NASA NTRS1977

Evaluation of aircraft brake materials

A test program was carried out to evaluate several new high-temperature friction materials for use in aircraft disk brakes. A specially built test apparatus utilizing a disk brake and wheel half from a small jet aircraft was used. The apparatus enabled control of brake pressure, velocity and braking time. Tests were run under both constant and variable velocity conditions and covered a kinetic energy range similar to that encountered in aircraft brake service. The materials evaluation showed that two newly developed friction materials show potential for use in aircraft disk brakes. One of the materials is a nickel-based sintered composite, while the other is a molybdenum-based material. Both materials show much lower wear rates than conventional copper-based materials and are better able to withstand the high temperatures encountered during braking. Additional materials improvement is necessary, however, since both materials show a significant negative slope of the friction-velocity curve at low velocities.

Ho, T. L.↗
NASA NTRS1977

Wear formulation for aircraft brake material sliding against steel

Predictions of wear on contemporary copper-based brake material sliding against 17-22 AS grade steel, wear testing equipment, formulation of wear, and test results are discussed. An initial investigation of worn surfaces of the brake material and a mating steel rotor was carried out. A wear model proposed suggests initiation of cracks at a hard particle inclusion site in the surface layer of the brake material; crack propagation allows particles to be removed by intersection of cracks. Mutual relations between sliding variables, load, time, hardness, and surface temperature are studied. Empirical formulas are exhibited.

Ho, T. L.↗
NASA NTRS1976

Development of aircraft brake materials

A program has been carried out to study and develop high temperature aircraft brake materials. A survey of the requirements of brake materials was made to select materials to meet these requirements. Based upon their physical and thermal properties, a number of materials were selected and evaluated in sliding tests which simulated aircraft braking. The mating material is 17-22 AS steel. Additives were incorporated into these materials to optimize their wear or strength behavior with particular emphasis on nickel and molybdenum base materials. Optimum materials were developed which had improved wear behavior over conventional brake materials in the simulated test. The best materials were a nickel, aluminum oxide, lead tungstate composition containing graphite and a molybdenum base material containing LPA 100 (an intermetallic compound of cobalt, molybdenum and silicon).

Ho, T.-L.↗
NASA NTRS1975

The design of aircraft brake systems, employing cooling to increase brake life

A research program was initiated to determine the feasibility of using cooling to increase brake life. An air cooling scheme was proposed, constructed and tested with various designs. Straight and curved slotting of the friction material was tested. A water cooling technique, similar to the air cooling procedure, was evaluated on a curved slotted rotor. Also investigated was the possibility of using a phase-change material within the rotor to absorb heat during braking. Various phase-changing materials were tabulated and a 50%, (by weight) LiF - BeF2 mixing was chosen. It was shown that corrosion was not a problem with this mixture. A preliminary design was evaluated on an actual brake. Results showed that significant improvements in lowering the surface temperature of the brake occurred when air or water cooling was used in conjunction with curved slotted rotors.

Scaringe, R. P.↗
NASA NTRS1975

Evaluation of materials and design modifications for aircraft brakes

A test program is described which was carried out to evaluate several proposed design modifications and several high-temperature friction materials for use in aircraft disk brakes. The evaluation program was carried out on a specially built test apparatus utilizing a disk brake and wheel half from a small het aircraft. The apparatus enabled control of brake pressure, velocity, and braking time. Tests were run under both constant and variable velocity conditions and covered a kinetic energy range similar to that encountered in aircraft brake service. The results of the design evaluation program showed that some improvement in brake performance can be realized by making design changes in the components of the brake containing friction material. The materials evaluation showed that two friction materials show potential for use in aircraft disk brakes. One of the materials is a nickel-based sintered composite, while the other is a molybdenum-based material. Both materials show much lower wear rates than conventional copper-based materials and are better able to withstand the high temperatures encountered during braking. Additional materials improvement is necessary since both materials show a significant negative slope of the friction-velocity curve at low velocities.

Ho, T. L.↗
NASA NTRS1974

Consideration of materials for aircraft brakes

A study has been made of the frictional behavior of several aircraft brake materials using a simple high-temperature Falex-type apparatus. Tests were run at velocities of seven ft/minute; loads to 600 pounds and temperatures to 700 C. The data for these brake materials sliding against a variety of steels and other materials indicate a large reduction in friction due to surface oxidation in the temperature range 250 to 300 C. It also was found that the retention of this oxide was a function of the temperature changes. With increasing temperature the oxide was removed, while with reducing temperature it was retained. Frictional behavior was more characteristic of the steel than the brake material.

Peterson, M. B.↗
NASA NTRS1974

Effect of frictional heating on brake materials

An exploratory study of the properties of aircraft brake materials was made to determine ways of improving friction and wear behavior while minimizing surface temperatures. It is found that frictional variation at high temperature involves material softening and metal transfer, formation of oxides, and surface melting. The choice of proper materials to combat these effects is discussed. Minimum surface temperatures are found to result from use of materials with large density-specific heat and density-specific heat-conductivity factors, use of a higher load-lower friction system, and maximization of the contact area. Some useful trade-off criteria for the size of brake disks against weight considerations are suggested. Additional information on material behavior and peak braking temperatures was gathered from an inspection of used brake pads and rotor disks.

Ho, T.-L.↗
NASA NTRS1974

Development of aircraft brake materials

The requirements of brake materials were outlined and a survey made to select materials to meet the needs of high temperature brakes. A number of metals and ceramic materials were selected and evaluated in sliding tests which simulated aircraft braking. Nickel, molybdenum tungsten, Zr02, high temperature cements and carbons were tested. Additives were then incorporated into these materials to optimize their wear or strength behavior with particular emphasis on nickel and molybdenum base materials and a high temperature potassium silicate cement. Optimum materials were developed which improved wear behavior over conventional brake materials in the simulated test. The best materials are a nickel, aluminum oxide, lead tungstate composition containing graphite or molybdenum disulphite; a molybdenum base material containing LPA100 (an intermetallic compound of cobalt, molybdenum, and silicon); and a carbon material (P5).

Ho, T. L.↗
NASA NTRS1972

Evaluation of materials for sliding at 600F-1800F in air.

Oscillating sliding tests were conducted in air under the following operating conditions: 500 psi, 600 F; 500 psi, 1200 F; 500 psi, 1800 F; 1500 psi, 1800 F; 3000 psi, 1800 F. Sixteen materials combinations were tested including ceramics, alloys and eutectics, cermets, and combinations of these. Friction, wear and surface damage (including surface roughening) were studied. The most outstanding materials combination was found to be nickel-molybdenum-bonded titanium carbide cermet sliding against dense magnesia stabilized ZrO2.

Finkin, E. F.↗
NASA NTRS1972

Consideration of Materials for Aircraft Brakes

An exploratory investigation was conducted concerning materials and their properties for use in aircraft brakes. Primary consideration was given to the heat dissipation and the frictional behavior of materials. Used brake pads and rotors were analyzed as part of the investigation. A simple analysis was conducted in order to determine the most significant factors which affect surface temperatures. It was found that where size and weight restrictions are necessary, the specific heat of the material, and maintaining uniform contact area are the most important factors. A criterion was suggested for optimum sizing of the brake disks. Bench friction tests were run with brake materials. It was found that there is considerable friction variation due to the formation and removal of surface oxide films. Other causes of friction variations are surface softening and melting. The friction behavior at high temperature was found to be more characteristic of the steel surface rather than the copper brake material. It is concluded that improved brake materials are feasible.

Peterson, M. B.↗