DOE OSTI2023

Surface Chemistry and Reactions for Bimetallic Au Catalysis (Final Report)

Gold-based catalysts offer tremendous opportunities for developing new technologies for selective oxidation reactions that directly use gas-phase oxygen as a benign reagent and produce either no byproducts or water as the only byproduct. These processes are urgently needed and critical for achieving the sustainable production of chemicals. While recent studies demonstrate that the catalytic properties of gold can be significantly enhanced by addition of other metals, the development of these catalysts with sufficient performance for commercialization is hindered by a lack of fundamental understanding of how the catalytic properties of gold can be controlled and tailored. This project addressed this need by synergistically combining experimental and computational studies to establish fundamental composition-structure-activity relationships for gold-based catalysts for several industrially important reactions. Results from surface spectroscopy, atomic imaging and thermal desorption experiments were combined with molecular models and reaction mechanisms from quantum chemical calculations to link observable reaction rates to the structure and composition of surfaces at the molecular level. The results were used to develop improved catalyst formulations and identify optimized reaction conditions for gold-based catalysts. For broader impacts, the developed methodology was extended to other metallic catalysts, such as silver, platinum-molybdenum and nickel-tin, for improved catalytic efficiency and sustainable production of specialty and commodity chemicals.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Degradation and fate of 2,4-dinitroanisole (DNAN) and its intermediates treated with Mg/Cu bimetal: Surface examination with XAS, DFT, and LDI-MS

In this article, a novel Mg-based bimetal reagent (Mg/Cu) was used as an enhanced reductive system to degrade insensitive munition 2,4-dinitroanisole (DNAN), a contaminant found in energetic-laden waste. Degradation of DNAN was significantly impacted by dissolved oxygen and studied in anoxic and oxic bimetal systems (i.e., purging with N 2 , air, or O 2 gas). Degradation occurred through sequential nitroreduction: first one nitro group was reduced (ortho or para) to form short-lived intermediates 2-amino-4-nitroanisole or 4-amino-2-nitroanisole (2-ANAN or 4-ANAN), and then subsequent reduction of the other nitro group formed 2,4-diaminoanisole (DAAN). The nitro-amino intermediates demonstrated regioselective reduction in the ortho position to 2-ANAN; Regioselectivity was also impacted by the anoxic/oxic environment. Under O 2 -purging DNAN degradation rate was slightly enhanced, but most notably O 2 significantly accelerated DAAN generation. DAAN also further degraded only in the oxygenated Mg/Cu system. Adsorption of DNAN byproducts to the reagent occurred regardless of anoxic/oxic condition, resulting in a partition of carbon mass between the adsorbed phase (27%-35%) and dissolved phase (59%-72%). Additional surface techniques were applied to investigate contaminant interaction with Cu. Density functional theory (DFT) calculations identified preferential adsorption structures for DNAN on Cu with binding through two O atoms of one or both nitro groups. X-ray absorption spectroscopy (XAS) measurements determined the oxidation state of catalytic metal Cu and formation of a Cu-O-N bond during treatment. Laser desorption ionization mass spectrometry (LDI-MS) measurements also identified intermediate 2-ANAN adsorbed to the bimetal surface.

54 ENVIRONMENTAL SCIENCES↗
DOE OSTI2022

Kinetics and Reaction Mechanisms of Acetic Acid Hydrodeoxygenation over Pt and Pt–Mo Catalysts

In this work, kinetic measurements for silica-supported Pt and Pt-Mo catalysts were collected in vapor-phase acetic acid hydrodeoxygenation by varying the hydrogen partial pressure between 18 and 72 kPa and acetic acid partial pressure between 7 and 18 kPa at 423-473 K. At all testing conditions, the Pt-Mo catalyst was more active and selective. In addition, the apparent activation energy for Pt-Mo of 76±3 kJ/mol was lower than that of 84±4 kJ/mol for Pt. The apparent reaction orders were also different. The order in hydrogen of 0.8±0.1 for Pt-Mo changed to zero at higher hydrogen partial pressures while that for Pt remained constant at 0.6±0.1. A near-zero order in acetic acid for Pt-Mo changed to -2.1 at higher acetic acid pressures while that for Pt remained constant at -2.9±0.3. These differences in reaction kinetics as well as in selectivity trends with changes in temperature and feed composition indicated a change in the reaction mechanism for Pt-Mo. The catalysts were characterized with hydrogen temperature programmed desorption, oxygen temperature programmed oxidation and transmission electron microscopy with energy-dispersed X-ray spectroscopy elemental mapping. Mo was present in the form of subnanometer-size clusters on the surface of Pt nanoparticles. Both Pt and Pt-Mo catalysts were stable under the reaction conditions for 10 h, and the size and structure of Pt and Pt-Mo particles remained mostly unchanged, without coke accumulation. Density functional theory calculations show that surface acetate is not a major reaction intermediate on both Pt and Pt-Mo and, instead, C-OH bond splitting with the formation of acetyl is the first reaction step in hydrodeoxygenation. The activation energy for this step is dramatically lower on Pt-Mo. Furthermore, the activity of acetyl on Pt-Mo is different. Unlike on pure Pt, the reaction of C-O bond splitting becomes exothermic with a lower activation energy on Pt-Mo, and the reaction of C-C bond splitting, in contrast, becomes endothermic with a higher activation energy, explaining the experimentally observed higher activities and selectivities of Pt-Mo. In addition, the calculations demonstrate that a pair of Pt-Mo surface atoms acts as a single active site where Mo serves as a preferential binding anchor for O atoms. The presence of Mo atoms changes the structure and energy of adsorbed and reacting surface species.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2022

Spectroscopic observation and structure-insensitivity of hydroxyls on gold

Here, the O–H stretching vibration of surface hydroxyls remained at 3691 cm –1 for gold structures ranging in size from clusters to nanoparticles, to non-flat bulk surfaces. In contrast, this vibration was not observed on flat gold surfaces. Therefore, this vibration can serve as an indicator of the roughness of the gold surface and associated functional properties, such as catalytic activity.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2020

Acetic Acid Adsorption and Reactions on Ni(110)

Acetic acid adsorption and reactions at multiple surface coverage values on Ni(110) were studied with temperature-programmed desorption (TPD) and infrared reflection absorption spectroscopy (IRAS) at 90–500 K. The experimental measurements were interpreted with density functional theory (DFT) calculations that provided information on adsorbate geometries, energies, and vibrational modes. Below the monolayer saturation coverage of 0.36 ML at 90 K, acetic acid adsorbs mostly molecularly. Above this coverage, a physisorbed layer is formed with dimers and catemers, without detectable monomers. Dimers and catemers desorb as molecular acetic acid at 157 and 172 K, respectively. Between 90 and 200 K, the O–H bond in acetic acid breaks to form bridge-bonded bidentate acetate that becomes the dominant surface species. Desorption-limited hydrogen evolution is observed at 265 K. However, even after the acetate formation, acetic acid desorbs molecularly at 200–300 K due to recombination. Minor surface species observed at 200 K, acetyls or acetates with a carbonyl group, decompose below 350 K and generate adsorbed carbon monoxide. At 350 K, the surface likely undergoes restructuring, the extent of which increases with acetic acid coverage. The initial dominant bridge-bonded bidentate acetate species formed below 200 K remain on the surface, but they now mostly adsorb on the restructured sites. Here, the acetates and all other remaining hydrocarbon species decompose simultaneously at 425 K in a narrow temperature range with concurrent evolution of hydrogen, carbon monoxide, and carbon dioxide. Above 425 K, only carbon remains on the surface.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