DOE OSTI2025

Physical model and experimental validation of a high temperature proton exchange membrane electrochemical hydrogen pump cell for efficient single-stage extraction of low concentration hydrogen gas

There is interest in valorization of existing natural gas infrastructure to facilitate the co-transportation of hydrogen via blending of hydrogen gas initially at limited concentrations of 1–20 vol% H2 and to subsequently extract hydrogen at fuel cell quality standards (SAE J2719/ISO14687-2). High temperature proton exchange membrane electrochemical hydrogen pump (HT-PEM EHP) based on phosphoric acid doped polybenzimidazole (PA-PBI) exhibits good performance at elevated temperatures (>120 °C), which provides desirable tolerance to non-methane natural gas constituents that are problematic for lower temperature based EHP. To better understand the suitability of the HT-PEM EHP for such gas separation processes, a two-dimensional model of EHP based on PA-PBI was developed. The model is validated for several relevant operating conditions and across cells with differing amounts of phosphoric acid content in the electrodes. Operando micro x-ray computed tomography (CT) imaging of an HT-PEM EHP was used to further validate physical parameters and assumptions of the model. The impacts of pressure, relative humidity of the anode feed, and concentration of feed gases on separation performance are investigated. This study shows that a specific energy of separation of 5.1 kWh/kg H2 at a hydrogen recovery factor (HRF) of 50 vol% can be achieved in a single stage with the EHP, producing fuel cell quality hydrogen purity of 99.99 vol% H2 from a 2 vol% H2/CH4 feed blend, while pressurizing the product H2 at a pressure ratio of 1.3 relative to feed pressure.

Stansberry, John M↗

DOE OSTI2022

Highly Durable Fluorinated High Oxygen Permeability Ionomers for Proton Exchange Membrane Fuel Cells

For proton exchange membrane fuel cells to be cost-competitive in light- and heavy-duty vehicle applications, their Pt content in the catalyst layers needs to be lowered. However, lowering the Pt content results in voltage losses due to high local oxygen transport resistances at the ionomer–Pt interface. It is therefore crucial to use ionomers that have higher oxygen permeability than Nafion. In this paper, novel high oxygen permeability ionomers (HOPIs) are presented, with up to five times higher oxygen permeability than Nafion, synthesized by copolymerization of perfluoro-2,2-dimethyl-1,3-dioxole (PDD) with perfluoro(4-methyl-3,6-dioxaoct-7-ene) sulfonyl fluoride (PFSVE). PDD is the source of higher permeability due to its open ring structure, while PFSVE provides ionic conductivity. Optimization of PDD content and equivalent weight enables increased fuel cell performance, mainly at high current densities, where HOPIs can achieve power densities >1.25 W cm -2 and exceed the 0.8 A cm -2 U.S. Department of Energy durability target by losing only 4.5 mV, which is over six times less than 30 mV. Finally, the interactions between HOPI and SO 3 - groups with a PtCo/C catalyst are also elucidated here at a fundamental level.

25 ENERGY STORAGE↗

DOE OSTI2021

Probing Heterogeneous Degradation of Catalyst in PEM Fuel Cells under Realistic Automotive Conditions with Multi-Modal Techniques

The heterogeneity of polymer electrolyte fuel cell catalyst degradation is studied under varied relative humidity and types of feed gas. Accelerated stress tests (ASTs) are performed on four membrane electrode assemblies (MEAs) under wet and dry conditions in an air or nitrogen environment for 30 000 square voltage cycles. The largest electrochemically active area loss is observed for MEA under wet conditions in a nitrogen gas environment AST due to constant upper potential limit of 0.95 V and significant water content. The mean Pt particle size is larger for the ASTs under wet conditions compared to dry conditions, and the Pt particle size under land is generally larger than under the channel. Observations from ASTs in both conditions and gas environments indicate that water content promotes Pt particle size growth. ASTs under wet conditions and an air environment show the largest difference in Pt particle size growth for inlet versus outlet and channel versus land, which can be attributed to larger water content at outlet and under land compared to inlet and under channel. From X-ray fluorescence experiments Pt particle size increase is a local phenomenon as Pt loading remains relatively uniform across the MEA.

25 ENERGY STORAGE↗

DOE OSTI2021

Interpreting Ionic Conductivity for Polymer Electrolyte Fuel Cell Catalyst Layers with Electrochemical Impedance Spectroscopy and Transmission Line Modeling

A cathode catalyst layer containing optimally distributed ionomer is critical to reduce the platinum loading and increase its utilization in polymer electrolyte fuel cells. Here, electrochemical impedance spectroscopy (EIS) was used to measure effective ionic conductivity of pseudo catalyst layers (PCLs) at a relative humidity (RH) range of 50%-120%. These results are compared to previous work using the hydrogen pump (HP) method. EIS effective ionic conductivity results reported here are higher than those from the HP because in the HP set-up ionic pathways must be effectively connected through the PCL to be counted, whereas in the EIS measurement, ionomer segments that are in contact with the membrane but are not effectively connected all the way through the PCL can be detected. Double layer capacitances and effective ionic conductivities of Pt/C catalyst layers with various supports and ionomer to carbon (I/C) ratios were studied. High surface area carbon support resulted in a lower effective ionic conductivity compared to the graphitized carbon support due to worse ionomer dispersion. Effective ionic conductivities of Pt/C layers were compared to that of PCLs. On average, effective ionic conductivities of Pt/C layers were higher than PCLs because of possible carbon agglomeratio n within the PCLs.