DOE OSTI2024

Thermal stability of 3D interface Cu/Nb nanolaminates

Nanocrystalline alloys are promising structural materials yet lack thermal stability in many cases. Recent work shows that interface structure has an outsize effect on the thermal behavior of nanostructured alloys. Here, this work focuses on the role of controlled heterophase interface structure in the thermal evolution of model Cu/Nb nanolaminates. We introduce 3D interfaces containing nanoscale heterogeneities in all spatial dimensions between Cu and Nb, forming 3D Cu/Nb. TEM, nanoindentation, and DSC are used in tandem to establish thermal stability and to identify shifts in microstructure as a function of static annealing temperature. 3D interfaces are shown to survive annealing to 300 °C for 1 hr., while 3D Cu/Nb microstructure evolves to form low-density and voided regions correlating to the onset of layer pinch-off between 500 and 600 °C annealing temperatures. A diffusivity- and vacancy energetics-based mechanism is developed to explain void formation driven by 3D interface degradation at elevated temperature.

3D interfaces↗

DOE OSTI2023

Gas nitriding behavior of refractory metals and implications for multi-principal element alloy design

Multi-principal element alloys (MPEAs) comprise a large, flexible compositional space that enables tuning of their chemistry, structure, and properties. Here, to facilitate the development of nitriding-based surface-enhancement strategies that harness a broad compositional space, this study examined the gas nitriding behavior of Hf, Mo, Nb, Ta, Ti, and Zr as a function of time, temperature (750 and 1000 °C), and nitriding potential (i.e. ammonia-to-hydrogen ratio). These metals were selected because they have a strong driving force to form nitrides, and appear in many promising refractory MPEA compositions. The nitriding temperatures were selected based on the phase transformation temperature of Ti and Zr, and the nitriding potentials were chosen such that all elements are expected to form nitrides. Mass gain measurements indicate that all six elements follow parabolic kinetics. The microstructure observations and quantitative microchemical analysis show formation of dense and well-adhered compound layers for Mo, Nb, and Ta. Thick diffusion zones appear in Hf, Ta, Ti, and Zr, and diffusion coefficients were fit to the composition profiles. Partial delamination of the compound layer occurred for Ti and Zr. Peak hardness values above 30 GPa are obtained in the dense compound layers, and the solute hardening of the underlying alloy is correlated with the nitrogen content. The results provide insight into the dynamics of nitride compound formation relative to interstitial dissolution of nitrogen, and are discussed in the context of MPEA composition and processing design.

36 MATERIALS SCIENCE↗