Formation of a metastable ferromagnetic tau phase during containerless melt processing in Mn-Al-C alloys
This paper reports the production of a metastable ferromagnetic tau phase directly from the melt in Mn(0.55)Al(0.433)C(0.017), using a containerless processing method involving levitation melting followed by quenching. Using the results from differential thermal analysis measurements and an analysis of the phase equilibria, it was found that the minimum amount of undercooling level required for ferromagnetic metastable tau phase formation in this alloy was Delta T = 87 K. The attainment of this undercooling may be facilitated by the application of containerless melt processing.
Containerless processing of undercooled melts
The investigation focused on the control of microstructural evolution in Mn-Al, Fe-Ni, Ni-V, and Au-Pb-Sb alloys through the high undercooling levels provided by containerless processing, and provided fundamental new information on the control of nucleation. Solidification analysis was conducted by means of thermal analysis, x-ray diffraction, and metallographic characterization on samples processed in a laboratory scale drop tube system. The Mn-Al alloy system offers a useful model system with the capability of phase separation on an individual particle basis, thus permitting a more complete understanding of the operative kinetics and the key containerless processing variables. This system provided the opportunity of analyzing the nucleation rate as a function of processing conditions and allowed for the quantitative assessment of the relevant processing parameters. These factors are essential in the development of a containerless processing model which has a predictive capability. Similarly, Ni-V is a model system that was used to study duplex partitionless solidification, which is a structure possible only in high under cooling solidification processes. Nucleation kinetics for the competing bcc and fcc phases were studied to determine how this structure can develop and the conditions under which it may occur. The Fe-Ni alloy system was studied to identify microstructural transitions with controlled variations in sample size and composition during containerless solidification. This work was forwarded to develop a microstructure map which delineates regimes of structural evolution and provides a unified analysis of experimental observations. The Au-Pb-Sb system was investigated to characterize the thermodynamic properties of the undercooled liquid phase and to characterize the glass transition under a variety of processing conditions. By analyzing key containerless processing parameters in a ground based drop tube study, a carefully designed flight experiment may be planned to utilize the extended duration microgravity conditions of orbiting spacecraft.
Microstructural transitions during containerless processing of undercooled Fe-Ni alloys
In order to identify the possible hierarchy of microstructural pathways and transitions, a systematic evaluation of the microstructural evolution in undercooled Fe-Ni alloys was performed on uniformly processed samples covering seven orders of magnitude in volume. At appropriate undercooling levels, alternate solidification pathways become thermodynamically possible and metastable product structures can result from the operation of competitive solidification kinetics. For thermal history evaluation, a heat flow analysis was applied and tested with large Fe-Ni alloy particles (1 to 3 mm) to assess undercooling potential. Alloy powders (10 to 150 microns), with large liquid undercoolings, were studied under the same composition and processing conditions to evaluate the solidification kinetics and microstructural evolution, including fcc/bcc phase selection and the thermal stability of a retained metastable bcc phase. The identification of microstructural transitions with controlled variations in sample size and composition during containerless solidification processing was used to develop a microstructure map which delineates regimes of structural evolutions and provides a unified analysis of experimental observations in the Fe-Ni system.
Formation of a metastable ferromagnetic tau phase during containerless melt processing and rapid quenching in Mn-Al-C alloys
Solidification of selected Mn-Al-C alloys during containerless levitation and rapid quenching has yielded the first report for a ferromagnetic metastable tau phase formed directly from the melt. Complete solidification to tau phase was interrupted by the competitive evolution of an equilibrium epsilon phase during recalescence. The amount of undercooling required to produce the metastable ferromagnetic tau phase in a Mn(0.55)Al(0.433)C(0.017) alloy during solidification was estimated as approximately 470 K based on differential thermal analysis results. When the alloy carbon content was increased to 3.4 at. pct, transition in structure development occurred so that the samples exhibited gamma 2 phase formation as well as tau and epsilon phases.
