Oxygen vacancy migration and impact on high voltage DC polarization in 0.8BaTiO 3 –0.2BiZn 0.5 Ti 0.5 O 3

Electrical polarization and defect transport are examined in 0.8BaTiO 3 –0.2BiZn 0.5 Ti 0.5 O 3 , an attractive capacitor material for high power electronics. Oxygen vacancies are suggested to be the majority charge carrier at or below 250°C with a grain conduction hopping activation energy of 0.97 eV and 0.92 eV for thermally stimulated depolarization current (TSDC) and impedance spectroscopy measurements, respectively. At higher temperature, thermally generated electronic conduction with an activation energy of 1.6 eV is dominant. Significant oxygen vacancy concentration is indicated (up to ~1%) due to cation vacancy formation (i.e., acceptor defects) from observed Bi (and likely Zn) volatility. Oxygen vacancy diffusivity is estimated to be 10 -12.8 cm 2 /s at 250°C. Low diffusivity and high activation energies are indicative of significant defect interactions. Dipolar oxygen vacancy defects are also indicated, with an activation energy of 0.59 eV from TSDC measurements. In conclusion, the large oxygen vacancy content leads to a short lifetime during high voltage (30 kV/cm), high temperature (250°C) direct current (DC) electrical measurements.

46 INSTRUMENTATION RELATED TO NUCLEAR SCIENCE AND ↗
DOE OSTI2024

Can a Coating Mitigate Molten Na Dendrite Growth in NaSICON Under High Current Density?

Alkali metals are among the most desirable negative electrodes for long duration energy storage due to their extremely high capacities. Currently, only high-temperature (>250 °C) batteries have successfully used alkali electrodes in commercial applications, due to limitations imposed by solid electrolytes, such as low conductivity at moderate temperatures and susceptibility to dendrites. Toward enabling the next generation of grid-scale, long duration batteries, we aim to develop molten sodium (Na) systems that operate with commercially attractive performance metrics including high current density (>100 mA cm –2 ), low temperature (<200 °C), and long discharge times (>12 h). In this work, we focus on the performance of NaSICON solid electrolytes in sodium symmetric cells at 110 °C. Specifically, we use a tin (Sn) coating on NaSICON to reduce interfacial resistance by a factor of 10, enabling molten Na symmetric cell operation with “discharge” durations up to 23 h at 100 mA cm –2 and 110 °C. Unidirectional galvanostatic testing shows a 70% overpotential reduction, and electrochemical impedance spectroscopy (EIS) highlights the reduction in interfacial resistance due to the Sn coating. Detailed scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS) show that Sn-coated NaSICON enables current densities of up to 500 mA cm –2 at 110 °C by suppressing dendrite formation at the plating interface (Mode I). In conclusion, this analysis also provides a mechanistic understanding of dendrite formation at current densities up to 1000 mA cm –2 , highlighting the importance of effective coatings that will enable advanced battery technologies for long-term energy storage.

25 ENERGY STORAGE↗
DOE OSTI2023

Electrode Blocking Due to Redox Reactions in Aluminum Chloride-Sodium Iodide Molten Salts

Iodide redox reactions in molten NaI/AlCl 3 are shown to generate surface-blocking films, which may limit the useful cycling rates and energy densities of molten sodium batteries below 150 °C. An experimental investigation of electrode interfacial stability at 110 °C reveals the source of the reaction rate limitations. Electrochemical experiments in a 3-electrode configuration confirm an increase of resistance on the electrode surface after oxidation or reduction current is passed. Using chronopotentiometry, chronoamperometry, cyclic voltammetry, and electrochemical impedance spectroscopy, the film formation is shown to depend on the electrode material (W, Mo, Ta, or glassy carbon), as well as the Lewis acidity and molar ratio of I − /I 3 − in the molten salt electrolytes. These factors impact the amount of charge that can be passed at a given current density prior to developing excessive overpotential due to film formation that blocks the electrode surface. The results presented here guide the design and use of iodide-based molten salt electrolytes and electrode materials for grid scale battery applications.

25 ENERGY STORAGE↗
DOE OSTI2023

Dynamic high pressure phase transformation of ZrW 2 O 8

Phase transformations under high strain rates (dynamic compression) are examined in situ on ZrW 2 O 8 , a negative thermal expansion ternary ceramic displaying polymorphism. Amorphization, consistent with prior quasi-static measurements, was observed at a peak pressure of 3.0 GPa under dynamic conditions, which approximate those expected during fabrication. Evidence of partial amorphization was observed at lower pressure (1.8 GPa) that may be kinetically restrained by the short (<~150 ns) time scale of the applied high pressure. The impact of kinetics of pressure-induced amorphization from material fabrication methods is briefly discussed.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2022

Singleplex, multiplex and pooled sample real-time RT-PCR assays for detection of SARS-CoV-2 in an occupational medicine setting

