DOE OSTI2023

In-situ measurement and control of the tool-workpiece interface temperature during friction stir processing of 304/304L stainless steel

Friction stir processing of 304/304L stainless steel is an area of interest for repair of spent nuclear fuel canisters. To enable repair without canister deflection or fracture, it is necessary to define the limitations for the depth of the processing zone which will be critically dependent on the thermal history of the material. Here, this work provides the first direct measurement of the interface temperature for friction stir processing of steel. The measured temperature is in the range of 850–1050 °C which is 20–30 % higher than previously reported values. Notably, the peak temperature occurs at the pin tip which is attributed to a higher sticking fraction and subsequently higher strain rate near the tool axis of rotation. Furthermore, a clear correlation between the temperature, grain size, and hardness is established within a single weld nugget and across different processing conditions. In the future, this data may lead to improved process modelling through direct validation and allow for property optimization through direct microstructure control.

304 stainless steel↗
DOE OSTI2023

Extent of interlocking and metallurgical bonding in friction riveting of aluminum alloy to steel

In this study, the joining of 6061-T6 aluminum alloy and DP590 steel using a M42 steel rivet via friction riveting technique is investigated. The surface morphology and microstructure characterization reveal the formation of an anchor zone that imparts mechanical interlock as well as the formation of metallurgical bonds at the interface of aluminum and steel. A combination of interlocking and bonding results in the achievement of a high load-carrying capacity of 5.7 kN during lap shear testing at room temperature. A finite element-based computational model was developed which accurately predicted the lap shear response of the joint. The model revealed that the metallurgical bond formed during fric-riveting adds 39% peak load strength to the joint. An extensive microstructural investigation, post-lap-shear fractography, and the modeling results, together provided insights on the joint failure mechanism. In conclusion, this study highlights that friction riveting is a promising method for aluminum-to-steel dissimilar joining, which is important for lighweighing automotive vehicles for energy efficiency.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Shear deformation of pure-Cu and Cu/Nb nano-laminates using micromechanical testing

Solid phase processing by introducing shear deformation into materials can result in unique microstructure evolution and enhanced mechanical properties, especially for immiscible systems such as Cu/Nb. To better understand the correlation between microstructure and deformation behavior during shear, a dedicated testing design of stress localization at predicted sites is necessary. In this study, a specialized S-shaped specimen geometry is implemented to apply localized simple-shear loading in pure-Cu and Cu/Nb accumulative roll-bonded nanolaminates. The nanoscale microstructure and proximity of interfaces in Cu/Nb offer a ~2.8-fold increase in shear stresses than pure-Cu. In pure-Cu, the plastic instability causes shear banding and an in-plane lattice rotation. In Cu/Nb, a partial bending of the interfaces occurred, resulting in a localized lattice rotation. The adapted geometry for micro-scale specimens thus successfully captures the shear deformation at predicted sites in two distinct material systems and could potentially be a powerful technique to study the deformation mechanisms.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Modes of strain accommodation in Cu-Nb multilayered thin film on indentation and cyclic shear

Two-phase layered thin films with a high density of semi-coherent interfaces exhibit excellent mechanical properties and thermal stability. Here, in this study, a magnetron-sputtered Cu-Nb dual-layered thin film (~500 nm for Cu and ~150 nm for Nb) having an amorphous interface between Cu and Nb with a high density of aligned growth twins in Cu is subjected to severe surface deformation. The material is loaded using indentation and cyclic shear under tribological testing. The strain accommodation in the subsurface microstructure after deformation varies based on the local structure and deformation mode. Grain refinement and crack formations in the stressed region of the Nb layer and localized crystallization of the amorphous interface are observed after indentation and scratch testing. Pronounced detwinning of growth twins in the Cu layer under the cyclic shear strain leaves large dislocations sites and loops which are observed both by high-resolution transmission electron microscopy and experiment-guided molecular dynamic (MD) simulations. Our simulations provided insights into understanding the pathway for the detwinning process under cyclic shear loading.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Temperature-dependent formation of gradient structures with anomalous hardening in an Al–Si alloy

The temperature effect on forming gradient structure in an Al-Si alloy during surface severe deformation is studied in this report. The intermediate temperature (473 K) produces the steepest gradient structure by an anomalous hardening on the top layer compared to lower (300 K) and higher temperature (673 K) counterparts. Our analysis shows profuse aluminum oxide particles in the top layer of the gradient structure under 473 K and thus lead to anomalous hardening by oxide-dispersion strengthening. Here, the counterintuitive enhancement of strengthening at the intermediate temperature is explained by the dynamic interplay between thermal-driven, mechanical-aided oxidation and the wear-induced loss of surface materials as a function of temperature, which yields a critical processing temperature to achieve the steepest gradient structure.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Solid Phase Processing of Lead-Free Brass with Carbon Additives

Currently, “lead-free” brass alloys (like C27450/C27451/C6930), used extensively in drinking water fixtures and automotive, electrical, and electronic applications contain maximum 0.25% lead to maintain mechanical performance and machinability. Adding graphite to brass as an alternative to lead, using casting, powder metallurgy, and extrusion methods, has been explored previously. However, all these methods have proven to be energy-, time-, and resource-intensive, while not enabling performance equivalent to that of C36000 brass. In this project, we developed a one-step approach using friction extrusion and ShAPE to make lead-free brass/graphite components such as wires, rods and tubes with mechanical performance equivalent to commercial lead-free brass alloys. Manufacturing temperatures were maintained ~550-730 °C with feed rates ranging between 4 – 25 mm/min. Results show larger grains at the center of the rods and wires with smaller grains developing at the edges. Graphite particles were sheared in the direction of extrusion with higher strains observed towards the edges. Hardness of the brass/graphite samples was over 25% higher than that of the corresponding brass-only samples (rods and wires), also friction extruded. Our results show that the sub-micron graphite plays an important role in limiting process temperature and restraining grain growth during friction extrusion, thus reducing grain size in composites.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Decoupling of strain and temperature effects on microstructural evolution during high shear strain deformation