Free energy change of off-eutectic binary alloys on solidification
A formula for the free energy difference between the undercooled liquid phase and the stable solid phase is derived for off-eutectic binary alloys in which the equilibrium solid/liquid transition takes place over a certain temperature range. The free energy change is then evaluated numerically for a Bi-25 at. pct Cd alloy modeled as a sub-subregular solution.
JTEC panel report on advanced composites in Japan
The JTEC Panel on Advanced Composites visited Japan and surveyed the status and future directions of Japanese high performance ceramic and carbon fibers and their composites in metal, intermetallic, ceramic and carbon matrices. The panel's interests included not only what composite systems were chosen, but also how these systems were developed. A strong carbon and fiber industry makes Japan the leader in carbon fiber technology. Japan has initiated an oxidation resistant carbon/carbon composite program. The goals for this program are ambitious, and it is just starting, but its progress should be closely monitored in the United States.
Containerless processing of undercooled melts
All practical solidification processes involve some level of melt undercooling. Usually in bulk liquids crystallization is initiated at a heterogeneous nucleation site at low undercooling. The realization of appreciable levels of liquid undercooling requires some control over the kinetics of crystal nucleation. One level of control is available in containerless processing where the capability to melt and solidify samples without a container removes a major source of impurities and heterogeneous nucleation sites which can be effective in promoting large undercooling and in studying other potential nucleants. The microgravity environment offers a unique opportunity for containerless processing of large liquid samples with negligible melt disturbance and continuous temperature measurement throughout processing. Perhaps the most important potential for microgravity containerless processing lies in the significant structural control to develop distinct microstructures and metastable phases during solidification at high undercooling.
Noncontact temperature measurement: Requirements and applications for metals and alloys research
Temperature measurement is an essential capability for almost all areas of metals and alloys research. In the microgravity environment many of the science priorities that have been identified for metals and alloys also require noncontact temperature measurement capability. For example, in order to exploit the full potential of containerless processing, it is critical to have available a suitable noncontact temperature measurement system. This system is needed to track continuously the thermal history, including melt undercooling and rapid recalescence, of relatively small metal spheres during free-fall motion in drop tube systems. During containerless processing with levitation-based equipment, accurate noncontact temperature measurement is required to monitor one or more quasi-static samples with sufficient spatial and thermal resolution to follow the progress of solidification fronts originating in undercooled melts. In crystal growth, thermal migration, coarsening and other experiments high resolution thermal maps would be a valuable asset in the understanding and modeling of solidification processes, fluid flows and microstructure development. The science and applications requirements place several constraints on the spatial resolution, response time and accuracy of suitable instrumentation.
The glass transition, crystallization and melting in Au-Pb-Sb alloys
The glass transition, crystallization and melting of Au(55)Pb(22.5)Sb(22.5) alloys have been studied by differential scanning calorimetry DSC. Crystallization on heating above the glass transition temperature Tg (45 C) begins at 64 C. Further crystallization events are observed at 172 C and 205 C. These events were found to correspond to the formation of the intermetallic compounds AuSb2, Au2Pb, and possibly AuPb2, respectively. Isothermal DSC scans of the glassy alloy above Tg were used to monitor the kinetics of crystallization. The solidification behavior and heat capacity in the glass-forming composition range were determined with droplet samples. An undercooling level of 0.3T(L) below the liquidus temperature T(L) was achieved, resulting in crystallization of different stable and metastable phases. The heat capacity C(P) of the undercooled liquid was measured over an undercooling range of 145 C.
Containerless processing of undercooled melts
Containerless drop tube processing allows for significant levels of liquid undercooling through control of parameters such as sample size, surface coating and cooling rate. A laboratory scale (3 m) drop tube has been developed which allows the undercooling and solidification behavior of powder samples to be evaluated under low gravity free-fall conditions. The level of undercooling obtained in an InSb-Sb eutectic alloy has been evaluated by comparing the eutectic spacing in drop tube samples with a spacing/undercooling relationship established using thermal analysis techniques. Undercoolings of 0.17 and 0.23 T(e) were produced by processing under vacuum and He gas conditions respectively. Alternatively, the formation of an amorphous phase in a Ni-Nb eutectic alloy indicates that undercooling levels of approximately 500 C were obtained by drop tube processing. The influence of droplet size and gas environment on undercooling behavior in the Ni-Nb eutectic was evaluated through their effect on the amorphous/crystalline phase ratio. To supplement the structural analysis, heat flow modeling has been developed to describe the undercooling history during drop tube processing, and the model has been tested experimentally.
