NASA NTRS2005

High Strength Aluminum Alloy For High Temperature Applications

A cast article from an aluminum alloy has improved mechanical properties at elevated temperatures. The cast article has the following composition in weight percent: Silicon 6.0-25.0, Copper 5.0-8.0, Iron 0.05-1.2, Magnesium 0.5-1.5, Nickel 0.05-0.9, Manganese 0.05-1.2, Titanium 0.05-1.2, Zirconium 0.05-1.2, Vanadium 0.05-1.2, Zinc 0.05-0.9, Strontium 0.001-0.1, Phosphorus 0.001-0.1, and the balance is Aluminum, wherein the silicon-to-magnesium ratio is 10-25, and the copper-to-magnesium ratio is 4-15. The aluminum alloy contains a simultaneous dispersion of three types of Al3X compound particles (X=Ti, V, Zr) having a LI2 crystal structure, and their lattice parameters are coherent to the aluminum matrix lattice. A process for producing this cast article is also disclosed, as well as a metal matrix composite, which includes the aluminum alloy serving as a matrix containing up to about 60% by volume of a secondary filler material.

Jonathan A Lee↗
NASA NTRS2003

Process for Producing a Cast Article from a Hypereutectic Aluminum-Silicon Alloy

A process for making a cast article from an aluminum alloy includes first casting an article from an alloy having the following composition, in weight percent: Silicon (Si) 14.0-25.0, Copper (CU) 5.5-8.0, Iron (Fe) 0-0.8, Magnesium (Mg) 0.5-1.5, Nickel (Ni) 0.05-1.2, Manganese (Mn) 0-1.0, Titanium (Ti) 0.05-1.2, Zirconium (Zr) 0.12-1.2, Vanadium (V) 0.05-1.2, Zinc (Zn) 0-0.9, Phosphorus (P) 0.001-0.1, Aluminum, balance. In this alloy the ration of Si:Mg is 15-35, and the ratio of Cu:Mg is 4-15. After an article is cast from the alloy, the cast article is aged at a temperature within the range of 400 F to 500 F for a time period within the range of four to 16 hours. It has been found especially advantageous if the cast article is first exposed to a solutionizing step prior to the aging step. This solutionizing step is carried out by exposing the cast article to a temperature within the range of 875 F to 1025 F for a time period of fifteen minutes to four hours. It has also been found to be especially advantageous if the solutionizing step is followed directly with a quenching step, wherein the cast article is quenched in a quenching medium such as water at a temperature within the range of 120 F to 300 F. The resulting cast article is highly suitable in a number of high temperature applications, such as heavy-duty pistons for internal combustion engines.

Jonathan A Lee↗
NASA NTRSDate not supplied

Development of Directed Energy Deposited NASA HR-1 to Optimize Properties for Liquid Rocket Engine Applications

Metal additive manufacturing (AM) processes have been demonstrated to be effective at reducing costs and lead times associated with fabrication of complex propulsion component designs. Laser powder directed energy deposition (LP-DED) and laser powder bed fusion (L-PBF) are metal AM technologies that have effectively been used to produce a variety of parts for space applications. These technologies have enabled new designs and materials for these applications. The National Aeronautics and Space Administration (NASA) has identified the need to develop and advance new materials in unique space applications such as high-pressure hydrogen environments. One such metal alloy being developed for these applications is NASA HR-1. A high-strength Fe-Ni based superalloy, NASA HR-1 was designed to resist high pressure hydrogen environment embrittlement, oxidation, and corrosion. AM technologies have enabled the manufacturing of NASA HR-1 to be a feasible material for components in hydrogen environments. Development efforts for NASA HR-1 have completed build and heat treatment optimization, material characterization, thermophysical property testing, and mechanical testing in air and hydrogen environments to mature the understanding of the material. This poster will summarize the development of NASA HR-1 for AM including composition and heat treatment optimization, microstructure characterization, and results of mechanical testing in air and high pressure hydrogen.

NASA HR-1↗
NASA NTRSDate not supplied

Development and Optimization of Additively Manufactured NASA HR-1 for Space Applications

Metal additive manufacturing (AM) processes have been demonstrated to be effective at reducing costs and lead times associated with fabrication of complex propulsion component designs. Laser powder directed energy deposition (LP-DED) and laser powder bed fusion (L-PBF) are metal AM technologies that have effectively been used to produce a variety of parts for space applications. These technologies have enabled new designs and materials for these applications. The National Aeronautics and Space Administration (NASA) has identified the need to develop and advance new materials in unique space applications such as high-pressure hydrogen environments. One such metal alloy being developed for these applications is NASA HR-1. A high-strength Fe-Ni based superalloy, NASA HR-1 was designed to resist high pressure hydrogen environment embrittlement, oxidation, and corrosion. AM technologies have enabled the manufacturing of NASA HR-1 to be a feasible material for components in hydrogen environments. Development efforts for NASA HR-1 have completed build and heat treatment optimization, material characterization, thermophysical property testing, and mechanical testing in air and hydrogen environments to mature the understanding of the material. This presentation will summarize the development of NASA HR-1 for AM including composition and heat treatment optimization, microstructure characterization, and results of mechanical testing in air and high pressure hydrogen.

