NASA NTRS1991

Results of examination of silvered Teflon from the Long Duration Exposure Facility

Pieces of silvered Teflon thermal control blanket from seventeen locations on the Long Duration Exposure Facility (LDEF) were studied. Results of the measurements of surface texturing, and mechanical, electrical and thermal properties are presented. Photos of the blankets, scanning electron microscope pictures, infrared spectra, and surface analysis results are presented. Contamination issues relative to performance of the blankets are discussed. The variation in measured properties are reported as a function of exposure conditions.

Rousslang, Ken W.↗

NASA NTRS1991

Survey of results from the Boeing modules on the M0003 experiment on LDEF

The Boeing modules on the M0003 experiment included fiber optics, ceramic materials, a variety of electronic piece parts, composites and thermal control paints, fasteners, thin film lubricants, anodized surfaces, and adhesives. These materials were flown on the leading and trailing edge exteriors, and on the interior portion of LDEF M0003 providing exposure under three distinct environments. The condition of each of these material types is described. Results of optical, surface, and mechanical properties are presented.

Pippin, H. Gary↗

NASA NTRS1991

Results from analysis of Boeing composite specimens flown on LDEF experiment M0003

Specimens of three selected organic/graphite fiber composite materials were flown on both the leading and trailing edges of LDEF. Additional sets of compression, tension, flexure, and lap shear specimens were flown on the trailing edge. A large T300/934 panel was flown on the leading edge. One quarter of this specimen was directly exposed to a near ram environment; each of the other three quarters were covered with a different thermal control paint. Results of mechanical, optical, and chemical analysis of the specimens are presented. Recession rates of the fiber and resin under atomic oxygen exposure were estimated and are reported.

Hill, Sylvester G.↗

NASA NTRS1987

Comments on the interaction of materials with atomic oxygen

An explanation of the relative resistance of various materials to attack by atomic oxygen is presented. Data from both ground based and on-orbit experiments is interpreted. The results indicate the importance of bond strengths, size and structure of pendant groups, and fluorination to the resistance of certain polymers to atomic oxygen. A theory which provides a partial explanation of the degradation of materials in low Earth orbit due to surface recombination of oxygen atoms is also included. Finally, a section commenting on mechanisms of material degradation is provided.