DOE OSTI2024

Thermally generated magnonic spin currents in a polycrystalline gadolinium iron garnet thin film with perpendicular magnetic anisotropy

Rare-earth iron garnets (REIGs) are the benchmark systems for magnonics, including the longitudinal spin Seebeck effect (LSSE). While most research has focused on single-crystalline REIGs on complimentary garnet substrates, moving to more, cost-effective complementary metal-oxide semiconductor (CMOS)-compatible substrates is important to integrate REIG thin films with existing technology. In this regard, we grow a 130 nm-thick polycrystalline gadolinium iron garnet (GdIG) film on the Si/SiO2 substrate and investigate the temperature-dependent LSSE. Interestingly, the polycrystalline GdIG film exhibits perpendicular magnetic anisotropy (PMA) at room temperature which is induced by tensile in-plane (IP)-strain originating from the thermal-expansion mismatch between the GdIG film and the substrate during rapid thermal annealing. Further, a spin-reorientation transition from the out-of-plane IP direction below TS = 180 K is observed. Additionally, the film reveals a magnetic compensation temperature, TComp, of ≈240 K. The LSSE voltage not only demonstrates a sign-inversion around TComp, but also shows noticeable changes around TS. As compared to a single-crystalline GdIG film, the lower LSSE voltage for the polycrystalline GdIG is attributed to the higher effective magnetic anisotropy and enhanced magnon scattering at the grain boundaries. Our study not only paves the way for the cost-effective growth of CMOS-compatible REIG-based systems with PMA for magnonic memory and information processing applications, but also highlights the fact that the spincaloritronic and spin-insulatronic properties of the polycrystalline REIGs follow those of their single-crystalline counterparts with reduced spin-to-charge conversion efficiency through LSSE which can be tuned further by controlling the average gran size and interface engineering.

Physics↗
DOE OSTI2022

Emergent magnetism and exchange bias effect in iron oxide nanocubes with tunable phase and size

Abstract We report a systematic investigation of the magnetic properties including the exchange bias (EB) effect in an iron oxide nanocube system with tunable phase and average size (10, 15, 24, 34, and 43 nm). X-ray diffraction and Raman spectroscopy reveal the presence of Fe 3 O 4 , FeO, and α -Fe 2 O 3 phases in the nanocubes, in which the volume fraction of each phase varies depending upon particle size. While the Fe 3 O 4 phase is dominant in all and tends to grow with increasing particle size, the FeO phase appears to coexist with the Fe 3 O 4 phase in 10, 15, and 24 nm nanocubes but disappears in 34 and 43 nm nanocubes. The nanocubes exposed to air resulted in an α -Fe 2 O 3 oxidized surface layer whose thickness scaled with particle size resulting in a shell made of α -Fe 2 O 3 phase and a core containing Fe 3 O 4 or a mixture of both Fe 3 O 4 and FeO phases. Magnetometry indicates that the nanocubes undergo Morin (of the α -Fe 2 O 3 phase) and Verwey (of the Fe 3 O 4 phase) transitions at ∼250 K and ∼120 K, respectively. For smaller nanocubes (10, 15, and 24 nm), the EB effect is observed below 200 K, of which the 15 nm nanocubes showed the most prominent EB with optimal antiferromagnetic (AFM) FeO phase. No EB is reported for larger nanocubes (34 and 43 nm). The observed EB effect is ascribed to the strong interfacial coupling between the ferrimagnetic (FiM) Fe 3 O 4 phase and AFM FeO phase, while its absence is related to the disappearance of the FeO phase. The Fe 3 O 4 / α -Fe 2 O 3 (FiM/AFM) interfaces are found to have negligible influence on the EB. Our findings shed light on the complexity of the EB effect in mixed-phase iron oxide nanosystems and pave the way to design exchange-coupled nanomaterials with desirable magnetic properties for biomedical and spintronic applications.

Physics↗
DOE OSTI2021

Sub-second and ppm-level optical sensing of hydrogen using templated control of nano-hydride geometry and composition

Abstract The use of hydrogen as a clean and renewable alternative to fossil fuels requires a suite of flammability mitigating technologies, particularly robust sensors for hydrogen leak detection and concentration monitoring. To this end, we have developed a class of lightweight optical hydrogen sensors based on a metasurface of Pd nano-patchy particle arrays, which fulfills the increasing requirements of a safe hydrogen fuel sensing system with no risk of sparking. The structure of the optical sensor is readily nano-engineered to yield extraordinarily rapid response to hydrogen gas (<3 s at 1 mbar H 2 ) with a high degree of accuracy (<5%). By incorporating 20% Ag, Au or Co, the sensing performances of the Pd-alloy sensor are significantly enhanced, especially for the Pd 80 Co 20 sensor whose optical response time at 1 mbar of H 2 is just ~0.85 s, while preserving the excellent accuracy (<2.5%), limit of detection (2.5 ppm), and robustness against aging, temperature, and interfering gases. The superior performance of our sensor places it among the fastest and most sensitive optical hydrogen sensors.

36 MATERIALS SCIENCE↗