Abstract For workplaces which cannot operate as telework or remotely, there is a critical need for routine occupational SARS-CoV-2 diagnostic testing. Although diagnostic tests including the CDC 2019-Novel Coronavirus (2019-nCoV) Real-Time RT-PCR Diagnostic Panel (CDC Diagnostic Panel) (EUA200001) were made available early in the pandemic, resource scarcity and high demand for reagents and equipment necessitated priority of symptomatic patients. There is a clearly defined need for flexible testing methodologies and strategies with rapid turnaround of results for (1) symptomatic, (2) asymptomatic with high-risk exposures and (3) asymptomatic populations without preexisting conditions for routine screening to address the needs of an on-site work force. We developed a distinct SARS-CoV-2 diagnostic assay based on the original CDC Diagnostic Panel (EUA200001), yet, with minimum overlap for currently employed reagents to eliminate direct competition for limited resources. As the pandemic progressed with testing loads increasing, we modified the assay to include 5-sample pooling and amplicon target multiplexing. Analytical sensitivity of the pooled and multiplexed assays was rigorously tested with contrived positive samples in realistic patient backgrounds. Assay performance was determined with clinical samples previously assessed with an FDA authorized assay. Throughout the pandemic we successfully tested symptomatic, known contact and travelers within our occupational population with a ~ 24–48-h turnaround time to limit the spread of COVID-19 in the workplace. Our singleplex assay had a detection limit of 31.25 copies per reaction. The three-color multiplexed assay maintained similar sensitivity to the singleplex assay, while tripling the throughput. The pooling assay further increased the throughput to five-fold the singleplex assay, albeit with a subtle loss of sensitivity. We subsequently developed a hybrid ‘multiplex-pooled’ strategy to testing to address the need for both rapid analysis of samples from personnel at high risk of COVID infection and routine screening. Herein, our SARS-CoV-2 assays specifically address the needs of occupational healthcare for both rapid analysis of personnel at high-risk of infection and routine screening that is essential for controlling COVID-19 disease transmission. In addition to SARS-CoV-2 and COVID-19, this work demonstrates successful flexible assays developments and deployments with implications for emerging highly transmissible diseases and future pandemics.

60 APPLIED LIFE SCIENCES↗
DOE OSTI2022

94ND10 Intergranular Phase Analysis and Fabrication

The composition and phase fraction of the intergranular phase of 94ND10 ceramic is determined and fabricated ex situ. The fraction of each phase is 85.96 vol% Al 2 O 3 bulk phase, 9.46 vol% Mg-rich intergranular phase, 4.36 vol% Ca/Si-rich intergranular phase, and 0.22 vol% voids. The Ca/Si-rich phase consists of 0.628 at% Mg, 12.59 at% Si, 10.24 at% Ca, 17.23 at% Al, and balance O. The Mgrich phase consists of 14.17 at% Mg, 0.066 at% Si, 0.047 at% Ca, 28.69 at% Al, and balance O. XRD of the ex situ intergranular material made by mixed oxides consisting of the above phase and element fractions yielded 92 vol% MgAl 2 O 4 phase and 8 vol% CaAl 2 Si 2 O 8 phase. The formation of MgAl 2 O 4 phase is consistent with prior XRD of 94ND10, while the CaAl 2 Si 2 O 8 phase may exist in 94ND10 but at a concentration not readily detected with XRD. The MgAl 2 O 4 and CaAl 2 Si 2 O 8 phases determined from XRD are expected to have the elemental compositions for the Mg-rich and Ca/Si-rich phases above by cation substitutions (e.g., some Mg substituted for by Ca in the Mg-rich phase) and impurity phases not detectable with XRD.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Processing, structure, and thermal properties of ZrW 2 O 8 , HfW 2 O 8 , HfMgW 3 O 12 , Al(HfMg) 0.5 W 3 O 12 , and Al 0.5 Sc 1.5 W 3 O 12 negative and zero thermal expansion coefficient ceramics

Negative and zero coefficient of thermal expansion (CTE) materials are of interest for developing polymer composites in electronic circuits that match the expansion of Si and in zero CTE supports for optical components, e.g., mirrors. In this work, the processing challenges and stability of ZrW 2 O 8 , HfW 2 O 8 , HfMgW 3 O 12 , Al(HfMg) 0.5 W 3 O 12 , and Al 0.5 Sc 1.5 W 3 O 12 negative and zero thermal expansion coefficient ceramics are discussed. Al 0.5 Sc 1.5 W 3 O 12 is demonstrated to be a relatively simple oxide to fabricate in large quantity and is shown to exhibit single phase up to 1300 °C in air and inert N 2 environments. The negative and zero CTE behavior was confirmed with dilatometry. Thermal conductivity and heat capacity were reported for the first time for HfMgW 3 O 12 and Al 0.5 Sc 1.5 W 3 O 12 and thermal conductivity was found to be very low (~0.5 W/mK). Grüneisen parameter is also estimated. Methods for integration of Al 0.5 Sc 1.5 W 3 O 12 with other materials was examined and embedding 50 vol% of the ceramic powder in flexible epoxy was demonstrated with a commercial vendor.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Characterizing mechanical and microstructural properties of novel montmorillonite-rich polyethylene composites

Montmorillonite (MMT) clays are important industrial materials used as catalysts, chemical sorbents and fillers in polymer–clay nanocomposites. The layered structure of these clays has motivated research into further applications of these low-cost materials, including use as ion exchange media and solid-state ionic conductors. In these applications, the mechanical properties of MMT are key when considering long-term, reliable performance. Previous studies have focused on the mechanical properties of nanocomposites with MMT as the minority component or pure MMT thin films. In this work, the microstructure and mechanical properties of pure MMT and majority MMT/polyethylene composites pressed into dense pellets are examined. Characterization methods such as X-ray diffraction, atomic force microscopy and scanning electron microscopy together with nanoindentation reveal important structure–property relationships in the clay-based materials. Here, utilizing these techniques, we have discovered that MMT processing impacts the layered microstructure, chemical stability and, critically, the elastic modulus and hardness of bulk MMT samples. Particularly, the density of the pellets and the ordering of the clay platelets within them strongly influence the elastic modulus and hardness of the pellets. By increasing pressing force or by incorporating secondary components, the density, and therefore mechanical properties, can be increased. If the layered structure of the clay is destroyed by exfoliation, the mechanical properties will be compromised. Understanding these relationships will help guide new studies to engineer mechanically stable MMT-based materials for industrial applications.

36 MATERIALS SCIENCE↗