaries can provide a basis for connecting micro- to macroscale failure behavior in metals under extreme conditions. Copper bicrystal samples were shock loaded using flyer-plate impacts in a light gas gun with shock stresses ranging from 3 to 6 GPa. Pulse duration as well as crystal orientation along the shock direction were varied for a fixed boundary misorientation to determine their effects on void nucleation and coalescence. Samples were soft recovered and cross-sectioned to characterize damage using electron backscattering diffraction and scanning electron microscopy to gather information on damage characteristics at and around the GB, with emphasis on growth of boundary and bulk voids. Chemistry and composition analysis were also performed on samples to determine if trace elements present in a sample affected the threshold for void nucleation. Results show that the kinetics of damage growth at the boundary are strongly affected by stress level and impurities. It was found that the boundary selected had a similar or even lower tendency to show damage than the bulk at low pulse durations and amplitudes. As pulse duration and amplitude increased damage localized at the boundary, which was found to consist of many small voids, indicating that the boundary experienced rapid void nucleation and coalescence. Furthermore, the presence of impurities correlated strongly with scatter on damage evolution.

36 MATERIALS SCIENCE↗