Rapid solidification of highly undercooled liquids
Melt undercooling is considered as a fundamental processing parameter for powders and for melt-spun and surface-melted samples. With reference to experimental results for Mn, Al, Al-Be, Al-Fe, and InSb-Sb powders, it is shown that the undercooling behavior in droplets is influenced by powder size, coating, melt superheat, and cooling rate. Droplet sample microstructures can be compared directly with those of rapidly quenched powders to establish the application of laboratory-scale studies to large-scale processing.
Undercooling and crystallization behaviour of antimony droplets
The droplet emulsion technique is presently used to examine the undercooling and crystallization behavior of pure antimony. Control of droplet size and applied cooling rate allowed maximum undercooling to be extended from 0.08 to 0.23 T(m). A droplet coating was produced by means of emulsification which appears to furnish a favorable crystallographic matching for effective nucleation catalysis of a metastable simple cubic structure. Thermal analysis shows the melting temperature of the single cubic phase to be about 625 C.
Containerless Processing of Undercooled Melts
The physical mechanisms controlling liquid undercooling were studied for application to solidification processing methods. The undercooling potential of containerless processing was assessed on droplet samples of high melting temperature metals drop tube and drop tower facilities and in a laboratory-scale apparatus. New insight into nucleation and crystal growth will be obtained in undercooled liquids of high melting temperature iron and nickel-base systems. The processing parameters include melt superheat, droplet size and particle statistics and droplet surface coating. The solidification behavior is determined by thermal analysis and by structural and metallographic characterization.
Solidification of undercooled liquids
During rapid solidification processing (RSP) the amount of liquid undercooling is an important factor in determining microstructural development by controlling phase selection during nucleation and morphological evolution during crystal growth. While undercooling is an inherent feature of many techniques of RSP, the deepest undercoolings and most controlled studies have been possible in carefully prepared fine droplet samples. From past work and recent advances in studies of nucleation kinetics it has become clear that the initiation of crystallization during RSP is governed usually by heterogeneous sites located at surfaces. With known nucleant sites, it has been possible to identify specific pathways of metastable phase formation and microstructural development in alloys. These advances have allowed for a clearer assessment of the interplay between undercooling, cooling rate and particle size statistics in structure formation. New approaches to the examination of growth processes have been developed to follow the thermal behavior and morphology in small samples in the period of rapid crystallization and recalescence. Based upon the new experimental information from these studies, useful models can be developed for the overall solidification process to include nucleation behavior, thermodynamic constraints, thermal history, growth kinetics, solute redistribution and resulting structures. From the refinement of knowledge concerning the underlying factors that govern RSP a basis is emerging for an effective alloy design and processing strategy.
Amorphous metallizations for high-temperature semiconductor device applications
The initial results of work on a class of semiconductor metallizations which appear to hold promise as primary metallizations and diffusion barriers for high temperature device applications are presented. These metallizations consist of sputter-deposited films of high T sub g amorphous-metal alloys which (primarily because of the absence of grain boundaries) exhibit exceptionally good corrosion-resistance and low diffusion coefficients. Amorphous films of the alloys Ni-Nb, Ni-Mo, W-Si, and Mo-Si were deposited on Si, GaAs, GaP, and various insulating substrates. The films adhere extremely well to the substrates and remain amorphous during thermal cycling to at least 500 C. Rutherford backscattering and Auger electron spectroscopy measurements indicate atomic diffussivities in the 10 to the -19th power sq cm/S range at 450 C.