Additive Manufacturing↗
NASA NTRSDate not supplied

Development of Laser Powder Bed Fusion NASA HR-2 for Hydrogen Sensitive Liquid Rocket Engine Applications

The National Aeronautics and Space Administration (NASA) has been involved in the development and maturation of metal additive manufacturing (AM) for space applications since the late 2000’s. AM has provided new design and manufacturing opportunities to reduce cost and schedule, consolidate parts, and optimize performance. Laser Powder Bed Fusion (L-PBF) is one of the most commonly used AM processes to fabricate components that have complex shape and need fine feature resolution. Due to exposure to high pressure gaseous hydrogen, mechanical property degradation caused by hydrogen environment embrittlement (HEE) is a critical concern for many materials in liquid hydrogen propulsion systems. NASA has identified the need to develop and advance new materials in unique engine applications using liquid hydrogen as a propellant. One such material being developed at NASA Marshall Space Flight Center is L-PBF NASA HR-2 (Hydrogen Resistant-2), a high-strength Fe-Ni-based superalloy resistant to HEE. The chemistry of NASA HR-2 was formulated to meet requirements for key liquid rocket engine (LRE) components that operate in high-pressure hydrogen environments. Initial development and material characterization found NASA HR-2 has excellent L-PBF printability and its microstructure evolves well after heat treatment. This new alloy has undergone fundamental metallurgical evaluations, heat treatment studies, detailed microstructure characterization, and mechanical testing across a range of temperatures. Tensile testing was performed in pressurized gaseous hydrogen (GH2) environment to assess its resistance to HEE. L-PBF NASA HR-2 has an average yield stress of 95 ksi, ultimate tensile stress of 165 ksi, and very high fracture elongation at 34 - 36% when tested in a 5 ksi high pressure hydrogen environment. The tensile property data confirms hydrogen has little influence on its ductility, strength, and fracture behavior. L-PBF NASA HR-2 is a promising option for many hydrogen sensitive LRE components that require exceptional resistance to HEE. The development of L-PBF NASA HR-2 is funded under the grants provided by Jacobs TIPI program and the Liquid Engine Office at NASA Marshall Space Flight Center. This paper will provide an overview of the L-PBF process development, material characterization, mechanical and thermophysical properties, and LRE hardware development for NASA HR-2.

NASA HR-2↗
NASA NTRSDate not supplied

Development of Laser Powder Bed Fusion NASA HR-2 for Hydrogen Sensitive Liquid Rocket Engine Applications

The National Aeronautics and Space Administration (NASA) has been involved in the development and maturation of metal additive manufacturing (AM) for space applications since the late 2000’s. AM has provided new design and manufacturing opportunities to reduce cost and schedule, consolidate parts, and optimize performance. Laser Powder Bed Fusion (L-PBF) is one of the most commonly used AM processes to fabricate components that have complex shape and need fine feature resolution. Due to exposure to high pressure gaseous hydrogen, mechanical property degradation caused by hydrogen environment embrittlement (HEE) is a critical concern for many materials in liquid hydrogen propulsion systems. NASA has identified the need to develop and advance new materials in unique engine applications using liquid hydrogen as a propellant. One such material being developed at NASA Marshall Space Flight Center is L-PBF NASA HR-2 (Hydrogen Resistant-2), a high-strength Fe-Ni-based superalloy resistant to HEE. The chemistry of NASA HR-2 was formulated to meet requirements for key liquid rocket engine (LRE) components that operate in high-pressure hydrogen environments. Initial development and material characterization found NASA HR-2 has excellent L-PBF printability and its microstructure evolves well after heat treatment. This new alloy has undergone fundamental metallurgical evaluations, heat treatment studies, detailed microstructure characterization, and mechanical testing across a range of temperatures. Tensile testing was performed in pressurized gaseous hydrogen (GH2) environment to assess its resistance to HEE. L-PBF NASA HR-2 has an average yield stress of 95 ksi, ultimate tensile stress of 165 ksi, and very high fracture elongation at 34 - 36% when tested in a 5 ksi high pressure hydrogen environment. The tensile property data confirms hydrogen has little influence on its ductility, strength, and fracture behavior. L-PBF NASA HR-2 is a promising option for many hydrogen sensitive LRE components that require exceptional resistance to HEE. The development of L-PBF NASA HR-2 is funded under the grants provided by Jacobs TIPI program and the Liquid Engine Office at NASA Marshall Space Flight Center. This paper will provide an overview of the L-PBF process development, material characterization, mechanical and thermophysical properties, and LRE hardware development for NASA HR-2.

NASA HR-2↗
NASA NTRSDate not supplied

Parameter, Post-Processing Sensitivities, and Qualification Approach of Laser Powder Bed Fusion Hydrogen Resistant Alloy NASA HR-1

Metal additive manufacturing (AM) processes are being used to enable economical manufacturing of legacy alloys as well as advancing new alloys. Laser powder bed fusion (L-PBF) is a metal AM process that has high maturity and being used to produce a variety of parts for space applications including complex propulsion components. The National Aeronautics and Space Administration (NASA) has identified the need to develop and advance new materials in unique space applications such as high-pressure hydrogen environments. NASA HR-1 is a high strength Fe-Ni based superalloy designed to resist high pressure hydrogen environment embrittlement (HEE), oxidation, and corrosion that has been successfully adapted to laser powder directed energy deposition (LP-DED). Insights gained from the NASA HR-1 development for LP-DED have guided the development process for L-PBF. However, adapting NASA HR-1 to L-PBF posed new challenges due to the distinct differences between the additive manufacturing processes. During parameter development, sensitivities were observed in post-processing that necessitated additional optimization of heat treatments. Additionally, the variations in thickness and how it influenced the microstructural response during heat treatment was characterized. Understanding these sensitivities is important to qualification of the material in a L-PBF machine. This ensures that the microstructures and properties of the material maintain consistency in production. This presentation will cover parameter development along with post-processing challenges and solutions will be discussed in addition to key material properties as it pertains to application performance and qualification per NASA-STD-6030. Improvements made by developing a derivative alloy, NASA HR-2, will be highlighted through preliminary small scale parameter development, material characterization, and initial property testing.

NASA HR-1↗