The interplay between defect generation by shear strain and defect annihilation by local heating is difficult to predict in shear-assisted processing techniques. In this study, we decoupled the effects of high shear strain and external heating in an immiscible Cu-Nb alloy using a pin-on-disk tribometer to mimic the microstructural evolution of material during solid-phase processing. The change in sub-surface deformation, strain distribution, and redistribution of the second phase as a function of temperature were examined using transmission electron microscopy and atom probe tomography. Zener-Hollomon parameter is used to semi-quantify the deformation of Cu-Nb alloys as a function of strain and temperature.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Thermal Stability and Mechanical Properties of Cold-Sprayed Nickel-Yttria Coating

The microstructural evolution under the extreme environments imposed during cold spray deposition of cermet coatings and the microstructural recovery during post-processing annealing treatments is rather complex and not well understood. Here, Ni-Yttria cermet coatings on an SS304 substrate were produced using cold spray technique, resulting in a bimodal grain structure. The grain growth, phase stability, hardness, and wear properties are observed in as-deposited and annealed (at 400 °C) Ni-Yttria and pure Ni coatings. A multimodal microstructural characterization using electron microscopy, and atom probe tomography shows the structural and compositional stability of yttria particles and Ni grains. A fragmentation of Y-rich particles and dispersion in Ni was observed, however, no forced mixing/dissolution of Y in Ni is detected. Nano-yttria dispersed within the Ni grains slowed the grain growth during annealing. After annealing, Yttria reinforced coating was 1.5 times harder and showed better thermal and mechanical stability compared to the Ni coating.

Gwalani, Bharat↗
DOE OSTI2021

Cold Spray for Mitigation and Repair of Spent Nuclear Fuel Dry Storage Canisters

The purpose of this work is to investigate the use of cold spray for repair and mitigation of chloride-induced stress corrosion cracking (CISCC) in dry cask storage system (DCSS) canisters to ensure their integrity far beyond their original license period. This report provides a viability analysis of cold spray for repair and mitigation of CISCC in DCSS canisters to extend canister life.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗
DOE OSTI2021

Evaluating Effects of Shear Processing on 2D Crystalline Materials in 3D Metal Matrices: Atomistic Understanding of High Shear Deformation of Copper Graphene Composites

Composites made of copper and graphene demonstrate high strength, lubricity and enhanced electrical and thermal conductivity compared pure copper. However, manufacturing these composites at bulk volumes for industrial applications has been a big challenge. Shear deformation assisted processing is an effective method for manufacturing materials such as copper-graphene composites demonstrating ultra-fine grain structures and compositional homogeneity. Nevertheless, microstructural evolution of the composites and their property development under such conditions is not clearly understood currently. To rectify this gap in literature, high strain shear deformation of copper coated graphene foils was performed using a tribometer pin in this study. Changes in microstructure of the composite as well as the constituent components under shear deformation was correlated to process conditions. A sharp increase in the coefficient of friction attributed to rupture and smearing of graphene layer into copper substrate was observed during the shear processing. The coefficient of friction of the sheared copper/graphene composite was lower than that of pure copper, suggesting that partially worn graphene is effectively lubricious at the macroscale. A multimodal characterization of the processed region further revealed a shear deformation-induced ultrafine two-phase grain-structure consisting of copper and graphitic domains. Shear deformation reduced the copper grain size from around 50 – 100 µm to ~200 nm on an average and ~2 – 5 nm in some locations. The semicrystalline graphene films were observed to fracture into 10 – 50 µm size flakes. Oxygen enrichment was observed in the processed region. Finally, graphitic domain were identified for the first time in the copper matrix and not just at the grain boundaries providing evidence for a metastable composite microstructure as a result of solid phase processing at room temperature.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Influence of fine-scale B2 precipitation on dynamic compression and wear properties in hypo-eutectic Al0.5CoCrFeNi high-entropy alloy

The near equiatomic high-entropy alloys based on Al, Co, Cr, Fe, Ni have provided a novel microstructural template for alloy design. The face-centered cubic (FCC) matrix strengthened by body-centered cubic (BCC) based ordered B2 precipitates can be used to develop a new generation of precipitation strengthened alloys. The present study focuses on an Al0.5CoCrFeNi hypo-eutectic alloy consisting of an as-solidified FCC+B2 microstructure. Guided by solution thermodynamic modeling, this alloy has been isothermally aged for solid-state precipitation of a high fraction of fine-scale intragranular B2 particles. The dynamic compressive strength, hardness, and sliding wear response of the alloy as a function of B2 phase fraction is examined. The flow stress at 0.02% true strain increased from ~ 670 MPa to ~1350 (102%) MPa, the ultimate compressive strength increased from ~1160 MPa to 1500 MPa (20%), and the wear resistance increased more than 5 times with progressively increasing phase fraction of B2 precipitates.

Gwalani, Bharat↗